JPH0354975B2 - - Google Patents
Info
- Publication number
- JPH0354975B2 JPH0354975B2 JP14995485A JP14995485A JPH0354975B2 JP H0354975 B2 JPH0354975 B2 JP H0354975B2 JP 14995485 A JP14995485 A JP 14995485A JP 14995485 A JP14995485 A JP 14995485A JP H0354975 B2 JPH0354975 B2 JP H0354975B2
- Authority
- JP
- Japan
- Prior art keywords
- membered heterocyclic
- oxygen
- oxidizing agent
- heterocyclic compound
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は導電性膜の製造方法に関する。詳しく
は、特定の方法で複素５員環式化合物重合体の膜
を製造する方法に関する。
は、特定の方法で複素５員環式化合物重合体の膜
を製造する方法に関する。
複素５員環式化合物が酸化剤によつて重合体を
生成することはすでに知られている（アドバンシ
ス イン ヘテロサイクリツク ケミストリー
15巻 67ページ（1973））。又、電解重合法によつ
て複素５員環式化合物の膜を製造する方法もすで
に知られている（例えば、ジヤーナル オブ ケ
ミカル ソサエテイ ケミカル コミユニケーシ
ヨン（1979）635ページ、ジヤパン ジヤーナル
オブ アプライド フイジツクス21巻L562
（1982）及び同誌23巻L527（1984））。
生成することはすでに知られている（アドバンシ
ス イン ヘテロサイクリツク ケミストリー
15巻 67ページ（1973））。又、電解重合法によつ
て複素５員環式化合物の膜を製造する方法もすで
に知られている（例えば、ジヤーナル オブ ケ
ミカル ソサエテイ ケミカル コミユニケーシ
ヨン（1979）635ページ、ジヤパン ジヤーナル
オブ アプライド フイジツクス21巻L562
（1982）及び同誌23巻L527（1984））。
しかしながら、電解重合法による方法で特殊な
装置及び電解質が必要であるという問題がある。
そこで本発明者らは、特定の方法で酸化剤を用い
て複素５員環式化合物の重合体の膜を製造する方
法を先に提案した（特願昭59−171430号）。
装置及び電解質が必要であるという問題がある。
そこで本発明者らは、特定の方法で酸化剤を用い
て複素５員環式化合物の重合体の膜を製造する方
法を先に提案した（特願昭59−171430号）。
この方法は高価な電解質とか特別の電解反応用
の装置を必要としないなど優れた方法であるが、
均一の膜を製造するためにはかなりの熟練を必要
とする上に、反応に一定の時間を要するという問
題があつた。
の装置を必要としないなど優れた方法であるが、
均一の膜を製造するためにはかなりの熟練を必要
とする上に、反応に一定の時間を要するという問
題があつた。
本発明者らは上記問題点を解決して、簡便に導
電性膜を製造する方法について鋭意検討し、本発
明を完成した。
電性膜を製造する方法について鋭意検討し、本発
明を完成した。
即ち、本発明は酸化剤を溶解した溶液中に複素
５員環式化合物を加え混合した後不溶分をを分離
して得た溶液を基材上に塗布あるいは流延した
後、酸素の存在下で溶媒を除去することを特徴と
する導電性膜の製造方法である。
５員環式化合物を加え混合した後不溶分をを分離
して得た溶液を基材上に塗布あるいは流延した
後、酸素の存在下で溶媒を除去することを特徴と
する導電性膜の製造方法である。
本発明において使用する酸化剤としては、無機
酸、金属化合物が有効であり、硫酸、塩酸、硝
酸、クロルスルホン酸などが無機酸の具体例とし
て挙げられ、金属化合物としてはルイス酸として
知られる化合物が好ましく用いられ、アルミニウ
ム、錫、チタン、ジルコニウム、クロム、マンガ
ン、鉄、銅、モリブデン、タングステン、ルテニ
ウム、パラジウム、白金などの金属の塩化物、硫
酸塩、硝酸塩、アセチルアセトナート化合物など
が具体例として挙げられる。又、ペルオキソニ硫
酸あるいは過炭酸の塩なども好ましく使用でき
る。さらに、ペンゾキノン、ジアゾニウム塩など
の有機化合物も使用可能である。これらの酸化剤
は２種以上混合して用いることも可能である。
酸、金属化合物が有効であり、硫酸、塩酸、硝
酸、クロルスルホン酸などが無機酸の具体例とし
て挙げられ、金属化合物としてはルイス酸として
知られる化合物が好ましく用いられ、アルミニウ
ム、錫、チタン、ジルコニウム、クロム、マンガ
ン、鉄、銅、モリブデン、タングステン、ルテニ
ウム、パラジウム、白金などの金属の塩化物、硫
酸塩、硝酸塩、アセチルアセトナート化合物など
が具体例として挙げられる。又、ペルオキソニ硫
酸あるいは過炭酸の塩なども好ましく使用でき
る。さらに、ペンゾキノン、ジアゾニウム塩など
の有機化合物も使用可能である。これらの酸化剤
は２種以上混合して用いることも可能である。
上記酸化剤を溶解せしめる溶媒としては、アル
コール類、ハロゲン化炭化水素類、芳香族炭化水
素類、エーテル類、水などが使用でき、好ましく
は、１当り上記酸化剤を0.01ｇ以上 溶解し得
るものである。
コール類、ハロゲン化炭化水素類、芳香族炭化水
素類、エーテル類、水などが使用でき、好ましく
は、１当り上記酸化剤を0.01ｇ以上 溶解し得
るものである。
本発明において複素５員環式化合物としては、
ピロール類、チオフエン類、フラン類、セレノフ
エン類、テルロフエン類が具体例として挙げられ
中でもピロール、Ｎ−置換ピロール、３−及び／
又は４−置換ピロール類が反応性も高く好まし
い。
ピロール類、チオフエン類、フラン類、セレノフ
エン類、テルロフエン類が具体例として挙げられ
中でもピロール、Ｎ−置換ピロール、３−及び／
又は４−置換ピロール類が反応性も高く好まし
い。
複素５員環式化合物の使用量としては酸化剤１
モル当り0.1〜100モル、通常当モル〜10モルが適
当である。
モル当り0.1〜100モル、通常当モル〜10モルが適
当である。
酸化剤溶液中と複素５員環式化合物の混合は温
度、時間、混合方法については特に限定はなく、
室温で数分〜数十分行えば充分である。混合後不
溶分は分離除去される。分離法としてはデカンテ
ーシヨン、あるいは別など通常の方法が採用でき
る。こうして得られた均一溶液は、適当な基材上
に塗布あるいは流し込むことで一定の形状とし、
次いで溶媒を除去することで導電性の膜とするこ
とができる。
度、時間、混合方法については特に限定はなく、
室温で数分〜数十分行えば充分である。混合後不
溶分は分離除去される。分離法としてはデカンテ
ーシヨン、あるいは別など通常の方法が採用でき
る。こうして得られた均一溶液は、適当な基材上
に塗布あるいは流し込むことで一定の形状とし、
次いで溶媒を除去することで導電性の膜とするこ
とができる。
本発明において肝要なのは溶媒を除去する操作
を酸素の存在下に行うことにある。酸素としては
純酸素のみならず他の不活性ガスで希釈して用い
ることも可能であり、空気を酸素源として使用す
ることもできる。溶媒の除去は、酸素又は酸素含
有ガスの気流下に必要に応じ塗膜等を加熱するこ
とで達成される。
を酸素の存在下に行うことにある。酸素としては
純酸素のみならず他の不活性ガスで希釈して用い
ることも可能であり、空気を酸素源として使用す
ることもできる。溶媒の除去は、酸素又は酸素含
有ガスの気流下に必要に応じ塗膜等を加熱するこ
とで達成される。
本発明の方法を実施することによつて複素５員
環式化合物重合体からなる導電性膜を簡単に製造
することが可能となり、工業的に極めて価値があ
る。
環式化合物重合体からなる導電性膜を簡単に製造
することが可能となり、工業的に極めて価値があ
る。
以下、実施例を挙げ本発明をさらに説明する。
実施例 １
酸化剤として塩化第二鉄・６水和物10ｇをメタ
ノール50mlに溶解した溶液をピロール５mlをメタ
ノール20mlに溶解した溶液に撹拌しながらゆつく
り加えた。約１時間撹拌した後過し不溶分を除
いた。こうして得られた均一溶液をガラス板上に
塗布し、酸素気流下でメタノールを除去した。ガ
ラス板上に生成したポリピロール膜の厚みは約
10μｍであり、その四探針法による比抵抗は1.1×
100Ωcmであつた。
ノール50mlに溶解した溶液をピロール５mlをメタ
ノール20mlに溶解した溶液に撹拌しながらゆつく
り加えた。約１時間撹拌した後過し不溶分を除
いた。こうして得られた均一溶液をガラス板上に
塗布し、酸素気流下でメタノールを除去した。ガ
ラス板上に生成したポリピロール膜の厚みは約
10μｍであり、その四探針法による比抵抗は1.1×
100Ωcmであつた。
実施例 ２
実施例１と同様にして調製した均一溶液をシヤ
ーレに薄く入れ、空気中で乾燥した後、メタノー
ルを入れて薄膜をはがした。薄膜の厚みは0.1mm
であつた。メタノールで塩化鉄を洗い流した後の
比抵抗は2.4×101Ωcmであつた。
ーレに薄く入れ、空気中で乾燥した後、メタノー
ルを入れて薄膜をはがした。薄膜の厚みは0.1mm
であつた。メタノールで塩化鉄を洗い流した後の
比抵抗は2.4×101Ωcmであつた。
比較例 １
実施例２と同様の操作を窒素気流下で行つた。
得られた薄膜の比抵抗は6.7×102Ωcmであつた。
得られた薄膜の比抵抗は6.7×102Ωcmであつた。
実施例 ３
実施例１と同様の操作を、ピロールのかわりに
Ｎ−メチルピロールを用いて行つた。得られた薄
膜の比抵抗は3.8×104Ωcmであつた。
Ｎ−メチルピロールを用いて行つた。得られた薄
膜の比抵抗は3.8×104Ωcmであつた。
比較例 ２
実施例３と同様の操作を窒素気流下で行つた。
得られた薄膜の比抵抗は4.6×106Ωcmであつた。
得られた薄膜の比抵抗は4.6×106Ωcmであつた。
Claims (1)
- １ 酸化剤を溶解した溶液と複素５員環式化合物
を混合した後、不溶分を分離して得た溶液を基材
上に塗布あるいは流延した後、酸素の存在下に溶
媒を除去することを特徴とする導電性膜の製造方
法。