WO2008044266A1 - Superstrong adhesive tape - Google Patents

Superstrong adhesive tape Download PDF

Info

Publication number
WO2008044266A1
WO2008044266A1 PCT/JP2006/319965 JP2006319965W WO2008044266A1 WO 2008044266 A1 WO2008044266 A1 WO 2008044266A1 JP 2006319965 W JP2006319965 W JP 2006319965W WO 2008044266 A1 WO2008044266 A1 WO 2008044266A1
Authority
WO
WIPO (PCT)
Prior art keywords
foam material
adhesive tape
plastic foam
pressure
sensitive adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2006/319965
Other languages
English (en)
French (fr)
Inventor
Fumikazu Yamada
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MUSASHI CHEMICALS INDUSTRY Co Ltd
Original Assignee
MUSASHI CHEMICALS INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MUSASHI CHEMICALS INDUSTRY Co Ltd filed Critical MUSASHI CHEMICALS INDUSTRY Co Ltd
Priority to JP2008538507A priority Critical patent/JPWO2008044266A1/ja
Priority to PCT/JP2006/319965 priority patent/WO2008044266A1/ja
Priority to KR1020097008028A priority patent/KR20090086952A/ko
Priority to US12/311,547 priority patent/US20100173111A1/en
Priority to CN200680056514A priority patent/CN101547986A/zh
Priority to EP06811303A priority patent/EP2090631A4/en
Publication of WO2008044266A1 publication Critical patent/WO2008044266A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

明 細 書
超強粘着テープ
技術分野
[0001] 本発明は、吸着機能を併せ備えることによって、試着面に対して安定に粘着される 超強粘着テープの提供に関する。
背景技術
[0002] 釘やビス等によって取り付けのできない取り付け対象物、例えばタイル面に対して 各種物品を取り付ける場合や取り付け物品に釘、ビスなどの止め跡を残すことが憚か れる場合には、通常、両面粘着テープ等の粘着止め着け手段による固定、あるいは 吸盤等による吸着状態での止め着けがなされている。
[0003] 力かる両面粘着テープ等を用いた取り付け物品の粘着、止め着けにあっては、取り 付け物品が、取り付け対象面に対して固定的に止着されることが無ぐ取り付け面に おいてずれ出し、あるいは取り付け面から引き剥がされる等の難がある。粘着面にお けるずれ出し、あるいは引き剥しは、取り付け物品の重さ等に対応して、粘着面にも たらされる荷重が大きくなるほど顕著に生ずるとともに、粘着後の時間の経過に伴つ て、より顕著に生ずる難がある。
[0004] また、吸盤等の吸着機能を用いて、各種物品の取り付けをなす場合にあっては、こ の吸着対象とされる取り付け面の平滑性が特に厳格に要請され、物品の取り付け対 象物が多くの制約を受けるという難がある。さらに、吸着機能による各種物品の取り付 けにあっては、吸盤等の吸着具における構成素材の経時的な劣化により、吸着面に おける気密性が欠落する等の不都合を生じ易 、。
[0005] このような状況から、本願出願人は、プラスチックフォームの吸着機能を利用した強 粘構造を提案している (特許文献 1を参照)。この強粘構造は、粘着剤層を備えるプ ラスチックフォーム材において、少なくとも粘着対象面に粘着される粘着剤層を備え た面に開口されている孔が、該プラスチックフォーム材の圧縮変形後における弹性復 帰に伴って、前記粘着対象面に吸着する吸着機能を備えており、粘着剤層による粘 着機能と、孔による吸着機能とが、同時に取付け物の取付け面に作用することとなり 、取付け物を確実に止着状態に保持することができる特長を有している。
特許文献 1：特許第 3016730号公報
[0006] 前記のように、特許文献 1記載の強粘構造及びそれを備える粘着テープによれば、 非常に強い接着固定力を得ることができ、し力も比較的簡単に剥がせ、剥離後に跡 が残ることもない等、幾多の長所を有する。
発明の開示
[0007] 本発明は、前記特許文献 1記載の強粘構造を有する粘着テープより一層改良する ことを目的に提案されたものである。すなわち、本発明は、特許文献 1記載の強粘構 造よりも優れた接着力を実現することが可能な超強粘着テープを提供することを目的 とする。
[0008] 本発明の超強粘着テープは、前記粘着対象面に臨むように開口された孔が形成さ れたプラスチックフォーム材と、前記孔に対応する位置に凹部を形成するように前記 プラスチックフォーム材の粘着対象面に備えられた粘着剤層とを有し、前記プラスチ ックフォーム材の圧縮変形にともなって前記凹部が略平面状に変形し、前記プラスチ ックフォーム材の弹性復帰に応じて吸着機能を有することを特徴とする。
[0009] 本発明の超強粘着テープによれば、粘着剤層の吸盤状の凹部による吸着機能に より、粘着剤の粘着力と吸盤状の凹部の吸着力によって粘着対象物をより強く粘着 することができる。
[0010] また、本発明の超強粘着テープにおいて、前記凹部は、吸盤状であることを特徴と する。これにより、孔を粘着剤によって吸盤状とすることで、単なる吸着機能に比べせ ん断接着力が向上させることができる。
[0011] 本発明の超強粘着テープにおいて、前記プラスチックフォーム材をシート状基材上 に形成されていることを特徴とする。また、本発明の超強粘着テープにおいて、前記 プラスチックフォーム材は、前記シート状基材の両面に粘着対象面を外側となるよう に形成されていることを特徴とする。これにより、両面に粘着することができる。
[0012] さらに、本発明の超強粘着テープにおいて、前記粘着剤層と接して離型処理され た剥離シートが設けられ、使用時に前記剥離シートが粘着剤層から剥離されることを 特徴とする。これにより、粘着剤層の経時劣化や埃等の進入を防止することができ、 粘着剤層の粘着力の低下を防ぐことができる。
[0013] 本発明の超強粘着テープによれば、粘着剤層の吸盤状の凹部による吸着機能に より、粘着剤の粘着力と凹部の吸着力によって粘着対象物をより強く粘着することが できる。また、孔を粘着剤によって吸盤状とすることで、従来のものに比べて著しく高 いせん断接着力を実現することが可能である。
図面の簡単な説明
[0014] [図 1]本発明の超強粘着テープの一例である粘着テープを示す概略断面図である。
[図 2]本発明の超強粘着テープの一例である粘着テープの凹部を示す拡大断面図 である。
[図 3]本発明の超強粘着テープの一例である粘着テープに粘着対象物を押し付けた 状態を示す拡大断面図である。
[図 4]本発明の超強粘着テープの一例である両面粘着テープを示す概略断面図で ある。
[図 5]本発明の超強粘着テープの一例である両面粘着テープの一方の面を圧縮させ た状態の断面を示す図である。
発明を実施するための最良の形態
[0015] [実施の形態 1]
以下、本発明の超強粘着テープについて、図面を参照して詳細に説明する。この 粘着テープの基本構成は、図 1のように、シート状基材 1と、粘着対象面に望むように 開口される孔 20及び内部に空間を有するプラスチックフォーム材 2と、プラスチックフ オーム材 2の粘着対象面に形成される粘着剤層 3と、粘着剤層 3と接して離型処理さ れた剥離シート 4とにより構成されている。
[0016] シート状基材 1は、プラスチックフォーム材 2と粘着剤層 3とを有する強粘構造を備え るシート状の部材である。このシート状基材 1は、粘着テープの用途に応じて材質等 を適宜変更することができ、例えば、ポリエチレンテレフタレートといったポリマーを使 用したシートとすることができる。さらに、例えばこのシート状基材 1を非通気性の材料 を使用することで、下記で説明する粘着剤層 3の凹部 30の気密性を高めることができ 、吸着機能を高めることができる。 [0017] プラスチックフォーム材 2は、内部や表面に孔 20を有する多孔質構造で、粘着テー プに対する押圧にともなって圧縮変形し、この押圧を解除した際に、押圧前の状態に 弾性復帰する各種のプラスチックフォーム材である。例えば、ポリウレタンフォーム材 、ポリエチレンフォーム材、ポリアクリルフォーム材等が挙げられる。このプラスチックフ オーム材は、実施の形態 1のような粘着テープの場合、シート状基材 1上に形成され 、本発明の強粘構造の使用を容易にする。
[0018] このプラスチックフォーム材 2は、図 1のように、少なくとも粘着対象面に孔 20が開口 されている。この孔 20は、プラスチックフォーム材 2の形成時に形成された孔 20であ り、粘着対象面に限らず、プラスチックフォーム材 2の内部に形成されている。
[0019] このプラスチックフォーム材 2は、粘着テープに対する押圧時に変形し、その押圧が 解除された際に弾性復帰するものであれば、 、かなる態様の発泡体孔であってもよ い。例えば、連続気泡タイプのプラスチックフォーム材、独立気泡タイプのプラスチッ クフォーム材、及び独立気泡と連続気泡との混在タイプのプラスチックフォーム材等、 任意のフォ一ム材を用いることができる。
[0020] 粘着剤層 3は、粘着剤からなる層で、少なくとも、プラスチックフォーム材 2の粘着対 象面に形成されている。そして、この粘着剤層 3は、プラスチックフォーム材 2の粘着 対象面にある孔 20に対応する位置に凹部 30が形成されている。
[0021] この凹部 30は、プラスチックフォーム材 2の孔 20に孔 20の大方を埋めるように粘着 剤が入り込んでいる。そして、図 2のように、凹部 30の中心近傍が孔 20に入り込むよ うに凹部 30の中心に向力つて徐々に深くする。この吸盤状の凹部 30は、粘着剤の量 や層の厚さを調節して、このような形状 、わゆる吸盤状となるように形成されて 、る。 この凹部 30の吸着機能により粘着対象物を吸着することができる。そして、凹部 30を 吸盤状とすることで、凹部 30と粘着対象物との気密性が高くなり、吸着力が向上する 。したがって、吸盤としての機能が向上し、高いせん断接着力が実現され、粘着対象 物をより強く粘着することができる。また、押しつけることで、強いせん断接着力が実 現される。
[0022] この凹部 30を吸盤状とするためには、プラスチックフォーム材 2の孔 20が気泡 1つ によって形成されている方が好ましい。あるいは、 2つ以上の気泡が連なって形成さ れた状態であっても、例えば気泡 1つから 2つ程度のあまり深くない孔 20が好ましい。 深すぎる孔の場合、粘着剤層 3の形成時に凹部 30の略中央のくぼみが深くなり、粘 着対象物の粘着の際に凹部 30が略平面となりに《なり、凹部 30の気密性が損なわ れる。
[0023] したがって、気泡 1つすなわち単独気泡タイプのフォーム材を使用する力 連続気 泡タイプ又は混在タイプのフォーム材の場合、プラスチックフォーム材 2の厚さを薄く したものを使用することで好適となる。例えば、プラスチックフォーム材 2の厚さを 10m mから 0. Olmmとすることが好ましい。さらに好ましくは、プラスチックフォーム材 2の 厚さが 0. 5mmから 0. 05mmである。プラスチックフォーム材 2の厚さを薄くすること で、単独の気泡を増加させることができ、 2つ以上の気泡が連なって形成された孔 20 であっても、 1つから 2つ程度のあまり深くないものとなる。したがって、孔 20の大部分 を粘着剤によって埋めるのが容易となる。
[0024] 粘着剤層 3は、典型的には、溶剤タイプのウレタン系粘着剤、溶剤タイプのアクリル 系粘着剤、あるいはェマルジヨンタイプの酢酸ビニル系粘着剤、紫外線硬化型接着 剤等を用いることができる。例えば、粘着剤層 3は、比較的粘性の強い粘着剤を、口 一ラーコーティング法等によって、プラスチックフォーム材 2の貼着面に塗布すること によって形成することができる。
[0025] また、この粘着剤層 3の凹部 30を非気密構造とすることで、より強い吸着機能が得 られる。そのために、例えば、プラスチックフォーム材 2の粘着対象面に、その形状に 合わせ、粘着剤層 3の凹部 30の形成を阻害しない程度に薄く合成樹脂を塗布して、 粘着剤層 3の凹部 30への通気を防ぐことができ、吸着機能が向上する。また、また、 例えば、プラスチックフォーム材の貼着面以外の面に合成樹脂液を塗布し、貼着面 以外の面を非通気性の榭脂コーティング面としても同様の効果が得られる。
[0026] 剥離シート 4は、粘着テープが粘着対象物に粘着する前に粘着剤層 3に接するよう に設けられている。この剥離シート 4は、すくなくとも、粘着剤層 3と接する面に離型処 理が施され、容易に粘着剤層 3から剥離することができる。
[0027] このように形成される粘着テープは、粘着剤による粘着機能と、粘着剤層 3に形成さ れた凹部 30の吸着機能とが、同時に粘着対象物 5に作用し、粘着対象物相互を確 実に粘着することができる。すなわち、この粘着テープは、プラスチックフォーム材 2 における粘着対象面、粘着剤層 3の凹部 30の開口周縁が、粘着剤によって、粘着対 象面に対して粘着されることとなり、このプラスチックフォーム材 2に吸着機能をもたら す孔の吸着面に対する気密状態での密着を可能としている。
[0028] 上述のように構成される粘着テープにおいては、図 2及び図 3のように粘着対象物 5 を粘着テープの粘着機能と吸着機能とにより、強固に粘着することができる。図 2は、 粘着テープに粘着対象物 5が粘着する前の状態を示す図であり、図 3は、粘着対象 物 5の粘着テープに対する押圧によって、粘着テープに粘着させている状態を示す 図である。
[0029] 図 2のように、粘着テープの粘着剤層 3には、吸盤状の凹部 30が形成されている。
この粘着テープに粘着対象物 5を粘着する際、剥離シート 4を剥離し、表出した粘着 剤層 3に対する粘着対象物 5の押圧によって、プラスチックフォーム材 2が弾性圧縮 する。このとき、プラスチックフォーム材 2の孔 20が変形する。そして、この孔 20の対 応する位置に形成されて ヽる吸盤状の凹部 30が粘着対象物 5に押し付けられる。
[0030] 凹部 30が粘着対象物 5に押し付けられることで、図 3のように、凹部 30の粘着対象 物 5との接触部分が略平面となる。これ〖こより、凹部 30と粘着対象物 5とが密着し、粘 着対象物 5が押し付ける前に存在した凹部 30内の空気が外に逃げ、負圧となる。す なわち、粘着対象物 5に対して凹部 30が吸着する。したがって、粘着対象物 5の粘着 テープに対する押圧を解除しても、凹部 30の吸着機能により、粘着対象物 5を吸着 することができる。また、同時に、粘着剤層 30の粘着機能を有するため、粘着対象物 5を粘着テープにより強固に粘着させることができる。また、凹部 30が吸盤状であるた め、せん断接着力が強い。
[0031] このようにして構成される粘着テープにおいては、粘着対象物に対して、圧縮後に おける弾性復帰に伴う孔の有する吸着機能と、この孔を有する面における粘着剤層 による粘着機能とによって、強固な止着状態を作り出すことができる。そして、凹部 30 が吸盤としての機能を備えることで、せん断接着力が向上する。一方、凹部 30は吸 盤として機能するため、粘着対象物を粘着テープカゝら引き剥がすことで容易に引き 剥がすことができる。 [0032] [実施の形態 2]
実施の形態 1で説明した粘着テープは、片面の粘着テープに限られるものではなく 、例えば、シート状基材の両面に粘着対象面を外側となるようにプラスチックフォーム 材を有するような両面粘着テープであってもよ 、。
[0033] この両面粘着テープは、図 4のように、シート状基材 1の両面に、プラスチックフォー ム材 2と、粘着剤層 3と、剥離シート 4とを備えている。そして、プラスチックフォーム材 2の粘着対象面には、孔 20を備えている。そして、粘着剤層 3は、その孔 20の対応 する位置に吸盤状の凹部 30を備えている。尚、実施の形態 2で説明する両面粘着テ ープの各部材は、同一の番号を付し、説明を省略する。
[0034] 両面に強粘構造を備えた両面粘着テープとすることで、粘着テープの両側から 2つ の粘着対象物 5の粘着テープに対する押圧によって、上述と同様に、粘着テープの 粘着剤層 30に 2つの粘着対象物 5が押し付けられる。 2つの粘着対象物 5が押し付 けられることで、凹部 30が粘着対象物 5に対して略平面となり、吸着機能が生じ、粘 着テープが粘着機能と吸着機能とによって強固に粘着する。また、凹部 30が吸盤状 であることで、せん断接着力が高くなる。また、粘着対象物 5を両面粘着テープから 引き剥がすことも容易である。
[0035] 図 5は、一方の面が圧縮された状態の両面粘着テープの断面を示す写真である。
シート状基材 1は、プラスチックフォーム材 2と粘着剤層 3が備えられ、図 5にはシート 状基材 1を構成する繊維 10が確認できる。そして、シート状基材 1の図 5中下方には 、シート状基材 1から粘着剤層 3に向力 ように空隙 35が形成されている。一方、シー ト状基材 1の図 5中上方は、プラスチックフォーム材 2が圧縮されている。粘着対象物 を粘着させる際に、この粘着テープを図 5のような状態となるように粘着対象物を押し つけることで、吸着力が向上し、粘着対象物をより強く粘着することができるとともに、 強いせん断接着力が実現される。

Claims

請求の範囲
[1] 前記粘着対象面に臨むように開口された孔が形成されたプラスチックフォーム材と 前記孔に対応する位置に凹部を形成するように前記プラスチックフォーム材の粘着 対象面に備えられた粘着剤層とを有し、
前記プラスチックフォーム材の圧縮変形にともなって前記凹部が略平面状に変形し 、前記プラスチックフォーム材の弾性復帰に応じて吸着機能を有することを特徴とす る超強粘着テープ。
[2] 前記凹部は、吸盤状であることを特徴とする請求項 1記載の超強粘着テープ。
[3] 前記プラスチックフォーム材をシート状基材上に形成されて 、ることを特徴とする請 求項 1記載の超強粘着テープ。
[4] 前記プラスチックフォーム材は、前記シート状基材の両面に粘着対象面を外側とな るように形成されて 、ることを特徴とする請求項 3記載の超強粘着テープ。
[5] 前記粘着剤層と接して離型処理された剥離シートが設けられ、使用時に前記剥離 シートが粘着剤層から剥離されることを特徴とする請求項 1記載の超強粘着テープ。
PCT/JP2006/319965 2006-10-05 2006-10-05 Superstrong adhesive tape Ceased WO2008044266A1 (en)