PL1658387T3 - Sposób produkcji oraz układ do produkcji blachy stalowej z powłoką cynkowo-żelazową, o wysokiej wytrzymałości - Google Patents

Sposób produkcji oraz układ do produkcji blachy stalowej z powłoką cynkowo-żelazową, o wysokiej wytrzymałości

Info

Publication number
PL1658387T3
PL1658387T3 PL04772179T PL04772179T PL1658387T3 PL 1658387 T3 PL1658387 T3 PL 1658387T3 PL 04772179 T PL04772179 T PL 04772179T PL 04772179 T PL04772179 T PL 04772179T PL 1658387 T3 PL1658387 T3 PL 1658387T3
Authority
PL
Poland
Prior art keywords
partial pressure
log
steel sheet
production
high strength
Prior art date
Application number
PL04772179T
Other languages
English (en)
Inventor
Kazuhiko Honda
Koki Tanaka
Original Assignee
Nippon Steel Corp
Arcelormittal France
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp, Arcelormittal France filed Critical Nippon Steel Corp
Publication of PL1658387T3 publication Critical patent/PL1658387T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C21D1/76—Adjusting the composition of the atmosphere
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/54—Furnaces for treating strips or wire
    • C21D9/56—Continuous furnaces for strip or wire
    • C21D9/561—Continuous furnaces for strip or wire with a controlled atmosphere or vacuum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C23C2/004—Snouts
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
PL04772179T 2003-08-19 2004-08-19 Sposób produkcji oraz układ do produkcji blachy stalowej z powłoką cynkowo-żelazową, o wysokiej wytrzymałości PL1658387T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2003207881A JP4192051B2 (ja) 2003-08-19 2003-08-19 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
EP04772179A EP1658387B1 (en) 2003-08-19 2004-08-19 Process of production and production system of high strength galvannealed steel sheet
PCT/JP2004/012223 WO2005017214A1 (en) 2003-08-19 2004-08-19 Process of production and production system of high strength galvannealed steel sheet

Publications (1)

Publication Number Publication Date
PL1658387T3 true PL1658387T3 (pl) 2012-08-31

Family

ID=34190081

Family Applications (1)

Application Number Title Priority Date Filing Date
PL04772179T PL1658387T3 (pl) 2003-08-19 2004-08-19 Sposób produkcji oraz układ do produkcji blachy stalowej z powłoką cynkowo-żelazową, o wysokiej wytrzymałości

Country Status (13)

Country Link
US (1) US8491734B2 (pl)
EP (1) EP1658387B1 (pl)
JP (1) JP4192051B2 (pl)
KR (1) KR100766165B1 (pl)
CN (1) CN100385019C (pl)
AT (1) ATE550447T1 (pl)
BR (1) BRPI0413708B1 (pl)
CA (1) CA2536153C (pl)
ES (1) ES2381364T3 (pl)
PL (1) PL1658387T3 (pl)
RU (1) RU2323266C2 (pl)
TW (1) TWI268964B (pl)
WO (1) WO2005017214A1 (pl)

Families Citing this family (47)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4741376B2 (ja) * 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
BRPI0617390B1 (pt) * 2005-10-14 2017-12-05 Nippon Steel & Sumitomo Metal Corporation METHOD OF CONTINUOUS CUTTING AND COATING BY HOT IMMERSION AND CONTINUOUS CUTTING AND COATING SYSTEM BY HOT IMMERSION OF STEEL PLATES CONTAINING Si
JP4912684B2 (ja) * 2006-01-18 2012-04-11 新日本製鐵株式会社 高強度溶融亜鉛めっき鋼板およびその製造装置ならびに高強度合金化溶融亜鉛めっき鋼板の製造方法
PL1980638T3 (pl) * 2006-01-30 2014-03-31 Nippon Steel & Sumitomo Metal Corp Wysokowytrzymała blacha cynkowana ogniowo o doskonałej podatności na formowanie i nadająca się do platerowania, wysokowytrzymała stopowa blacha cynkowana ogniowo oraz procesy i urządzenie do ich wytwarzania
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
JP4837459B2 (ja) * 2006-06-30 2011-12-14 新日本製鐵株式会社 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP4932363B2 (ja) * 2006-07-20 2012-05-16 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板及びその製造方法
JP4932376B2 (ja) * 2006-08-02 2012-05-16 新日本製鐵株式会社 めっき性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
DE102006039307B3 (de) * 2006-08-22 2008-02-21 Thyssenkrupp Steel Ag Verfahren zum Beschichten eines 6-30 Gew.% Mn enthaltenden warm- oder kaltgewalzten Stahlbands mit einer metallischen Schutzschicht
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5103988B2 (ja) * 2007-03-30 2012-12-19 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板
FR2920439B1 (fr) 2007-09-03 2009-11-13 Siemens Vai Metals Tech Sas Procede et dispositif d'oxydation/reduction controlee de la surface d'une bande d'acier en defilement continu dans un four a tubes radiants en vue de sa galvanisation
JP5200463B2 (ja) * 2007-09-11 2013-06-05 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
JP5119903B2 (ja) 2007-12-20 2013-01-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法
TWI396772B (zh) 2009-02-03 2013-05-21 Nippon Steel & Sumitomo Metal Corp 合金化熔融鍍鋅鋼板及其製造方法
WO2011025042A1 (ja) 2009-08-31 2011-03-03 新日本製鐵株式会社 高強度溶融亜鉛めっき鋼板及びその製造方法
JP5614159B2 (ja) * 2009-10-30 2014-10-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法
CN101781745A (zh) * 2010-03-19 2010-07-21 杭州创宇金属制品科技有限公司 钢丝钢带热镀零排放节能生产系统及生产方法
JP2011224584A (ja) * 2010-04-16 2011-11-10 Jfe Steel Corp 熱延鋼板の製造方法及び溶融亜鉛めっき鋼板の製造方法
ES2425916T5 (es) 2010-11-30 2024-08-09 Tata Steel Uk Ltd Procedimiento para galvanizar una banda de acero en una línea de galvanización en caliente de templado continuo
CN102031474A (zh) * 2010-12-07 2011-04-27 重庆万达薄板有限公司 高强度热浸镀锌钢带生产方法
TWI523975B (zh) * 2011-09-30 2016-03-01 Nippon Steel & Sumitomo Metal Corp A galvanized steel sheet excellent in formability and an alloyed hot-dip galvanized steel sheet and a method for producing the same
PL2762600T3 (pl) * 2011-09-30 2019-09-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania
EP2762585B8 (en) * 2011-09-30 2019-07-31 Nippon Steel Corporation High-strength hot-dip galvanized steel sheet with excellent mechanical cutting characteristics, high-strength alloyed hot-dip galvanized steel sheet, and method for producing said sheets
MX359228B (es) * 2011-09-30 2018-09-20 Nippon Steel & Sumitomo Metal Corp Planta de acero que tiene capa galvanizada por inmersión en caliente y que muestra humectabilidad por deposición y adhesión por deposición superior, y método de producción para la misma.
JP5505430B2 (ja) * 2012-01-17 2014-05-28 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍炉及び連続焼鈍方法
DE102012100509B4 (de) * 2012-01-23 2015-10-08 Thyssenkrupp Rasselstein Gmbh Verfahren zum Veredeln einer metallischen Beschichtung auf einem Stahlband
DE102012101018B3 (de) * 2012-02-08 2013-03-14 Thyssenkrupp Nirosta Gmbh Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts
EP2835432B1 (en) 2012-04-06 2016-11-02 JFE Steel Corporation Continuous hot-dip zinc plating facility
WO2014021452A1 (ja) 2012-08-03 2014-02-06 新日鐵住金株式会社 溶融亜鉛めっき鋼板及びその製造方法
BR112015008396B1 (pt) * 2012-11-06 2019-12-03 Nippon Steel Corporation chapa de aço galvanizada por imersão a quente em liga e método de produção da mesma
KR20150084051A (ko) * 2012-12-04 2015-07-21 제이에프이 스틸 가부시키가이샤 연속 용융 아연도금 강판의 제조 설비 및 제조 방법
JP5626324B2 (ja) 2012-12-11 2014-11-19 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
PL2997173T3 (pl) * 2013-05-17 2019-04-30 Ak Steel Properties Inc Sposób wytwarzania stali powleczonej cynkiem do utwardzania w procesie tłoczenia na gorąco
CN104342547B (zh) * 2013-07-31 2017-03-01 宝山钢铁股份有限公司 一种连续退火炉的分级式热吹扫方法
WO2015088501A1 (en) * 2013-12-10 2015-06-18 Arcelormittal Investigacion Y Desarrollo A method of annealing steel sheets
MX2017005507A (es) 2014-11-05 2017-06-20 Nippon Steel & Sumitomo Metal Corp Hoja de acero galvanizad por inmersion en caliente.
BR112017008460A2 (pt) 2014-11-05 2017-12-26 Nippon Steel & Sumitomo Metal Corp chapa de aço galvanizada por imersão a quente
US10822683B2 (en) 2014-11-05 2020-11-03 Nippon Steel Corporation Hot-dip galvanized steel sheet
EP3421625A4 (en) * 2016-02-25 2019-07-31 Nippon Steel Corporation METHOD FOR PRODUCING STEEL PLATE AND DEVICE FOR PERMANENTLY GLOWING STEEL PLATE
JP6455544B2 (ja) * 2017-05-11 2019-01-23 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
BR112020001163A2 (pt) 2017-07-31 2020-07-21 Nippon Steel Corporation chapa de aço galvanizada por imersão a quente
WO2019026116A1 (ja) 2017-07-31 2019-02-07 新日鐵住金株式会社 溶融亜鉛めっき鋼板
BR112020001437A2 (pt) 2017-07-31 2020-07-28 Nippon Steel Corporation chapa de aço galvanizada por imersão a quente
US11384419B2 (en) * 2019-08-30 2022-07-12 Micromaierials Llc Apparatus and methods for depositing molten metal onto a foil substrate
IT202000013879A1 (it) 2020-06-10 2021-12-10 Tenova Spa Gruppo bruciatore a fiamma libera per forni per il trattamento termo-chimico di nastri d’acciaio in impianti per la zincatura a caldo continua.
EP4177363A4 (en) * 2020-07-14 2023-07-05 JFE Steel Corporation DEVICE FOR CONTINUOUS ANNEALING, DEVICE FOR CONTINUOUS HOT GALVANIZING AND METHOD FOR MANUFACTURING A STEEL SHEET

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5917169B2 (ja) * 1978-12-25 1984-04-19 日本鋼管株式会社 無酸化炉の雰囲気制御方法
CA1137394A (en) * 1979-12-05 1982-12-14 Hajime Nitto Process for continuously annealing a cold-rolled low carbon steel strip
US4361448A (en) * 1981-05-27 1982-11-30 Ra-Shipping Ltd. Oy Method for producing dual-phase and zinc-aluminum coated steels from plain low carbon steels
JPH0645853B2 (ja) 1988-07-26 1994-06-15 住友金属工業株式会社 合金化溶融亜鉛めっき鋼板の製造方法
JP2513532B2 (ja) 1990-11-30 1996-07-03 新日本製鐵株式会社 高Ｓｉ含有鋼の高張力溶融亜鉛めっき鋼板の製造方法
RU2040556C1 (ru) * 1993-06-15 1995-07-25 Череповецкий металлургический комбинат Способ производства полос из малоуглеродистой горячекатаной стали
JP3176843B2 (ja) 1996-06-05 2001-06-18 川崎製鉄株式会社 溶融亜鉛めっき鋼板の製造方法および製造設備
JPH09324210A (ja) 1996-06-07 1997-12-16 Kawasaki Steel Corp 溶融亜鉛めっき鋼板の製造方法および製造設備
RU2128719C1 (ru) * 1997-03-05 1999-04-10 Научно-производственный институт АО "Новолипецкий металлургический комбинат" Способ производства горячеоцинкованного металла высших категорий вытяжки с тончайшим цинковым покрытием с превосходной штампуемостью
JP3956550B2 (ja) 1999-02-02 2007-08-08 Ｊｆｅスチール株式会社 強度延性バランスに優れた高強度溶融亜鉛メッキ鋼板の製造方法
JP2001279412A (ja) * 2000-03-29 2001-10-10 Nippon Steel Corp 耐食性の良好なＳｉ含有高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP2001323355A (ja) 2000-05-11 2001-11-22 Nippon Steel Corp めっき密着性と塗装後耐食性の良好なＳｉ含有高強度溶融亜鉛めっき鋼板と塗装鋼板およびその製造方法
FR2828888B1 (fr) * 2001-08-21 2003-12-12 Stein Heurtey Procede de galvanisation a chaud de bandes metalliques d'aciers a haute resistance
JP5338087B2 (ja) 2008-03-03 2013-11-13 Ｊｆｅスチール株式会社 めっき性に優れる溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき設備

Also Published As

Publication number Publication date
CN1839210A (zh) 2006-09-27
US8491734B2 (en) 2013-07-23
KR20060026970A (ko) 2006-03-24
CN100385019C (zh) 2008-04-30
CA2536153C (en) 2009-10-06
ES2381364T3 (es) 2012-05-25
KR100766165B1 (ko) 2007-10-10
TW200510567A (en) 2005-03-16
US20070051438A1 (en) 2007-03-08
EP1658387A1 (en) 2006-05-24
TWI268964B (en) 2006-12-21
BRPI0413708A (pt) 2006-10-17
RU2323266C2 (ru) 2008-04-27
WO2005017214A1 (en) 2005-02-24
BRPI0413708B1 (pt) 2012-12-11
JP4192051B2 (ja) 2008-12-03
CA2536153A1 (en) 2005-02-24
RU2006108544A (ru) 2006-07-27
ATE550447T1 (de) 2012-04-15
JP2005060743A (ja) 2005-03-10
EP1658387B1 (en) 2012-03-21

Similar Documents

Publication Publication Date Title
CA2536153A1 (en) Process of production and production system of high strength galvannealed steel sheet
CA2640646A1 (en) High strength hot-dip galvanized steel sheet and high strength hot-dip galvannealed steel sheet and methods of production and apparatuses for production of the same
JP5370244B2 (ja) 高強度溶融亜鉛めっき鋼板の製造方法
MX368095B (es) Metodo de produccion de lamina de acero galvano-recocida.
UA94252C2 (ru) СПОСОБ ПОЛУЧЕНИЯ вспененного шлака на расплаве металла
NZ591730A (en) Process and apparatus for producing dip coated steel sheets including controlling oxygen concentration above the bath
MX2020006497A (es) Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente y aparato de galvanizacion por inmersion en caliente continua.
JP5338087B2 (ja) めっき性に優れる溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき設備
WO2013187039A1 (ja) 鋼帯の連続焼鈍方法、鋼帯の連続焼鈍装置、溶融亜鉛めっき鋼帯の製造方法及び溶融亜鉛めっき鋼帯の製造装置
CA2020077A1 (fr) Procede de traitement thermique de metaux
JP5672747B2 (ja) 高強度溶融亜鉛めっき鋼板およびその製造方法
PL1735116T3 (pl) Sposób ciągłego wytwarzania taśmy ze stali nierdzewnej austenitycznej o matowym wyglądzie powierzchni
KR20150121212A (ko) 용융 아연도금 강판의 제조 방법 및 연속 용융 아연도금 장치
FI62143B (fi) Foerfarande foer framstaellning av staol med hoeg kvaevehalt
TW363937B (en) A method for decreasing the metal impurities in the ozone gas piping
US8568137B2 (en) Method for operating a continuous annealing or galvanization line for a metal strip
MX2025000317A (es) Metodo para calentar laminas de acero, metodo para producir laminas de acero recubiertas, horno de combustion directa e instalacion de galvanizado en caliente continuo
JP4912684B2 (ja) 高強度溶融亜鉛めっき鋼板およびその製造装置ならびに高強度合金化溶融亜鉛めっき鋼板の製造方法
JP2019189894A (ja) 連続溶融亜鉛めっき鋼板の製造方法
MY145982A (en) A process for the production of chlorine dioxide
JP2012126964A (ja) 表面性状に優れた冷延鋼板の製造方法および製造装置
JP5200463B2 (ja) 溶融亜鉛めっき鋼板の製造方法
JP2007146242A (ja) 高強度溶融亜鉛めっき鋼板の製造方法および溶融亜鉛めっき鋼板の製造設備
WO2004058924A3 (fr) Procede de generation de gaz de synthese par oxydation partielle catalytique
MX2023014739A (es) Metodo de desnitrificacion de acero fundido y metodo de produccion de acero.