JPH0619858B2 - 光学的情報記憶媒体の製造方法 - Google Patents

光学的情報記憶媒体の製造方法

Info

Publication number
JPH0619858B2
JPH0619858B2 JP58089169A JP8916983A JPH0619858B2 JP H0619858 B2 JPH0619858 B2 JP H0619858B2 JP 58089169 A JP58089169 A JP 58089169A JP 8916983 A JP8916983 A JP 8916983A JP H0619858 B2 JPH0619858 B2 JP H0619858B2
Authority
JP
Japan
Prior art keywords
storage medium
optical information
information storage
plastic substrate
halogenated hydrocarbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP58089169A
Other languages
English (en)
Other versions
JPS59217241A (ja
Inventor
通治 安倍
秀章 大庭
勉 佐藤
正彬 梅原
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ricoh Co Ltd
Original Assignee
Ricoh Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ricoh Co Ltd filed Critical Ricoh Co Ltd
Priority to JP58089169A priority Critical patent/JPH0619858B2/ja
Publication of JPS59217241A publication Critical patent/JPS59217241A/ja
Publication of JPH0619858B2 publication Critical patent/JPH0619858B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 技術分野 本発明は基板として透明プラスチック基板を用いるとと
もに記録層材料として特定の色素化合物を用いた光学的
情報記録媒体の製造方法に関する。
従来技術 従来、回転しているディスク状の光学的情報記憶媒体に
レーザ光を照射して情報の記録再生を行う情報記録再生
装置が知られている。この種の情報記録再生装置に用い
られる光学的情報記憶媒体としては基板、金属反射膜お
よび色素を含む半透明着色層から構成されているものが
知られている。この光学的情報記憶媒体は色素を含む半
透明着色層に入射するレーザ光が金属反射膜に達して反
射されるようにして反射光を検出し易いようにしたもの
であって、この際前記金属反射膜は着色層のみでは不足
する反射光量を補なうために設けられている。しかしな
がら、金属反射膜の存在は光学的情報記録媒体の構成を
複雑にすると共に高コスト化の原因となっている。そこ
で、本発明者等は反射率の高いブロンズ光沢のある有機
色素単層膜を使用して上記欠点を除去することを先に提
案した。特に、記録膜として光吸収の大きいシアニン系
色素を用いると、膜厚３００Å〜６００Åで金属光沢
（反射率２０〜３０％）を示す光吸収反射膜が得られ、
レーザ記録可能で、反射読出が可能になる。この際、特
にレーザ光源として波長７５０〜８５０nmの半導体レー
ザを用いると装置の小型化が可能になるという利点が得
られる。
ところが、プラスチック基板上にシアニン系色素薄膜を
スピンニングなどのコーティング法によって形成させる
際にシアニン系色素に対する溶媒としてプラスチックに
溶解性の高いジクロルエタンなどのハロゲン化炭化水素
がしばしば用いられることから塗布時にプラスチック基
板までも溶解してしまうという問題があった。塗布時に
プラスチック基板を少しでも溶解すると色素膜の反射率
が大きくならず、ひいては上述したシアニン系色素薄膜
の利点が損なわれることになる。だからといって、透明
基板としてガラスを使用すれば溶媒に対する溶解性の問
題は解消されるが比重が大きいため記憶媒体全体の重量
が増加し取扱いに不便であり、また基板の破損の危険性
が大きくなるという問題がある。
目 的 本発明は上記問題に鑑みてなされたものであって、その
主な目的は反射率が高く(20〜30%)しかも光吸収率の大
きい反射型に適した光学的情報記憶媒体を提供すること
である。
構 成 上記目的を達成するために、本発明によれば、透明プラ
スチック基板にハロゲン化炭化水素溶媒に対する不溶化
処理をした後、該基板上に、シアニン系色素をハロゲン
化炭化水素溶媒に溶解させた溶液を塗布することにより
シアニン系色素薄膜を形成することからなる光学的情報
記録媒体の製造方法が提供される。
本発明は、シアニン系色素は一般にジクロルエタン、ジ
クロルメタンなどのハロゲン化炭化水素によく溶け、こ
の溶媒を用いてガラス基板に塗布すると塗布膜の均一性
が良くなり反射率２０％〜３０％の光反射吸収膜が得ら
れるが、ハロゲン化炭化水素を溶媒としてシアニン系色
素をプラスチック基板に塗布すると、通常のアクリル
板、ポリカーポネート板を溶解するため、色素と基板樹
脂が混合しシアニン系色素の特徴である高い反射率の膜
が得られないという知見にもとづいている。それ故、本
発明は透明プラスチック基板をハロゲン化炭化水素溶媒
に対して不溶化させた後、シアニン系色素塗布膜を形成
するものであるが、この不溶化は例えば (a) ハロゲン化炭化水素に不溶な樹脂もしくはガラス質
の膜をプラスチック基板上に設けること、 (b) 無機透明膜をプラスチック基板上に設けること、 (c) 放射線もしくは電子線照射によりプラスチック基板
表面を架橋させ、溶剤不溶化処理を行なうことおよび (d) ハロゲン化炭化水素に不溶な透明プラスチック基板
を用いること などのいずれかの方法によって達成される。したがっ
て、本明細書において用いられる「透明プラスチック基
板にハロゲン化炭化水素溶媒に対して不溶化処理を施
す」なる語は広い意味を有し、プラスチック基板の直接
不溶化処理したもののみならずプラスチック基板上にハ
ロゲン化炭化水素不溶性膜などを設けることも含むこと
を理解するべきである。
本発明において使用される透明プラスチック基板として
は、アクリル、ポリカーポネート、ポリスチレン、ポリ
エステル、ポリ塩化ビニルなどの板が用いられるが、特
に好ましいのはアクリル板、ポリカーポネート板であ
る。
また、本発明において使用されるシアニン系色素は通常
ハロゲン化銀の分光増感色素として知られているもので
ある。かかる色素には一般に、例えば下記文献に記載さ
れてるシアニン色素が包含される。米国特許第１８４６
３０１号および同第１８４６３０２号、同第１９４２８
５４号、同第１９９０５５０７号、同第２１１２１４０
号、同第２１６５３３８号、同第２４９３７４７号、同
第２７３９９６４号、同第２４９３７４８号、同第２５
０３７７６号、同第２５１９００１号、同第２６６６７
６１号、同第２７３４９００号、同第２７３９１４９号
および英国特許第４５０９５８号ならびに米国特許第３
６９０８９１号明細書。
本発明では、シアニン系色素薄膜を、ハロゲン化炭化水
素溶媒に対する不溶化処理を施した透明基板上に、シア
ニン系色素をハロゲン化炭化水素溶媒に溶解した溶液を
コーティングすることにより形成する。ハロゲン化炭化
水素としては例えばメチレンクロライド、トリクロルエ
チレン、パークロルエチレン、ジクロロメタン、ジクロ
ロエタンなどを使用できるが、ジクロロメタンおよびジ
クロロエタンが特に好ましい。塗布はスプレー、ローラ
ーコーティング、ディッピングおよびスピンニングなど
の慣用のコーティング法によって行なわれる。
次に、本発明の方法によって得られた光学的情報記憶媒
体の構成例および情報の記録再生法を図面について説明
すると、図示の記憶媒体はプラスチック基板１にハロゲ
ン化炭化水素に不溶な下引層２を設けこの上にシアニン
系色素薄膜３を形成させたものである。この情報記憶媒
体に集光するレーザビーム４を照射して情報を記録し、
また反射光を検出することにより情報を再生することが
できる。図示した構成のものは本発明の方法により製造
された記憶媒体の一例であってプラスチック基板として
はプラスチック基板をハロゲン化炭化水素に対して直接
不溶化処理したものを使用できることはいうまでもな
い。また、上述した構成に加え下引層に案内溝を形成し
たり、シアニン系色素薄膜を保護するための保護層を設
けたりあるいはいわゆるエアーサンドイッチ構造にする
こともできる。
実施例 以下に比較例とともに実施例をあげて本発明をさらに説
明するが、これに限定されるものではない。実施例およ
び比較例においてはシアニン系色素として以下の構造式 で表わされる日本感光色素研究所の製品(NK2014)を用い
そしてシアニン色素の溶媒としてジクロロエタンを用い
てその結果を検討した。
この例の情報記憶媒体は上記シアニン色素をジクロロエ
タンに溶解した塗布溶液（１重量％）を回転塗布機によ
って不溶化処理板上に約３００Åの厚さで塗布し乾燥す
ることによって作製した。情報記憶媒体についての特性
は日本分光(株)製UVIDEC-610型可視紫外分光光度計によ
って測定した。
効 果 本発明によれば、軽量で安価な透明プラスチック基板を
用いてもシアニン系色素の溶液塗布により反射率が高く
(20〜30%)、しかも光吸収率の大きい、反射型に適した
光学的情報記録媒体を得ることができる。
【図面の簡単な説明】
図は本発明の方法により製造された光学的情報記憶媒体
の構成例を示す模式図である。 １……プラスチック基板、２……ハロゲン化炭化水素に
不溶な下引層、３……シアニン系色素薄膜、４……レー
ザビーム。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 梅原 正彬 東京都大田区中馬込１丁目３番６号 株式 会社リコ−内 (56)参考文献 特開 昭55−122242（ＪＰ，Ａ)

Claims (1)

    【特許請求の範囲】
  1. 【請求項１】透明プラスチック基板にハロゲン化炭化水
    素溶媒に対する不溶化処理をした後、該基板上に、シア
    ニン系色素をハロゲン化炭化水素溶媒に溶解させた溶液
    を塗布することによりシアニン系色素薄膜を形成するこ
    とからなる光学的情報記憶媒体の製造方法。
JP58089169A 1983-05-23 1983-05-23 光学的情報記憶媒体の製造方法 Expired - Lifetime JPH0619858B2 (ja)