WO2018128392A1 - 유리 질감의 폴리에스테르계 데코시트 - Google Patents

유리 질감의 폴리에스테르계 데코시트 Download PDF

Info

Publication number
WO2018128392A1
WO2018128392A1 PCT/KR2018/000129 KR2018000129W WO2018128392A1 WO 2018128392 A1 WO2018128392 A1 WO 2018128392A1 KR 2018000129 W KR2018000129 W KR 2018000129W WO 2018128392 A1 WO2018128392 A1 WO 2018128392A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
color
sheet
transparent layer
transparent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2018/000129
Other languages
English (en)
French (fr)
Inventor
한범택
민호진
강규원
이남희
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Chemical Korea Inc
Original Assignee
Toray Chemical Korea Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020170001369A external-priority patent/KR101906980B1/ko
Application filed by Toray Chemical Korea Inc filed Critical Toray Chemical Korea Inc
Priority to EP18735832.0A priority Critical patent/EP3566867B1/en
Publication of WO2018128392A1 publication Critical patent/WO2018128392A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 폴리에스테르계 수지를 기반으로 투명층과 컬러층으로 구성된 유리 질감의 데코시트를 제공한다. 본 발명은 가구, 자동차 내장재 등 시트를 부착하여 장식효과가 구현 가능한 용도에 사용가능한 데코시트를 제공하며, 유리의 질감과 유사한 투명층을 포함하여 하부 컬러 또는 장식층의 깊이감과 입체감을 구현하며, 일반적인 아크릴계 제품 대비 제조비용 절감이 가능한 폴리에스테르계 데코시트를 제공한다.

Description

유리 질감의 폴리에스테르계 데코시트
본 발명은 유리 질감의 폴리에스테르 데코시트에 관한 것이다.
가정용 가전제품, 가구, 자동차용 내장재료 등에 다양한 표면 질감을 구현하기 위해 페인트 코팅, 인쇄필름 접착 등을 방법을 활용해 다양한 질감을 구현하고 있다. 그 중에서도 유리 소재는 소재의 투명성, 강한 표면경도, 그리고 소재의 우수한 평탄성으로 인해 거울면과 같은 평탄한 표면질감과 더불어 유리하면에 부착된 컬러층, 디자인층의 깊이감으로 고급 장식 재료로 사용되고 있다.
또한, 그러나, 깨지기 쉬운 재료특성상 취급과정이 까다롭고, 재단/면취 등의 공정상의 어려움, 그리고 플라스틱 재질 대비 무거운 비중으로 인한 최종 제품의 무게 증가 등으로 인한 단점 등이 제품 적용에 걸림돌이 되고 있다.
유리의 단점을 극복하고 유리와 같은 질감을 구현하기 위해 아크릴계, 폴리카보네이트계 소재들이 대체 소재로 일부 적용되고 있으나, 높은 가격으로 인해 광범위한 적용에 제한이 되고 있어, 유리의 단점인 깨지기 쉬운 특성을 극복하고, 아크릴, 폴리카보네이트 대비 경제적인 제조가 가능한 제품의 개발이 요구되고 있다.
(선행기술문헌)
(특허문헌)
(특허문헌 1) 국제공개번호 WO 2012/148099
(특허문헌 2) 국제공개번호 WO 2015/026066
본 발명은 폴리에틸렌테레프탈레이트를 비롯한 폴리에스테르계 소재를 기반으로 유리의 질감을 구현하고, 이를 통해 아크릴 또는 폴리카보네이트 대비 제조원가를 절감할 수 있는 방법을 제공하고자 한다.
상기 과제를 해결하기 위해, 본 발명의 일 측면은 (a) 컬러층, (b) 상기 컬러층 상부에 형성되어 상기 컬러층과 인접한 투명층을 포함하는 데코시트로서, 상기 투명층 두께 : 상기 컬러층의 두께의 비율은 2 내지 19 : 1이며, 상기 컬러층 및 상기 투명층은 폴리에스테르계 재질로 구성된 것을 특징으로 하는 데코시트를 제공한다.
본 발명의 일 구현예에 따르면, 폴리에스테르계 수지를 기반으로 컬러층과 투명 또는 반투명 단일층이 서로 합지되거나 또는 공압출로 적층된 상태로 제조된 다층 데코시트를 제공한다. 투명 또는 반투명 폴리에스테르계 단일층은 유리와 같이 하층 컬러층의 컬러 깊이감을 나타내는 데에 있어서 핵심요소로, 유리와 같은 비정질로서 빛의 투과에 방해를 주지 않고, 공기와 다른 굴절율로 인해 하층의 컬러 또는 질감의 입체감을 부여하는 역할을 한다.
또한 본 발명의 다양한 구현예에 따르면, 컬러층의 깊이감을 유리와 같은 수준으로 향상시키기 위해, 투명 또는 반투명 폴리에스테르계 층을 단일층으로 적용하여 투명층 내 다중 굴절이 발생하지 않도록 설계하여 제조하는 방법을 제공한다.
본 발명은 가구, 자동차 내장재 등 시트를 부착하여 장식효과가 구현 가능한 용도에 사용가능한 데코시트를 제공하며, 유리의 질감과 유사한 투명층을 포함하여 하부 컬러 또는 장식층의 깊이감과 입체감을 구현하며, 일반적인 아크릴계 제품 대비 제조비용 절감이 가능한 폴리에스테르계 데코시트를 제공한다.
도 1은 본 발명의 일 구현예에 따른 데코시트의 단면 구조를 보여주는 개략도이다.
본 발명의 일 측면은 (a) 컬러층, (b) 상기 컬러층 상부에 형성되어 상기 컬러층과 인접한 투명층을 포함하는 데코시트로서, 상기 투명층 두께 : 상기 컬러층의 두께의 비율은 2 내지 19 : 1이며, 상기 컬러층 및 상기 투명층은 폴리에스테르계 고분자 재질로 구성된 것을 특징으로 하는 데코시트에 관한 것이다.
상기 두께에 관한 수치 범위의 하한값 미만인 경우에는 투명층 두께가 상대적으로 작아 유리 질감 효과가 저하될 있고, 상한값을 초과하는 경우에는 컬러층 두께가 상대적으로 작아 차폐성 확보를 위한 컬러 염료 또는 안료의 과도한 투입으로 이어져, 색분포가 균일한 컬러층의 제조가 어려운 압출공정상의 문제가 있을 수 있다.
본 발명에서 목적하는 발명의 효과로서 유리 질감이란 투명한 유리의 하면에 컬러 또는 디자인을 포함한 층이 위치할 경우, 비정질의 유리가 보이는 공기와의 굴절율 차이와 투명층의 가시광 흡수 특성으로 인하여, 하면 디자인층의 미세한 색변화, 그리고 유리표면 및 유리와 하면 컬러층 사이의 계면의 높은 평탄도를 보이게 되고, 또한 이로 인해 컬러층 또는 디자인층이 표면 밑의 깊이 있게 존재하는 느낌을 의미한다.
위 폴리에스테르계 고분자(1삭제)의 한 예로서 폴리에틸렌테레프탈레이트를 들 수 있다.
일 구현예에 따르면, (c) 상기 투명층 위에 형성되어 상기 투명층과 인접한 프라이머층, 및 (d) 상기 프라이머층 위에 형성되어 상기 프라이머층과 인접한 보호코팅층을 추가로 포함한다.
다른 구현예에 따르면, 상기 투명층은 단일층이다. 또 다른 구현예에 따르면, 상기 컬러층은 단일한 색상 또는 복수 개의 색상으로 이루어진 디자인을 포함한다. 본 발명에 있어서 단일층이란 층간 굴절율 차이로 인한 층간 계면을 확인할 수 없을 정도의 균일한 굴절율을 가지거나, 또는 굴절율 차이가 0.01 이내이고 상용성이 있는 동일 폴리에스터계 고분자로 이루어진 2개 이상의 다층 구조를 갖는 층을 의미한다.
또 다른 구현예에 따르면, 상기 투명층 상부에서 BYK사의 micro-TRI-gloss 등의 광택계를 이용하여 ASTM D523에 따라 분석한 광택도(60도)가 4% 내지 100%이고, 특히 바람직하게는 40% 내지 100%이다. 또 다른 구현예에 따르면, 상기 컬러층 하부에서 투명층 상부로의 전체 투과도는 Nippon Denshoku사의 COH-400 등의 장비를 이용하여 ASTM D1003에 따라 분석한 투과율이 0.1% 내지 10%이다. 또 다른 구현예에 따르면, 미놀타사의 CM-2500D 등의 장비를 이용하여 ASTM E1164에 따라 측정한 상기 데코시트의 투명층 방향에서의 색밝기(L)값은 상기 컬러층의 색밝기 지수보다 1% 내지 40% 낮다.
본 발명의 여러 구현예에 따른 무수한 구현예와 이를 벗어나는 수많은 대조예를 제조하여 분석한 결과, 유리 질감과 하부 컬러층의 디자인에 대한 시인성 및 입체감과 최하부 기재층 표면의 결점에 대한 차폐성 등의 물성을 동시에 향상시키기 위해서는 위와 같은 (i) 투명층-컬러층의 이중층 구조와 (ii) 투명층과 컬러층의 두께 비율에 추가하여 위에서 언급한 (iii) 투명층 상부에서 관측한 광택도, (iv) 컬러층에서 투명층으로 측정한 투과도, (v) 컬러층과 투명층의 색밝기 지수 차이가 일정한 범위 내에 있어야 한다는 점을 확인하였다.
즉, 유리 질감과 하부 컬러층의 디자인에 대한 시인성 및 입체감과 최하부 기재층 표면의 결점에 대한 차폐성 등의 물성을 동시에 향상시키기 위해서는 (i) 투명층-컬러층의 이중층 구조를 가져야 하고, (ii) 투명층과 컬러층의 두께 비율이 2 내지 19 : 1이어야 하며, (iii) ASTM D523에 따라 투명층 상부에서 관측한 광택도가 40% 내지 100%이어야 하고, (iv) ASTM D1003에 따라 컬러층 하부에서 투명층 상부로 관측한 데코시트 전체 투과율이 0.1% 내지 10%이어야 하며, (v) ASTM E1164에 따라 측정한 컬러층과 투명층의 색밝기 지수 차이가 1% 내지 40%이어야 하고, 만에 하나 위 5가지의 조건 중 어느 하나라로 만족하지 않는 경우에는 유리 질감과 하부 컬러층의 디자인에 대한 시인성 및 입체감과 최하부 기재층 표면의 결점에 대한 차폐성 등의 물성이 전체적으로 저하되는 것을 확인하였다.
또 다른 구현예에 따르면, 상기 데코시트의 두께는 600 내지 4,000 μm이다. 상기 데코시트 두께에 관한 수치 범위의 하한값 미만인 경우에는 유리질감 및 입체감이 효과적으로 드러나지 않는 문제가 있을 수 있고, 상한값을 초과하는 경우에는 압출공정 과정 중 폴리에스터계 수지의 미세 결정화 진행으로 인해 컬러의 변화, 투과도의 저하, 깊이감의 저하 문제가 있을 수 있다.
또 다른 구현예에 따르면 상기 투명층 상부에 프라이머액과 하드코팅액을 마이크로 그라비아 방식으로 코팅하였고, 또 다른 구현예에 따르면 상기 컬러층에는 입경이 0.1 내지 1 μm인 금속계 또는 무기계 또는 고분자계 입자가 분산되어 있다. 상기 컬러층에는 위에서 언급한 입자가 분산되어 있어서 펄, 무광 또는 반광, 미세한 불균일한 컬러가 표현된다.
또 다른 구현예에 따르면, 상기 컬러층과 상기 투명층은 압출 라미네이션 방법 또는 공압출에 의해 적층된다. 즉, 플라스틱 소재 중 가격이 저렴하고, 투명도가 좋은 폴리에스테르 소재를 이용해서 유리 질감을 구현하기 위해서는 두 가지 방법으로 제조가 가능하다. 첫 번째는 컬러염료 및 안료를 포함한 폴리에스테르 재질의 컬러필름을 압출방식으로 제조하고, 완성된 컬러 필름을 투명 폴리에스테르 압출과정 중 압출 라미네이션하여 컬러층/투명층으로 제조하는 방법이고, 두 번째는 컬러층과 투명층 폴리에스테르 재료를 공압출하여 다층 구조의 시트를 제조하는 방법이다.
이하에서 실시예 등을 통해 본 발명을 더욱 상세히 설명하고자 하며, 다만 이하에 실시예 등에 의해 본 발명의 범위와 내용이 축소되거나 제한되어 해석될 수 없다. 또한, 이하의 실시예를 포함한 본 발명의 개시 내용에 기초한다면, 구체적으로 실험 결과가 제시되지 않은 본 발명을 통상의 기술자가 용이하게 실시할 수 있음은 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연하다.
또한 이하에서 제시되는 실험 결과는 상기 실시예 및 비교예의 대표적인 실험 결과만을 기재한 것이며, 아래에서 명시적으로 제시하지 않은 본 발명의 여러 구현예의 각각의 효과는 해당 부분에서 구체적으로 기재하도록 한다.
실시예
실시예
컬러염료, 안료를 포함한 폴리에스테르계 수지를 기반으로 한 마스터 배치를 포함한 폴리에스테르계 수지, 그리고 폴리에스테르계 버진 원료를 각각의 압출기에 투입하고 270 ℃ 압출 실리더 온도 조건에서 투입하여 압출하고, 각각 용융 압출된 두 성분을 층상 구조의 시트 구조로 만들어주기 위해 피드블록 및 T-die를 통과시키거나, 다층구조의 T-die의 서로 다른 유로에 연결하여 압출하고, 냉각롤을 통과시켜 냉각시킨 후 권취하여 다층구조의 시트를 제조하였다. 투명층과 컬러층의 두께 비율은 본 발명이 목적하는 효과를 달성하기 위해서 2:1 이상 19:1 이하를 확보하는 것이 반드시 필요하며, 본 실시예에서는 투명층과 컬러층의 비율이 4:1인 1 mm 두께의 시트를 제조하였다.
컬러층의 압출성분은 폴리에스테르계 백색 컬러 마스터 배치 10 중량%로 버진 폴리에스테르계 수지에 혼합된 원료를 시간당 100 kg 토출양으로, 투명층 압출 성분이 버진 폴리에스테르계 수지를 시간당 400 kg 토출양으로 공압출하여 2층 구조의 유로기를 지나 T-Die를 거쳐 냉각롤을 통한 냉각하여 두께 1 mm, 컬러층 0.2 mm, 투명층 0.8 mm의 시트를 제조하였다. 제조한 시트의 표면에 프라이머액과 하드코팅액을 마이크로 그라비아 방식으로 코팅 후 열건조, UV 경화 방식으로 각각 건조 및 경화하여 보호코팅층을 형성하여 최종 제품을 제조하였다.
또한, 투명층 상부에서의 광택을 광택계(BYK社, micro-TRI-gloss)를 이용하여 ASTM D523에 따라 측정하였고, 컬러층에서 투과층으로의 전체 투과율은 COH-400(Nippon Denshoku社)으로 ASTM D1003에 따라 측정하였다. 그 결과 광택도는 92%, 전체 투과율은 1.2%이었다.
또한, 데코시트의 투명층 방향에서의 색밝기는 미놀타 CM2500D를 이용하여 D65 광원을 기준으로 측정하여 84.88의 색밝기 지수를 확인하였고, 컬러층 단독의 색밝기는 컬러층 방향에서 동일한 방법으로 측정하여, 92.51의 색밝기 지수를 확인하였다. 이를 통해 투명층 방향에서의 색밝기는 컬러층 대비 8.3% 감소하였다.
비교예 1
실시예와 동일한 공정으로 제조하되, 투명층 압출성분 대신 백색 컬러층 압출성분과 동일한 재료를 투입하여 컬러층과 단일층으로 구성된 1 mm 두께의 시트를 제조하고, 이후 보호코팅층을 형성하여 비교 제품을 제조하였다.
광택도는 91%, 전체 투과율은 0.5%, 컬러면 상하의 색밝기 지수는 각각 92.66, 92.71로 상하면의 색밝기 차이는 0.05%임을 확인하였다.
비교예 2
실시예와 동일한 공정으로 제조하되, 컬러층 압출원료의 컬러 마스터 배치 투입 중량 비율을 1%로 조정하고, 투명층 상부에 실시예와 동일한 보호코팅층을 형성하여 최종 제품을 제조하였다.
광택도는 91.5%, 전체 투과율은 18%, 투명층 방향 색밝기 지수는 73.20, 컬러층 방향 색밝기 지수는 75.82 로 투명층 방향과 컬러층 방향 색밝기 차이는 3.5%임을 확인하였다..
비교예 3
실시예와 동일한 공정으로 제조하되, 압출시 컬러층 원료 투입량을 시간당 400 kg, 투명층 원료를 시간당 100 kg으로 하여 투명층 200 μm, 컬러층 800 μm, 총 두께 1 mm 두께의 시트를 제조하고, 이후 보호코팅층을 형성하여 비교 제품을 제조하였다.
광택도는 91.8%, 전체 투과율은 0.3%, 투명층 방향 색밝기 지수는 92.24, 컬러층 방향 색밝기 지수는 92.98 로 투명층 방향과 컬러층 방향 색밝기 차이는 0.8%임을 확인하였다.
비교예 4
실시예와 동일한 공정으로 제조하되, 압출 시 라인 스피드를 변경하여 0.4 mm 두께의 시트를 제조하고, 이후 보호코팅층을 형성하여 비교 제품을 제조하였다.
광택도는 92%, 전체 투과율은 0.6%, 투명층 방향 색밝기 지수는 91.94, 컬러층 방향 색밝기 지수는 92.77 로 투명층 방향과 컬러층 방향 색밝기 차이는 0.9%임을 확인하였다.
시험예 1 및 비교시험예 1 내지 4
위 실시예 1과 비교예 1 내지 4에서 제조한 데코시트에 대해서 ① 유리와의 질감 유사성, ② 하부 컬러층의 디자인에 대한 시인성, ③ 깊이감 또는 입체감, ④ 최하부 기재층 표면의 결점에 대한 차폐성, ⑤ 색분포 균일성의 5개 항목에 대해 관능 검사를 실시하였다.
관능 검사 요원은 30세에서 50세 사이의 남성 50명과 여성 50명, 총 100명이었으며, 안정된 판단 결과가 나올 수 있도록 전 검사 요원에 대해 검사 전 1 시간에 걸친 공통 훈련 과정을 이수하도록 하였다.
위 5가지 항목에 대해 가장 저조한 물성은 0점, 가장 우수한 물성은 10점으로 하여 10점 만점을 기준으로 평가하였으며, 100명의 관능 검사 결과값을 평균하여 다음 표 1과 같은 결과를 얻었다.
검사항목 ① ② ③ ④ ⑤
실시예 1 9.6 9.4 9.1 9.5 9.4
비교예 1 3.4 9.4 1.1 9.4 9.4
비교예 2 4.7 5.3 7.5 2.0 6.3
비교예 3 5.4 9.3 3.2 7.1 9.2
비교예 4 2.8 9.4 3.0 5.2 7.1
검사 항목: ① 유리와의 질감 유사성, ② 하부 컬러층의 디자인에 대한 시인성, ③ 깊이감 또는 입체감, ④ 최하부 기재층 표면의 결점에 대한 차폐성, ⑤ 색분포 균일성
본 명세서에는 지면 관계상 모두 제시하지는 않았지만, 위에서도 언급한 바와 같이 아래 5가지 항목과 수치 범위를 만족하는 무수한 실시예와 이들 중 어느 하나라로 만족하지 않는 수많은 비교예를 분석하였으며, 그 결과 아래와 같은 5개의 항목이 데코시트가 갖추어야 하는 위 검사 항목을 전체적으로 구비하는데 중요한 역할을 하는 파라미터로 도출할 수 있었으며, 특이하게도 아래 항목 중 어느 하나라도 만족하지 않는 경우에는 위 5개의 검사 항목의 물성이 전체적으로 저하되는 것을 확인하였다.
(i) 투명층-컬러층의 이중층 구조, (ii) 투명층과 컬러층의 두께 비율이 2 내지 19 : 1, (iii) ASTM D523에 따라 투명층 상부에서 관측한 광택도가 40% 내지 100%, (iv) ASTM D1003에 따라 컬러층 하부에서 투명층 상부로 관측한 데코시트 전체 투과율이 0.1% 내지 10%, (v) ASTM E1164에 따라 측정한 컬러층과 투명층의 색밝기 지수 차이가 1% 내지 40%

Claims (7)

  1. (a) 컬러층, (b) 상기 컬러층 상부에 형성되어 상기 컬러층과 인접한 투명층을 포함하는 데코시트로서,
    상기 투명층 두께 : 상기 컬러층의 두께의 비율은 2 내지 19 : 1이며,
    상기 컬러층 및 상기 투명층은 폴리에스테르계 재질로 구성된 것을 특징으로 하는 데코시트.
  2. 제1항에 있어서, (c) 상기 투명층 위에 형성되어 상기 투명층과 인접한 프라이머층, 및 (d) 상기 프라이머층 위에 형성되어 상기 프라이머층과 인접한 보호코팅층을 추가로 포함하는 것을 특징으로 하는 데코시트.
  3. 제1항 또는 제2항에 있어서, 상기 투명층은 단일층이고,
    상기 컬러층은 단일한 색상 또는 복수 개의 색상으로 이루어진 디자인을 포함하는 것을 특징으로 하는 데코시트
  4. 제3항에 있어서, 상기 투명층 상부에 대해 ASTM D523에 따라 분석한 광택도는 4% 내지 100%이고,
    ASTM D1003에 따라 상기 컬러층에서 상기 투과층으로 분석한 데코시트 전체 투과율은 0.1% 내지 10%이며,
    ASTM E1164에 따라 분석한 상기 투명층과 상기 컬러청의 색밝기 지수의 차이는 1% 내지 40%인 것을 특징으로 하는 데코시트.
  5. 제4항에 있어서, 상기 데코시트의 두께는 600 내지 5,000 μm인 것을 특징으로 하는 데코시트.
  6. 제5항에 있어서, 상기 투명층 상부에는 광택이 4% 내지 100%로 조절된 하드코팅층이 있고,
    상기 컬러층에는 입경이 0.1 내지 1 μm인 금속계 또는 무기계 또는 고분자계 입자가 분산되어 있는 것을 특징으로 하는 데코시트.
  7. 제6항에 있어서, 상기 컬러층과 상기 투명층은 공압출 또는 압출 라미네이션 방법에 의해 적층되는 것을 특징으로 하는 데코시트.
PCT/KR2018/000129 2017-01-04 2018-01-03 유리 질감의 폴리에스테르계 데코시트 Ceased WO2018128392A1 (ko)