JPH0364334A - ポリオレフィン微多孔膜 - Google Patents

ポリオレフィン微多孔膜

Info

Publication number
JPH0364334A
JPH0364334A JP1201785A JP20178589A JPH0364334A JP H0364334 A JPH0364334 A JP H0364334A JP 1201785 A JP1201785 A JP 1201785A JP 20178589 A JP20178589 A JP 20178589A JP H0364334 A JPH0364334 A JP H0364334A
Authority
JP
Japan
Prior art keywords
polyolefin
molecular weight
weight
solvent
average molecular
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP1201785A
Other languages
English (en)
Other versions
JPH06104736B2 (ja
Inventor
Kotaro Takita
耕太郎 滝田
Koichi Kono
公一 河野
Tatsuya Takashima
高嶋　達也
Kenkichi Okamoto
岡本　健吉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tonen General Sekiyu KK
Original Assignee
Tonen Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=16446897&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JPH0364334(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Tonen Corp filed Critical Tonen Corp
Priority to JP1201785A priority Critical patent/JPH06104736B2/ja
Priority to EP90310331A priority patent/EP0476198B2/en
Priority to US07/585,461 priority patent/US5051183A/en
Publication of JPH0364334A publication Critical patent/JPH0364334A/ja
Publication of JPH06104736B2 publication Critical patent/JPH06104736B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、超高分子量ポリオレフィンを含有するポリオ
レフィン組成物の微多孔膜及びその製造方法に関し、特
に、生産性の良いポリオレフィン微多孔膜及びその製造
方法に関する。
〔従来の技術〕
微多孔膜は、電池用セパレーター、電解コンデンサー用
隔膜、各種フィルター、透湿防水衣料、逆浸透濾過膜、
限外濾過膜、精密濾過膜等の各種用途に用いられている
。
従来、ポリオレフィン微多孔膜の製造方法としては、例
えば異種ポリマー等の微粉体からなる孔形成剤をポリオ
レフィンに混合してミクロ分散させた後、孔形成剤を抽
出する混合抽出法、ポリオレフィン相を溶媒でミクロ相
分離することにより多孔構造とする相分離法、異種固体
がミクロ分散しているポリオレフィン成形体に延伸など
の歪を与えることにより、異種固体間を界面破壊して空
孔を生じさせて多孔化する延伸法などが行われている。
しかし、これらの方法では通常分子量が５０万未満程度
のポリオレフィンが用いられているため、延伸による薄
膜化及び高強度化には限界があった。
最近、高強度及び高弾性のフィルムに成形し得る超高分
子量ポリオレフィンが開発され、これによ゛る高強度の
微多孔膜の製造が種々提案された。
例えば特開昭５８−５２２８号は、超高分子量ポリオレ
フィンを不揮発性溶媒に溶解し、この溶液から繊維また
はフィルムなどのゲルを成形し、この溶媒を含むゲルを
揮発性溶剤で抽出処理した後、加熱延伸する方法を開示
している。しかしながら、不揮発性溶媒で高度に膨潤し
た多孔性組織を有するゲルは、２方向に延伸しようとし
ても、高配向の延伸ができず、網状組織の拡大により破
断し易く、得られるフィルムは強度が小さく、また形成
される孔径が大きくなるという欠点があった。
方不揮発性溶媒を揮発性溶剤で抽出した後に乾燥したゲ
ルは、網状組織が収縮緻密化するが、揮発性溶剤の不均
一な蒸発によりフィルム原反にそりが発生し易く、また
収縮緻密化により、高倍率の延伸ができないという欠点
があった。
これに対し、重量平均分子量が、５×１０５以上の超高
分子量ポリオレフィンを溶媒中で加熱溶解した溶液から
ゲル状シートを成形し、前記ゲル状シート中の溶媒量を
脱溶媒処理により調製し、次いで加熱延伸した後、残留
溶媒を除去することにより、超高分子量ポリオレフィン
（ポリエチレン）の微多孔膜を製造する方法が、以下に
示すように種々提案されている。
特開昭６０−２４２０３５号は、重量平均分子量が５×
１０５以上の超高分子量ポリエチレンを溶媒中で加熱溶
解した溶液からゲル状のシートを成形し、前記ゲル状シ
ートの溶媒量を１０〜８０重量％に脱溶媒処理し、次い
で加熱延伸した後、残留溶媒を除去することにより、厚
さが１０−以下、破断強度が２００ｋｇ／ｃｄ以上、空
孔率が３０％以上である超高分子量ポリエチレンの微多
孔膜を製造する方法を開示している。
特開昭６１−４９５１３２号は、重量平均分子量が５×
１０５以上の外オレフィンの重合体の溶液からゲル状物
を形成し、前記ゲル状成形物をそれに含まれる溶媒の少
なくとも１０重量％を除去して前記ゲル状成形物に含ま
れる前記Ｒオレフィン重合体が１０〜９０重遣％になる
ようにした後、前記α〜才レフィン重合体の融点＋１０
℃以下の温度で延伸し、得られた延伸成形物に含まれる
残存溶媒を除去することを特徴とする微多孔膜の製造方
法を開示している。
また特開昭６１−１９５１３３号は、重量平均分子量が
５Ｘ］、Ｏ５以上のωオレフィン重合体からなり、平均
孔径０．００１〜１ｍ、空孔率３０〜９０％を有し、ｌ
軸方向に２倍以上、面倍率で２０倍以上延伸してなるこ
とを特徴とする微多孔膜を開示している。
一方特開昭６３−３９６０２号は、重量平均分子量が５
Ｘ１．０’以上のポリエチレン溶液からゲル状成形物を
成形し、前記ゲル状成形物中の溶媒量を８０重置端を超
える９５重量％以下の範囲とし、次いで１２０℃以下の
温度で１軸方向に２倍以上、面倍率で２０倍以上延伸し
た後、残存溶媒を除去することにより、１００１／　ｒ
ｒＩ−ｈｒ−ａｔｅ以上の純水透過速度と、５０％以上
のγ−グロブリンに対する阻止率を有するポリエチレン
微多孔膜を製造する方法を開示している。このポリエチ
レン微多孔膜は、通水性に優れ、かつ蛋白質溶液等の分
離に適した微細孔径を有するものである。
さらに特開昭６３−２７３６５１号は、重量平均分子量
が５Ｘ１．０’以−Ｌの超高分子量ポリオレフィンの溶
液を調製し、前記溶液をゲル化温度以下に急冷しながら
、ダイスより押し出してゲル状成形物中の前記超高分子
量ポリオレフィンの含有量を１０〜９０重量％にし、前
記超高分子量ポリオレフィンの融点＋１０℃以下の温度
で延伸し、しかる後残存溶媒を除去することを特徴とす
る方法を開示している。
この方法は、ｗｉ、多孔膜を１（ｂｃ＋ｎより厚く製造
することができるため、大きな強度と、耐圧性を要する
用途等に好適な微多孔膜を得ることができる。
〔発明が解決しようとする課題〕
しかしながら、上記超高分子量ポリオレフィン（ポリエ
チレン）ｙａ多孔膜の製造方法は、いずれも超高分子量
ポリオレフィンを２軸延伸するために、ポリオレフィン
の希薄溶液を調製する必要があり、このため得られた溶
液は、シート成形するダイス出口でスウェルやネックイ
ンが大きく、シートａ形が困難であり、さらにシート中
には、溶媒が過剰に含まれているため、そのまま延伸し
ても目的の微多孔膜は得られないので脱溶媒処理してシ
ート中の溶媒量を調製する必要がある等、生産性におい
て問題があった。
従って、本発明の目的は、延伸性が良好で、高濃度溶液
とすることが可能なポリオレフィン組成物からなるポリ
オレフィン微多孔膜を提供することである。
また本発明のもう一つの目的は、延伸性を損なうことな
く、ポリオレフィンの高濃度溶液からポリオレフィン微
多孔膜を効率良く製造する方法を提供することである。
〔課題を解決するための手段〕
上記目的に鑑み鋭意研究の結果、本発明者らは、超高分
子量ポリオレフィンを所定１以上含有し、重量平均分子
１７数平均分子量を所定の範囲まで大きくしたポリオレ
フィン組成物を用いれば、高濃度溶液が調製でき、この
溶液から各種特性の良好なポリオレフィン微多孔膜を効
率良く製造することができることを見出し、本発明に想
到した。
すなわち、本発明のポリオレフィン微多孔膜は、Ｍ量平
均分子量が７　Ｘ　１０’以上の超高分子量ポリオレフ
ィンを１重量％以上含有し、重量平均分子量／数平均分
子量が１０〜３００のポリオレフィン組成物からなり、
厚さが０．１〜２５ｍで、空孔率が３５〜９５％で、平
均貫通孔径が０．００１〜０．２．ｍであり、１５ｍｍ
幅の破断強度が０．２ｋｇ以上であることを特徴とする
。
また、かかるポリオレフィン微多孔膜を製造する本発明
の方法は、重量平均分子量が７Ｘ１０’以上の超高分子
量ポリオレフィンを１重量％以上含有し、重量平均分子
量／数平均分子量が１０〜３０［］のポリオレフィン組
組物１０〜３０重量と、溶媒５０〜９０重１％とからな
る溶液を調製し、前記溶液をダイより押出し、冷却して
ゲル状組成物を形成し、前記ゲル状組成物を前記ポリオ
レフィン組成物の融点＋１０℃以下の温度で延伸し、し
かる後残存溶剤を除去することを特徴とする。
本発明を以下詳細に説明する。
先ず本発明のポリオレフィン微多孔膜について説明する
。
本発明のポリオレフィン微多孔膜は、重量平均分子量が
７　Ｘ　１０５以上の超高分子量ポリオレフィンを１重
量％以上含有し、重量平均分子量／数平均分子量が１０
〜３００のポリオレフィン組成物からなる。
上記ポリオレフィン組成物の重量平均分子量／数平均分
子量は、１０〜３００、好ましくは１２〜２５０である
。重量平均分子量／数平均分子量が１０未満では、平均
分子鎖長が大きく、溶解時の分子鎮同志の絡み合い密度
が高くなるため、高濃度溶液の調製が困難である。また
３００を超えると、延伸時に低分子！成分の破断が起こ
り層全体の強度が低下する。
なお、重量平均分子量／数平均分子量は、分子量分布の
尺度として用いられるものであり、この分子量の比が大
きくなるほど分子量分布の幅は拡大する。すなわち重量
平均分子量の異なるポリオレフィンからなる組成物にお
いては、組成物の分子量の比が大きいほど、配合するポ
リオレフィンの重量平均分子量の差が大きく、また小さ
いほどｆｆ１ｆｆｉ平均分子量の差が小さいことを示し
ている。
本発明においては、ポリオレフィン組成物の重量平均分
子量／数平均分子量を１０〜３００と、超高分子量ポリ
オレフィン自身の重量平均分子量／数平均分子通（通常
６程度）よりも大きく設定している。この結果、分子量
分布は低分子量側へと広がりをみせるため、高濃度のポ
リオレフィン溶液の調製が可能となる。
上述したような本発明のポリオレフィン組成物は、重量
平均分子量が７　Ｘ　１０’以上の超高分″：Ｆ量ポリ
オレフィンと、重量平均分子量が７ＸＩＯ’未満のポリ
オレフィンとを重量平均分子量／数平均分子量が上記範
囲となるように適量混合することによって得ることがで
きる。
本発明において、超高分子量ポリオレフィンは、重量平
均分子量が７×１０５以上、好ましくはｌＸ１０６〜１
５Ｘ　１０’のものである。重量平均分子量が７　Ｘ　
１０’未満では、最大延伸倍率が低く、目的の微多孔膜
が得られない。一方、上限は特に限定的ではないが１５
Ｘ　１０’を超えるものは、ゲル状成形物の形成におい
て、成形性に劣る。
このような超高分子量ポリオレフィンとしては、エチレ
ン、プロピレン、ｌ−ブテン、４−メチル−ｌ−ペンテ
ン、１−ヘキセンなどを重合した結晶性の単独重合体ま
たは共重合体が挙げられる。これらのうち超高分子量ポ
リエチレン、特に高密度の超高分子量ポリエチレンが好
ましい。
また上記超高分子１ポリオレフインのポリオレフィン組
成物中の含有量は、ポリオレフィン組成物全体を１００
重量％として、１重量％以上である。
超高分子量ポリオレフィンの含有量が１重量％未満では
、延伸性の向上に寄与する超高分子量ポリオレフィンの
分子鎖の絡み合いがほとんど形成されず、高強度の微多
孔膜を得ることができない。
一方、上限は特に限定的ではないが、９０重量％を超え
ると目的とするポリオレフィン溶液の高濃度化の達成が
困難となるため好ましくない。
またポリオレフィン組成物中の超高分子量ポリオレフィ
ン以外のポリオレフィンは、重量平均分子量が、７　Ｘ
　１０’未満のものであるが、分子量の下限としてはｌ
Ｘｌ０’以上のものが好ましい。重量平均分子量がｌＸ
ｌ０’未満のポリオレフィンを用いると、延伸時に破断
が起こりやすく、目的の微多孔膜が得られないので好ま
しくない。特に重量平均分子量がｌＸｌ０’以上７×１
０５未満のポリオレフィンを超高分子量ポリオレフィン
に配合するのが好ましい。
このようなポリオレフィンとしては、前述の超高分子量
ポリオレフィンと同種のものが挙げられるが、特にエチ
レンを主体とする重合体である高密度ポリエチレンが好
ましい。
なお、上述したようなポリオレフィン組成物には、必要
に応じて、酸化防止剤、紫外線吸収剤、滑剤、アンチブ
ロッキング剤、顔料、染料、無機充填剤などの各種添加
剤を本発明の目的を損ｆｚねない範囲で添加することが
できる。
次に、本発明のポリオレフィン微多孔膜の製造方法につ
いて説明する。
本発明において、原料となるポリオレフィン組状物の高
濃度溶液は、上述のポリオレフィン組成物を溶媒に加熱
溶解することにより調製する。
この溶媒としては、ポリオレフィン組状物を十分に溶解
できるものであれば特に限定されない。
例えば、ノナン、デカン、ウンデカン、ドデカン、パラ
フィン油などの脂肪族または環式の炭化水素、あるいは
沸点がこれらに対応する鉱油留分などが挙げられるが、
溶媒含有量が安定なゲル状成形物を得るためにはパラフ
ィン油のような不揮発性の溶媒が好ましい。
加熱溶解は、ポリオレフィン組成物が溶媒中で完全に溶
解する温度で攪拌しながら行う。その温度は使用する重
合体及び溶媒により異なるが、例えばポリエチレン組成
物の場合には１４０〜２５０℃の範囲である。また、ポ
リオレフィン組成物溶液の濃度は、１０〜５０重量％、
好ましくは１０〜４０重量％である。濃度が１０重量％
未満では、使用する溶媒量が多く経済的でないばかりか
、シート状に底形する際に、ダイス出口で、スウェルや
ネックインが大きくシートの底形が困難となる。一方、
濃度が５０重覆髄を超えると、均一な溶液の調製が困難
となる。なお、加熱溶解にあたってはポリオレフィンの
酸化を防止するために酸化防止剤を添加するのが好まし
い。
次にこのポリオレフィン組成物の加熱溶液をダイスから
押し出して底形する。ダイスは、通常長方形の口金形状
をしたシートダイスが用いられるが、２重円筒状の中空
系ダイス、インフレーションダイス等も用いることがで
きる。シートダイスを用いた場合のダイスギャップは通
常０．１〜５Ｉｌｏｎであり、押出し成形時には１４０
〜２５０℃に加熱される。この際押し出し速度は、通常
２０〜３０ｃｍ／分乃至２〜３ｍ／分である。
このようにしてダイスから押し出された溶液は、冷却す
ることによりゲル状物に底形される。冷却は少なくとも
ゲル化温度以下までは５０℃／分以上の速度で行うのが
好ましい。冷却速度が遅いと結晶化度が上昇し、延伸に
適したゲル状物となりにくい。冷却方法としては、冷風
、冷却水、その他の冷却媒体に直接接触させる方法、冷
媒で冷却したロールに接触させる方法等を用いることが
できる。なおダイスから押し出された溶液は、冷却前あ
るいは冷却中に、１−１０好ましくは１〜５の引取比で
引き取っても良い。引取比が１０以上になるとネックイ
ンが大きくなり、また延伸時に破断を起こしやすくなり
好ましくない。
次にこのゲル状成形物を、延伸する。延伸は、ゲル状成
形物を加熱し、通常のテンター法、ロール法、インフレ
ーション法、圧延法もしくはこれらの方法の組合せによ
って所定の倍率で行う。２軸延伸が好ましく、縦横同時
延伸または逐次延伸のいずれでもよいが、特に同時２軸
延伸が好ましい。
延伸温度は、ポリオレフィン組状物の融点＋１０℃以下
、好ましくは結晶分散温度から結晶融点未満の範囲であ
る。例えば、ポリエチレンの場合は９０〜１４０℃で、
より好ましくは、１００〜１３０℃の範囲である。延伸
温度が融点＋１０℃を超える場合は、樹脂の溶融により
延伸による分子鎖の配向ができない。また、延伸温度が
結晶分散温度未満では、樹脂の軟化が不十分で、延伸に
おいて破膜し易く、高倍率の延伸ができない。
また、延伸倍率は原反の厚さによって異なるが、ｌ軸方
向で少なくとも２倍以上、好ましくは３〜２０倍、面倍
率で１０倍以上、好ましくは２０〜４００倍である。面
倍率が１０倍未満では延伸が不十分で高弾性、高強度の
微多孔膜が得られない。一方、面倍率が４００倍を超え
ると、延伸装置、延伸操作などの点で制約が生じる。
得られた延伸形成物は、溶剤で洗浄し残留する溶媒を除
去する。洗浄溶剤としては、ペンタン、ヘキサン、ヘプ
タンなどの炭化水素、塩化メチレン、四塩化炭素などの
塩素化炭化水素、三フッ化エタンなどのフッ化炭化水素
、ジエチルエーテル、ジオキサンなどのエーテル類など
の易揮発性のものを用いることができる。これらの溶剤
はポリオレフィン組状物の溶解に用いた溶媒に応じて適
宜選択し、単独もしくは混合して用いる。洗浄方法は、
溶剤に浸漬し抽出する方法、溶剤をシャワーする方法、
またはこれらの組合せによる方法などにより行うことが
できる。
上述のような洗浄は、延伸成形物中の残留溶媒が１重量
％未滴になるまで行う。その後洗浄溶剤を乾燥するが、
洗浄溶剤の乾燥方法は加熱乾燥、風乾などの方法で行う
ことができる。乾燥した延伸成形物は、結晶分散温度〜
融点の温度範囲で熱固定することが望ましい。
以上のようにして製造したポリオレフィン微多孔膜は、
空孔率が３５〜９５％で、平均貫通孔径が０゜００１〜
０．２　ｍで、かつ１５ｍｍ幅の破断強度が０．２ｋｇ
以上である。また本発明のポリオニ／フィン微多孔膜の
厚さは、用途に応じて適宜選択しうるが、般に０．ｌ〜
２５−であり、好ましくは２〜２０−にすることができ
る。
なお、得られたポリオレフィン微多孔膜は、必要に応じ
てさらに、プラズマ照射、界面活性剤含浸、表面クラフ
ト等で親水化処理することができる。
〔実施例〕
以下に本発明の実施例を示す。なお、実施例における試
験方法はつぎの通りである。
（１〕重遣平均分子量及び分子量分布：ウォーターズ＠
製のＧＰＣ装置を用い、カラムに東ソー＠Ｊ製ＧｔＡ１
トロ、溶媒にＤ−ジクロルベンゼンを使用し、温度１３
５℃、流量１．０Ｉｎ！！／分にて、ゲルパーミェーシ
ョンクロマトグラフィー（ＧＰＣ）法により測定。
（２）フィルムの厚さ：断面を走査型電子顕微鏡により
測定。
（３）引張破断強度：幅１５ｍｍの短冊状試験片の破断
強度をＡＳＴＭ　０８８２に準拠して測定。
（４）透気度：　ＪＩＳ　Ｐ８１１７に準拠。
（５）透水度：微多孔膜を平膜モジュールに組み込み、
蒸留水／エタノール混合液（５０１５０容積比〉で親水
化処理を行い、蒸留水で十分に洗浄した後、３８０　ｍ
ｍＨｌＨの水圧をかけたときの濾液の透過量を測定して
求めた。
（６）孔径；上記（５）で記載したモジュールを用いて
、３８０　ｍｍＨｇの差圧下で０．０５重量％のプルラ
ン（昭和電工■製）の水溶液を循環させたときに、濾液
中に含まれるプルランの濃度を示差屈折単側７定から求
めた。そして、次式により計算した阻止率が５０％にな
るプルランの分子量の値から、後述するようなＦ）ｏｒ
ｙの理論を利用して、孔径を換算した。
プルランの阻止率＝（１−（濾液中のプルラン濃度／原
液中のプルラ ン濃度））Ｘ１００ 溶液状態にある鎮状高分子は球状の糸まり状で、その直
径ｄは、分子鎖の両末端の２乗平均距離〈Ｔ２〉に対し
て、近似的に Ｃｄ／２　　Ｅ　　”　　＝　　＜　　γ　２　〉　　
・　　・　・　（１）の関係にあると考えて良い。
高分子溶液における粘性と分子鎖の広がりに関するＦｌ
ｏｒｙの理論によると、高分子の種類に無関係に ［η　］　　Ｍ＝２．Ｉ　　ＸＩＯ”　　（γ　２　　
）　　３／２　　　　　・　・　（２）が成立するので
、式（Ｌ）及び（２）により、固有粘度〔η〕の測定値
と、阻止率が５０％になる分子ｆｆ１Ｍとから鎖状高分
子の直径ｄを算出することができる。このｄをポリエチ
レン微多孔膜の孔径とした。
実施例１ 重量平均分子量（７；（ｗ＞が２゜５×１０５の超高分
子量ポリエチレン２重量部と、６．８×１０５のポリエ
チレン８重量部とを混合したＭｗ／ｉｎ　＝１６．８の
原料樹脂と、流動パラフィン　（６４ｃｓｔ／４０℃）
９０重量部とを混合し、ポリエチレン組成物の溶液を調
製した。次にこのポリエチレン組成物の溶液１００重量
部に、２．６−シーｔ〜ブチル−ｐ−クレゾール（ｒＢ
ｌ＋ＴＪ、住友化学工業＠製）０．１２５重量部とテト
ラキス〔メチレン−３−（３，５−ジー（−ブチル−４
−ヒドロキシルフェニル）−プロピオネートコメタン（
「イルガノックスｌ０ＩＯＪ　、チバガイギー製）０，
２５重量部とを酸化防止剤として加えて混合した。
この混合液を攪拌機付のオートクレーブに充填して均一
な溶液を得た。
この溶液を直径４５ｍｍの押出機により、Ｔダイから押
出し、冷却ロールで引取りながらゲル状シートを底形し
た。
得られたシートを二軸延伸機にセットして、温度１１５
℃、延伸速度０．５ｍ／分でＴＸ７倍に同時二軸延伸を
行った。得られた延伸膜を塩化メチレンで洗浄して残留
する流動パラフィンを抽出除去した後、乾燥して厚さ４
即のポリエチレン微多孔膜を得た。その特性を第１表に
示す。
実施例２ 重量平均分子ｆｆｉ（Ｍｗ）が２．５×１０５の超高分
子量ポリエチレン２重量部と、２．４ｘ１０’のポリエ
チレン１３重量部とを混合した７Ｊｗ／Ｕｎ　＝１６．
７の原料樹脂と、流動パラフィン８５重量部とをポリエ
チレン組成物の溶液とした以外は、実施例１と同一条件
で、厚さ５即のポリエチレン微多孔膜を得た。その特性
を第１表に示す。
実施例３ 重量平均分子！（？；Ｖｗ）が２．５×１０５の超高分
子量ポリエチレン２重量部と、４．ｌＸｌ０’のポリエ
チレン１３重１部とを混合したＦ７ｗ／Ｆ７ｗ＝１９０
の原料樹脂と、流動パラフィン８５重量部とをポリエチ
レン組成物の溶液とした以外は、実施例１と同一条件で
、厚さ４−のポリエチレン微多孔膜を（尋た。その特性
を第１表に示す。
実施例４ 重量平均分子！（ｉｗ）が２．５Ｘ１０６の超高分子量
ポリエチレン１重量部と、４．ｌＸ１０５のポリエチレ
ン１９重量部とを混合したＭｗ／Ｍｎ＝１５０の原料樹
脂と、流動パラフィン８０重量部とをポリエチレン組成
物の溶液とした以外は、実施例１と同一条件で、厚さ１
６ｍのポリエチレン微多孔膜を得た。その特性を第１表
に示す。
実施例５ 重量平均分子１（７７ｗ）が２．５×１０５の超高分子
量ポリエチレン１重量部と、３．５×１０５のポリエチ
レン３９重量部とを混合したＨｗ／Ｍｎ＝２４０の原料
樹脂と、流動パラフィン６０重Ｎ部とをポリエチレン組
成物の溶液とした以外は、実施例１と同一条件で、厚さ
１２即のポリエチレン微多孔膜を得た。その特性を第１
表に示す。
比較例１ 重量平均分子ｉｔ（Ｍｗ）が６．８×１０５のポリエチ
レン（Ｍｗ／１ｎ＝８．ＯＮ２重量部と、流動パラフィ
ン８８重量部とをポリエチレン溶液とした以外は、実施
例１と同一条件で製膜したが、高倍率で延伸できず、ポ
リエチレン微多孔膜は得られなかった。
比較例２ 重量平均分子１（Ｔｌ　ｗ　）が２．５×１０５の超高
分子量ポリエチレン２重量部と、５．９×１０５のポリ
エチレン１３重＠部とを混合したＨｗ／Ｈｎ＝３５０の
原料樹脂と、流動パラフィン８５重量部とをポリエチレ
ン組成物の溶液とした以外は、実施例１と同一条件で製
膜したが、破断強度の低いポリエチレン微多孔膜しか得
られなかった。
比較例３ 重量平均分子１（Ｍｗ）が２．５×１０５の超高分子遣
ポリエチレ：’　（Ｆ７ｗ／ｉｎ　＝６．０）１２重還
部を、流動パラフィン８８重＠部に実施例１と同一条件
で溶解しようとしたが、均一な溶液を調製することがで
きなかった。
比較例４ 重、１平均分子壜（”ｍ　ｗ　）が２．５×１０５の超
高分子量ポリエチレン０．２重量部と、３．５×１０５
のポリエチレン２４．８重量部とを混合したＴＸ　ｗ　
／　ＴＸ　ｎ　＝１２０の原料樹脂と、流動パラフィン
７５重量部とをポリエチレン組成物の溶液とした以外は
、実施例１と同一条件でＴＸ膜したが、延伸時の破断が
多く、ポリエチレン微多孔膜は得られなかった。
比較例５ 重量平均分子１１（Ｍｗ）が２，５×１０５の超高分子
量ポリエチレン２重量部と、２．４×１０５のポリエチ
レン５８重量部とを混合したＷｆ　ｗ　／　Ｍ　ｎ　＝
　１４．５の原料樹脂を、流動パラフィン４０重量部に
実施例１と同一条件で溶解しようとしたが、均一な溶液
を調製することができなかった。
〔発明の効果〕
以上詳述したように、本発明の方法によれば、原料とな
るポリオレフィン組成物の溶液の濃度を１０〜５０重量
％と高濃度に調製できるので、使用する溶剤の量が少な
くてすみ、また延伸の前にゲル状シート中の溶媒量を調
整する必要もない。このため、効率良くポリオレフィン
微多孔膜を得ることができる。しかもシート成形の際に
押出されたゲル状底形物には、スウェルやネックインの
発生が少ないという利点もある。
また、本発明の微多孔膜は高強度であり、不織布等と積
層する際の取扱い性や加工性に優れている。さらに透水
性に優れるため、分子量数百〜数十万の分子状物を効率
良く分画することができる。
かかるポリオレフィン微多孔膜は、電池用セパレーター
、電解コンデンサー用隔膜、超精密濾過膜、限外濾過膜
、各種フィルター、透湿防水衣料用多孔質膜等の各種用
途に好適である。

Claims (1)

  1. 【特許請求の範囲】 （１）重量平均分子量が７×１０＾５以上の超高分子量
    ポリオレフィンを１重量％以上含有し、重量平均分子量
    ／数平均分子量が１０〜３００のポリオレフィン組成物
    からなり、厚さが０．１〜２５μｍで、空孔率が３５〜
    ９５％で、平均貫通孔径が０．００１〜０．２μｍであ
    り、１５ｍｍ幅の破断強度が０．２ｋｇ以上であること
    を特徴とするポリオレフィン微多孔膜。 （２）請求項１に記載のポリオレフィン微多孔膜におい
    て、前記超高分子量ポリオレフィンが超高分子量ポリエ
    チレンであり、前記ポリオレフィン組成物中の他の成分
    が、エチレンを主体とする重量平均分子量１×１０＾４
    以上７×１０＾５未満の重合体であることを特徴とする
    ポリオレフィン微多孔膜。 （３）重量平均分子量が７×１０＾５以上の超高分子量
    ポリオレフィンを１重量％以上含有し、重量平均分子量
    ／数平均分子量が１０〜３００のポリオレフィン組成物
    １０〜５０重量％と、溶媒５０〜９０重量％とからなる
    溶液を調製し、前記溶液をダイより押出し、冷却してゲ
    ル状組成物を形成し、前記ゲル状組成物を前記ポリオレ
    フィン組成物の融点＋１０℃以下の温度で延伸し、しか
    る後残存溶媒を除去することを特徴とするポリオレフィ
    ン微多孔膜の製造方法。 （４）請求項３に記載のポリオレフィン微多孔膜の製造
    方法において、前記溶液の冷却を５０℃／分以上の冷却
    速度で行うことを特徴とする方法。 （５）請求項３又は４に記載のポリオレフィン微多孔膜
    の製造方法において、前記ゲル状組成物の延伸温度が結
    晶分散温度乃至結晶融点の範囲であることを特徴とする
    方法。 （６）請求項３乃至５のいずれかに記載のポリオレフィ
    ン微多孔膜の製造方法において、前記超高分子量ポリオ
    レフィン溶液の溶媒が不揮発性溶媒であることを特徴と
    する方法。（７）請求項３乃至６のいずれかに記載のポ
    リオレフィン微多孔膜の製造方法において、前記不揮発
    性溶媒がパラフィン油であることを特徴とする方法。 （８）請求項３乃至７のいずれかに記載のポリオレフィ
    ン微多孔膜の製造方法において、前記残存溶媒の除去を
    易揮発性溶剤による抽出により行うことを特徴とする方
    法。 （９）請求項３乃至８のいずれかに記載のポリオレフィ
    ン微多孔膜の製造方法において、前記超高分子量ポリオ
    レフィンが超高分子量ポリエチレンであり、前記ポリオ
    レフィン組成物中の他の成分が、エチレンを主体とする
    重量平均分子量１×１０＾４以上７×１０＾５未満の重
    合体であることを特徴とする方法。
JP1201785A 1989-08-03 1989-08-03 ポリオレフィン微多孔膜 Expired - Lifetime JPH06104736B2 (ja)