JPH0580502B2 - - Google Patents

Info

Publication number
JPH0580502B2
JPH0580502B2 JP60287909A JP28790985A JPH0580502B2 JP H0580502 B2 JPH0580502 B2 JP H0580502B2 JP 60287909 A JP60287909 A JP 60287909A JP 28790985 A JP28790985 A JP 28790985A JP H0580502 B2 JPH0580502 B2 JP H0580502B2
Authority
JP
Japan
Prior art keywords
fine powder
porous film
inorganic fine
stretching
polyolefin resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP60287909A
Other languages
English (en)
Other versions
JPS62148537A (ja
Inventor
Juichi Tsuji
Michasu Ito
Hideji Matsumura
Hisatoshi Suzuki
Shoichi Ito
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Toatsu Chemicals Inc
Original Assignee
Mitsui Toatsu Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Toatsu Chemicals Inc filed Critical Mitsui Toatsu Chemicals Inc
Priority to JP60287909A priority Critical patent/JPS62148537A/ja
Priority to CA000525608A priority patent/CA1305300C/en
Priority to NZ218669A priority patent/NZ218669A/xx
Priority to DE8686117615T priority patent/DE3680493D1/de
Priority to EP86117615A priority patent/EP0227037B1/en
Priority to NO865156A priority patent/NO169080C/no
Priority to AU66825/86A priority patent/AU595565B2/en
Priority to CN86108657A priority patent/CN1014064B/zh
Priority to KR1019860011146A priority patent/KR900003046B1/ko
Publication of JPS62148537A publication Critical patent/JPS62148537A/ja
Priority to US07/229,797 priority patent/US4921652A/en
Publication of JPH0580502B2 publication Critical patent/JPH0580502B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
〈産業上の利用分野〉 本発明は、柔軟性を有し、しかも均一微細孔を
有する構造のため、透湿性があり、耐水性にもす
ぐれた多孔性フイルムに関するものである。本フ
イルムは防水衣料、防水カバー、包装材料その他
に好適に使用できる。 〈従来の技術〉 従来より、ポリオレフイン樹脂に非相溶性物質
いわゆる無機質微粉体を特定の割合で混合した
後、溶融成形して得られたフイルムまたはシート
を一軸ないし二軸に延伸を行い、多孔性フイルム
を製造する方法は知られている。 延伸加工により樹脂が伸びて配向するため、シ
ートの硬度が増大し、柔軟性が損われるという欠
点があつた。この問題点を改善する多孔性フイル
ムの製造方法としては、(1)特開昭59−30833号に
開示されたとおり熱可塑性エラストマーを配合す
る方法、(2)特開昭58−15538号に開示されたとお
り液状またはワツクス状の炭化水素重合体を配合
する方法、また(3)特開昭60−129240号に開示され
たとおり無機質微粉体を硫酸バリウムに限定する
方法が提案されている。 しかしながらこれらの製造法による多孔性フイ
ルムは次の如き実用上の欠点を有している。すな
わち(1)の方法では多孔化が十分でなく透湿性に問
題がある。(2)の方法では多孔性フイルムは高温雰
囲気下あるいは長時間経過後、表面に炭化水素重
合体がブリードして表面がベタツクという問題が
ある。(3)の方法では得られた多孔性フイルムは柔
軟性があり、透湿性も十分であるが延伸安定性す
なわち高延伸性に劣る点があつた。また共通の問
題として20μ程度の極薄膜が出来ない。また第３
成分を配合する方法は大幅なコストアツプとな
る。 〈発明が解決しようとする問題点〉 本発明の目的は、耐薬品性に優れたポリオレフ
イン樹脂からなり、実用上充分な機械的強度と柔
軟性を備え、均一微細孔で、かつ高い透湿性を有
する多孔性フイルム、更に極薄膜の多孔性フイル
ムを提供することにある。 〈問題点を解決するための手段〉 本発明に従つて、比表面積が15m2／ｇ以下でか
つ平均粒子径が0.4〜4μｍの沈降炭酸カルシウム
及び沈降硫酸バリウムからなる群から選ばれた無
機質微粉体30〜80重量％及びポリオレフイン樹脂
20〜70重量％を混合した後、溶融成形し、少なく
とも一軸方向に2.0〜7.0倍延伸することを特徴と
する多孔性フイルムの製造法が提供される。 本発明におけるポリオレフイン系樹脂としては
例えば、ポリプロピレン、低密度ポリエチレン、
線状低密度ポリエチレン、高密度ポリエチレンな
どが挙げられ、単独あるは２種以上の混合物とし
ても用いられる。なかでも線状低密度ポリエチレ
ンおよび線状低密度ポリエチレンを含む混合物が
特に好ましい。線状低密度ポリエチレンのコモノ
マー成分としては例えばブテン、４−メチルペン
テン、ヘキセン、オクテン、デセン等が一般的で
ありなかでも、成形性および製品の物性の点で４
−メチルペンテン、オクテンが好ましい。 本発明で用いる無機質微粉体は比表面積が15
m2／ｇ以下かつ平均粒子径が0.4〜4μｍの沈降炭
酸カルシウム及び沈降硫酸バリウムからなる群か
ら選ばれた微小粒子である。これらは粒径及び比
表面積が均一であり、分散性及び加工性に富んだ
ものである。また、それらの形状は球状であるこ
とが好ましい。 無機質微粉体の比表面積としては15m2／ｇ以下
であり、0.5〜５m2／ｇの範囲がより好ましい。
比表面積が15m2／ｇを越えると、無機質微粉体の
形状が無定形、板状、針状などとなるので粒径分
布が広くなり、延伸性が低下し、フイルムの多孔
化が達成できない。また微粉体の表面の細孔度が
増し、細孔に付着している水分等の揮発成分のた
めに溶融成形時発泡が見られ、フイルムの孔径が
大きくなり耐水圧が著しく低下する。 無機質微粉体の平均粒子径としては0.4〜4μｍ
が好ましく、更に0.6〜2μｍがより好ましい。平
均粒子径4μｍを越えると延伸性が悪く、均一に
白化する前に延伸切れをおこす。作業安定性に劣
り、均一多孔化が出来ない。 一方、平均粒子径が0.4μｍ未満だと、無機質微
粉体が高充填出来ず多孔化が不可能となる。 無機質微粉体の混合量が、ポリオレフイン樹脂
に対し、30重量％に満たないと、延伸したフイル
ムに気孔が充分形成されず、多孔度が低くなる。
又80％を越えると混練性、分散性及び延伸性が劣
り、当然透湿性も悪く、柔軟性が低下する。 次に本発明の多孔性フイルムの製造方法を説明
する。無機質微粉体とポリオレフイン樹脂を所定
の割合で混合する。混合方法は特に限定されな
い。一般にブレンダーなどによる混合の後、バン
バリーミキサーその他の溶融混練機によりあらか
じめ混合した後、ペレツト化するか又はしないで
常法のシート成形装置によりシート化を行なう。
ステアリン酸カルシウム等の滑剤、顔料、熱、光
その他に対する安定剤、可塑剤、帯電防止剤など
の各種添加剤も任意に添加し得る。 一般にはカレンダリング、キヤステイング或い
は押出しによりフイルムとするが、サーキユラー
ダイ又はＴ−ダイを用いる押出しが好ましい。押
出されたシートは次いでポリオレフイン樹脂の軟
化温度以下で公知の延伸方法により2.0〜7.0の倍
率で一軸、或いは二軸に延伸すればよい。なかで
も延伸倍率が４倍から６倍までがより好ましい。
延伸倍率が2.0倍未満では充分な透湿度が得られ
ず、７倍を越える場合は延伸切れが生じ、安定し
て製造することが出来ない。 〈実施例〉 以下実施例により本発明をさらに詳細に説明す
る。各実施例中における物性測定は下記方法によ
り行つたものである。 比表面積（m2／ｇ）；BET吸着法により測定す
る。 平均粒子径（μｍ）；島津式粉体比表面積測定器
にて試料３ｇを２cm2×１cmの試料筒に充填し
500mm水柱で50c.c.の空気透過の時間より測定
する。 引張破断強度（Kg）；25mm（巾）×100mm（長さ）
のフイルム片を引張りスピード200mm／分で
テンシロン引張り試験機にて測定する。破断
強度をMD（流れ方向）、TD（流れに垂直な方
向）について各々測定する。 透湿度；ASTM−Ｅ−96−66に準じる。 柔軟性；手で触れた感じで下記の通り評価した。 Ａ；非常に柔らかい Ｂ；やや柔らかい Ｃ；バサバサしている 実施例 １〜８ MI＝２の線状低密度ポリエチレン（Ｌ−
LDPE；実施例１〜６）、MI＝５の低密度ポリエ
チレン（LDPE；実施例７）あるいはMI＝1.5の
ポリプロピレン（PP；実施例８）に表１に示す
比表面積及び平均粒子径を有する無機質微粉体
（沈降硫酸バリウム；実施例１〜４，７，８、沈
降炭酸カルシウム；実施例５，６を表１に示す量
で添加し、ヘンシエルミキサーで混合し、ペレツ
ト化した後、シート成形機によつて押出し成膜し
た。次いで一軸方向に50℃で２〜７倍ロール延伸
して厚み20μの多孔性フイルムを得た。得られた
フイルムについて、物性を測定した。その結果を
表１に示す。 実施例 ９ 実施例２と同一組成物を用いて成膜したフイル
ムを２軸延伸機により70℃で縦及び横方向に同時
に（３×３）倍延伸し厚み20μの多孔性フイルム
を得た。物性評価結果を表１に示す。 実施例 10 MI＝２の線状低密度ポリエチレン（Ｌ−
LDPE）を20wt％，MI＝５の低密度ポリエチレ
ン（LDPE）を20wt％、比表面積が4.1m2／ｇで
あり平均粒子径が0.8μｍである沈降硫酸バリウム
を60wt％を混合し、実施例１と同様な方法で多
孔性フイルムを得た。物性評価結果を表１に示
す。 比較例 １〜６ 表１に示すようにＬ−LDPEに無機質微粉体
（沈降硫酸バリウム；比較例１〜３，５〜６、炭
酸カルシウム；比較例４）の種類、充填量および
延伸条件を変化させ実施例１と同様な方法で多孔
性フイルムを試作した。これらの物性評価結果を
表１に示す。比較例１では無機質微粉体の添加量
が30％未満であるので多孔度が低下し透湿度が小
さい。比較例２では無機質微粉体の添加量が80％
をこえるので延伸性が低下して延伸倍率が1.5倍
で延伸切れを生じる。比較例３，４では無機質微
粉体の比表面積が15m2／ｇをこえているため延伸
性が低下し、またシート成形機によつて押出し時
発泡が見られ、開繊した。比較例５では無機質微
粉体の平均粒子径が4μｍをこえるため延伸性が
低下し延伸倍率２倍で安定して生産ができない。
比較例６では延伸倍率が２倍未満であるので充分
な透湿度が得られない。 〈発明の効果〉 本発明のフイルムは充分な開孔性を有している
ため、透湿性、通気性が良好であり、かつ耐水性
にもすぐれている。特に柔軟性が良好で感触がソ
フト感を与えるため衣料用、特にサニタリー用途
に好適である。従来の方法と比較して、厚さが
20μｍ以下の極薄膜フイルムも製造出来るため、
多孔性フイルムは単品で使用する用途がほとんど
なく、不織布、パルプ、ナイロンタフタ等と積層
する用途が主である。フイルムが薄くなるほど、
コストの低減さらに、積層体の厚さからくる着用
時の装着感が気にならない特徴が出てくる。
【表】
【表】

Claims (1)

  1. 【特許請求の範囲】 １ 比表面積が15m2／ｇ以下かつ平均粒子径が
    0.4〜4μｍの沈降炭酸カルシウム及び沈降硫酸バ
    リウムからなる群から選ばれた無機質微粉体30〜
    80重量％及びポリオレフイン樹脂20〜70重量％を
    混合した後、溶融成形し、少なくとも一軸方向に
    2.0〜7.0倍延伸することを特徴とする多孔性フイ
    ルムの製造法。 ２ 上記ポリオレフイン樹脂が線状低密度ポリエ
    チレン樹脂である特許請求の範囲第１項記載の多
    孔性フイルムの製造法。
JP60287909A 1985-12-23 1985-12-23 多孔性フイルムの製造法 Granted JPS62148537A (ja)