ES2155853T3 - Metodo de fabricacion de acero fundido de bajo contenido en carbono por desgasificacion y descarburacion en vacio. - Google Patents

Metodo de fabricacion de acero fundido de bajo contenido en carbono por desgasificacion y descarburacion en vacio.

Info

Publication number
ES2155853T3
ES2155853T3 ES94917160T ES94917160T ES2155853T3 ES 2155853 T3 ES2155853 T3 ES 2155853T3 ES 94917160 T ES94917160 T ES 94917160T ES 94917160 T ES94917160 T ES 94917160T ES 2155853 T3 ES2155853 T3 ES 2155853T3
Authority
ES
Spain
Prior art keywords
degasification
gas
vacuum
carbon content
low carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES94917160T
Other languages
English (en)
Inventor
Yasuo Obana
Koichi Endoh
Makoto Moriguchi
Toshihiko Kaku
Shigenori Yagura
Fumio Hayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Application granted granted Critical
Publication of ES2155853T3 publication Critical patent/ES2155853T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

CON LA PRESENTE INVENCION SE PUEDE REDUCIR EL COSTE DE GAS EN UN PROCESO DE DESGASIFICACION Y DESCARBONIZACION AL VACIO MEDIANTE LA UTILIZACION DE UN GAS DE CO{SUB,2} COMO GAS DE REFLUJO Y UN GAS DE AGITACION SIN PROVOCAR LA PARADA DE LA DESCARBONIZACION, NI UN AUMENTO DE LA CONCENTRACION DE CARBONO, NI UN AUMENTO EN LA CANTIDAD DE ADICION DE UNA ALEACION. LA PRESENTE INVENCION SE REFIERE A UN METODO PARA LA FABRICACION DE ACERO FUNDIDO CON UN BAJO CONTENIDO DE CARBONO MEDIANTE UN PROCESO DE DESGASIFICACION Y DESCARBONIZACION AL VACIO QUE CONSISTE EN SOPLAR UN GAS DE CO{SUB,2} EN UN HORNO DESDE EL MOMENTO EN QUE COMIENZA LA DESGASIFICACION HASTA EL MOMENTO EN QUE SE ALCANZA UNA CONCENTRACION DE CARBONO EN EL ACERO FUNDIDO DE 50 PPM EN UN PROCESO DE DESGASIFICACION Y DESCARBONIZACION AL VACIO DEL ACERO FUNDIDO Y DESPUES SE UTILIZA UN GAS DE AR.
ES94917160T 1993-06-04 1994-06-06 Metodo de fabricacion de acero fundido de bajo contenido en carbono por desgasificacion y descarburacion en vacio. Expired - Lifetime ES2155853T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP13433393 1993-06-04

Publications (1)

Publication Number Publication Date
ES2155853T3 true ES2155853T3 (es) 2001-06-01

Family

ID=15125893

Family Applications (1)

Application Number Title Priority Date Filing Date
ES94917160T Expired - Lifetime ES2155853T3 (es) 1993-06-04 1994-06-06 Metodo de fabricacion de acero fundido de bajo contenido en carbono por desgasificacion y descarburacion en vacio.

Country Status (9)

Country Link
US (1) US5693120A (es)
EP (1) EP0707080B1 (es)
JP (1) JP3176374B2 (es)
KR (1) KR0159182B1 (es)
CN (1) CN1037783C (es)
BR (1) BR9406712A (es)
CA (1) CA2163893C (es)
ES (1) ES2155853T3 (es)
WO (1) WO1994029488A1 (es)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4328045C2 (de) * 1993-08-20 2001-02-08 Ald Vacuum Techn Ag Verfahren zum Entkohlen von kohlenstoffhaltigen Metallschmelzen
US5603749A (en) * 1995-03-07 1997-02-18 Bethlehem Steel Corporation Apparatus and method for vacuum treating molten steel
KR100270113B1 (ko) * 1996-10-08 2000-10-16 이구택 극저탄소강의 용강 제조장치
KR100627468B1 (ko) * 2000-05-18 2006-09-22 주식회사 포스코 용강의 저취 교반방법
US6764528B2 (en) * 2000-12-13 2004-07-20 Jfe Steel Corporation Process for producing high-nitrogen ultralow-carbon steel
RU2215047C2 (ru) * 2001-12-25 2003-10-27 Открытое акционерное общество "Новолипецкий металлургический комбинат" Устройство для циркуляционного вакуумирования стали
EP1568790A1 (fr) * 2004-02-24 2005-08-31 Paul Wurth S.A. Dispositif pour le traitement de métal liquide en poche
CN102146494A (zh) * 2010-02-05 2011-08-10 鞍钢股份有限公司 一种细小氧化物弥散钢的生产方法
CN102146501B (zh) * 2010-02-05 2013-07-03 鞍钢股份有限公司 一种vod喷吹co2生产不锈钢的精炼方法
CN102146498A (zh) * 2010-02-05 2011-08-10 鞍钢股份有限公司 一种ans精炼炉喷吹co2生产低碳钢的精炼方法
RU2430974C1 (ru) * 2010-04-30 2011-10-10 Владимир Викторович Тиняков Способ вакуумирования стали
CA2755110C (en) 2010-10-13 2014-07-15 Unisearch Associates Inc. Method and apparatus for improved process control and real-time determination of carbon content during vacuum degassing of molten metals
CN102560002A (zh) * 2010-12-11 2012-07-11 鞍钢股份有限公司 一种去除钢液中细小夹杂物的方法及喷吹装置
CN108330253A (zh) * 2018-01-24 2018-07-27 北京首钢国际工程技术有限公司 一种用vd装置生产超低碳钢的方法
CN113614255A (zh) * 2019-02-13 2021-11-05 沙特基础工业全球技术公司 利用二氧化碳进行钢脱碳
CN109680125B (zh) * 2019-02-19 2021-01-26 南京钢铁股份有限公司 采用二氧化碳作为提升气体的真空精炼方法
CN110592325B (zh) * 2019-10-30 2021-06-22 攀钢集团攀枝花钢铁研究院有限公司 一种钢水的rh深脱碳的方法
CN110976787B (zh) * 2019-12-13 2021-08-17 首钢集团有限公司 一种超低碳钢的中包保护浇铸方法
CN110982992A (zh) * 2019-12-16 2020-04-10 首钢集团有限公司 一种rh真空脱碳方法
CN112226582A (zh) * 2020-08-26 2021-01-15 南京钢铁股份有限公司 一种rh精炼深度净化钢液的方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4071356A (en) * 1976-11-24 1978-01-31 Nippon Steel Corporation Method for refining a molten steel in vacuum
JPS5644711A (en) * 1979-09-17 1981-04-24 Nippon Kokan Kk <Nkk> Decarbonization method of molten steel under reduced pressure
SU901298A1 (ru) * 1980-04-22 1982-01-30 Московский Ордена Трудового Красного Знамени Институт Стали И Сплавов Способ обезуглероживани нержавеющих сталей
JPS6119727A (ja) * 1984-07-04 1986-01-28 Sumitomo Metal Ind Ltd 真空脱ガス設備排ガスの処理方法
JPS63111116A (ja) * 1986-10-29 1988-05-16 Sumitomo Metal Ind Ltd 真空脱ガス設備排ガスの使用方法
JPH02267213A (ja) * 1989-04-05 1990-11-01 Sumitomo Metal Ind Ltd 溶鋼の真空脱炭方法
JPH0361317A (ja) * 1989-07-27 1991-03-18 Nkk Corp 極低炭素鋼の溶製方法
JP2855867B2 (ja) * 1990-10-01 1999-02-10 大同特殊鋼株式会社 含クロム溶鋼の精錬法

Also Published As

Publication number Publication date
KR960702869A (ko) 1996-05-23
US5693120A (en) 1997-12-02
CN1037783C (zh) 1998-03-18
JP3176374B2 (ja) 2001-06-18
KR0159182B1 (ko) 1999-01-15
EP0707080B1 (en) 2001-04-04
BR9406712A (pt) 1996-03-19
EP0707080A1 (en) 1996-04-17
WO1994029488A1 (en) 1994-12-22
CN1126497A (zh) 1996-07-10
CA2163893A1 (en) 1994-12-22
CA2163893C (en) 1999-07-27
EP0707080A4 (en) 1996-07-03

Similar Documents

Publication Publication Date Title
ES2068982T3 (es) Procedimiento para la eliminacion de iones de metales pesados del vino y de bebidas similares al vino.
ES2189186T3 (es) Polvo de acero inoxidable.
NO20073032L (no) Fremgangsmate for rensing av silisium samt silisium
ES390792A1 (es) Procedimiento para estabilizar peroxido de hidrogeno.
DE50214513D1 (de) Vorrichtung zur erzeugung eines brennbaren gasgemisches
ES2181905T3 (es) Metodo para afino a vacio de acero fundido.
DE602005001248D1 (de) Verfahren zur Reduzierung des Sauerstoffgehalts eines Pulvers und das daraus hergestellte Produkt.
MX168339B (es) Conversion del metano
ES444545A1 (es) Un procedimiento para el afino de un metal a base de hierro fundido que contiene azufre, silicio y carbono.
MX171800B (es) Procedimiento mejorado para eliminar el sulfuro de hidrogeno prsente en un gas conteniendo oxigeno
GB1034333A (en) Improvements in or relating to the manufacture of flat glass
ES2045606T3 (es) Metodo para refinar acero al cromo fundido.
MX2023014739A (es) Metodo de desnitrificacion de acero fundido y metodo de produccion de acero.
CA2042773A1 (en) Method of producing ultra-low-carbon steel
UA89061C2 (ru) Способ получения циклопентанона и применение углеводородной смеси, которая содержит циклопентен
GB1013190A (en) Process for producing a low-temperature tough steel
GB1115552A (en) Method of producing low oxygen silicon-iron
ES2104896T3 (es) Un metodo para la produccion de acero inoxidable.
GB1109844A (en) Method of producing nonageing extra deep drawing cold-rolled steel sheet
SE9402119D0 (sv) Solution
AR031115A1 (es) Un proceso para la preparacion de una solucion acuosa de un principio activo de naturaleza fenolica, sensible a la oxidacion, utilizacion de dicha solucion y soluciones inyectables
ES2027940T1 (es) Metodo de aumentar la moldeabilidad del acero antes de su tratamiento final.
SU492587A1 (ru) Сталь
SU115914A1 (ru) Способ изготовлени сталей
UA153725U (uk) Спосіб виробництва бутильованої води тривалого зберігання

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 707080

Country of ref document: ES