JPS60125631A - 医療容器 - Google Patents

医療容器

Info

Publication number
JPS60125631A
JPS60125631A JP58233510A JP23351083A JPS60125631A JP S60125631 A JPS60125631 A JP S60125631A JP 58233510 A JP58233510 A JP 58233510A JP 23351083 A JP23351083 A JP 23351083A JP S60125631 A JPS60125631 A JP S60125631A
Authority
JP
Japan
Prior art keywords
propylene
random copolymer
transparency
blow molding
stretch blow
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP58233510A
Other languages
English (en)
Other versions
JPH0419925B2 (ja
Inventor
Toru Ueki
徹 植木
Hideo Amamiya
英夫 雨宮
Toyoaki Hata
畑　豊明
Takashi Miyazaki
宮崎　孝志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Toatsu Chemicals Inc
Original Assignee
Mitsui Toatsu Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Toatsu Chemicals Inc filed Critical Mitsui Toatsu Chemicals Inc
Priority to JP58233510A priority Critical patent/JPS60125631A/ja
Priority to EP84115106A priority patent/EP0151741A3/en
Priority to EP87110734A priority patent/EP0251340B1/en
Priority to DE3486446T priority patent/DE3486446T2/de
Priority to AU36543/84A priority patent/AU554076B2/en
Priority to CA000469959A priority patent/CA1240446A/en
Publication of JPS60125631A publication Critical patent/JPS60125631A/ja
Publication of JPH0419925B2 publication Critical patent/JPH0419925B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は透明性、耐熱性に優れたポリプロピレン系補刷
製の医療容器に関する。更に詳しくはリンゲル液、ハル
トマン液等の輸液用に適した容器に関する。
輸液用プラスチック容器の規格については日本薬局法に
定められているが、中でも透明性については、内容液中
の異物を観察するのにできるだけ高いことが要求されて
いる。ポリプロピレン系樹脂は機械的性質、滅菌時の耐
熱性、安全衛生性に優れた樹脂としてこの輸液用容器と
して使用されているが、透明性の点で不十分であり、押
出成形式２軸延伸ブロー成形等により透明性の改良が行
なわれているが、未だ不十分である。
本発明者らはポリプロピレン系樹脂製の輸液容器の透明
性を改良すべく鋭意検討した結果、特定のポリプロピレ
ン系樹脂を使用して、射出延伸ブロー成形を行なうこと
により、透明性の漬れた容器が得られることを見出し、
本発明に到達した。
即ち、本発明は、メルトフローインデックスが４〜２０
１ｉ’７１０分であるプロピレン−エチレンランダム共
重合体を、造核剤を添加することなく、射出延坤ブロー
成形法により成形されたことを特徴とする医療容器であ
る。
本発明において用いるプロピレン−エチレンランダム共
重合体とは日本工業規格ＪＩＳＫ−７２１０の条件１４
に従って測定したメルトフローインデックス（以下、Ｍ
ＦＩと略す）が４〜２０ｆ７１０分のものである。ＭＦ
Ｉが４１７１．０分以下では得られる容器の透明性は不
十分であり’１　、２０　ｆ／１０分を越えると容器の
偏肉が著しくなる。
又、本発明においてはプロピレン−エチレンランダム共
重合体としてはエチレンが少ないものが望ましく、特に
エチレン含量が０５〜８重量％好丑しくは１〜６重量係
置部るものが透明性、耐熱性の上から好適に用いうる。
更に造核剤を用いれば、透明性は向上するのであるが、
本用途においては使用する必要はない程に良好な透明性
が得られる。
本発明において用いる射出延伸ブロー成形法とは、有底
パリソンを射出成形によって成形し、ついで予備ブロー
、延伸温度調整後、延伸ブローすることによって製品を
得る成形法であり、延伸の方法としてはロンドによる機
械的なたて延伸と空気吹込みによる方法の組合せが普通
に行なわれる。
これに用いる成形機としては日精ＡＳＢ機械株式会社製
射出延伸ブロー成形機Ａ’５Ｂ−５０、ＡＳＢ−１５０
。
ＡＳＢ−２５０、ＡＳＢ−６５０等をあげることができ
る。
本発明の高透明で偏肉の少ないプロピレン−エチレンラ
ンダム共重合体製の医療容器を成形する条件としては、
例えば射出延伸ブロー成形機ＡＳＢ−５０を用いた場合
、下記条件が望ましい。
射出成形温度：２００〜２６０℃ 予備ブロー　：たて延伸倍率１０〜１８倍横延伸倍率　
１２〜２０倍 ブロー圧力　３〜６に９／ｃｍ 延伸温度調整金型温度＝９０〜１４０℃延伸ブロー　二
たて延伸倍率１２〜６５倍横延伸倍率　１２〜６０倍 ブロー圧力　４〜２０　Ｋｇ　／　ｃｒ１本発明の医療
容器は上記ブロピレンーエチレンランダム共重合体（て
、必要に応じ、安定剤等の添加物を極く少量、添加し、
上記射出延伸ブロー成形法により通常胴部の肉厚が０２
〜ｔｏｍｍになる様に成形されたものである。
本発明の医療容器は透明性、耐熱性に優れているので高
温滅菌が可能であり、輸液用容器として好適に用いうる
。
以下、実施例により本発明を説明する。
実施例１ ＭＦＩが１５１ｉ’／１０分で、エチレン含有量が４重
置部であるプロピレン−エチレンランダム共重合体を日
清ＡＳＢ機械（掬製、射出延伸ブロー成形機ＡＳＢ−５
０にて下記条件で射出延伸ブロー成形を行ない、胴部直
径７０闘、容量５００　Ｃｃの丸型ボトルを成形した。
射出延伸ブロー成形条件 射出成形温度：２２０℃ 射出成形金型温度＝１５℃ 予備ブロー：たで１倍、横１４倍 予備ブローエアー圧力ニ５Ｋｙ／ｃＪ 延伸温度調節金型温度：１００℃ 延伸プロｍ：たて１８倍、横１２倍 延伸ブロー圧力＝９にり／ｃｎｇ 得られたボトルは重量２４７で肉厚の均一性が良く、透
明性の優れた容器であシ、特に内容液を入れた時の透視
性は良好で、輸液容器等の医療容器として好適なもので
あった。胴部の肉厚は０．５０７ｎ７ｎで、切取った試
験片の霞度を日本重色製のヘーズメーターを用い、ＪＩ
Ｓ　Ｋ−６７１４記載の方法によって測定したところ７
８チであった。
実施例−２ 実施例１において、プロピレン−エチレンランダム共重
合体としてＭＦＩが６ｆ／１０分でエチレン含有量が２
重量裂のプロピレン−エチレンランダム共重合体を用い
た他は、実施例−１と同様にして、射出延伸ブロー成形
を行ない、容量５００ｃｃの丸型ボトルを成形した。得
られたボトルは重量２４ｆで、肉厚の均一性が良く、透
明性の優れた容器であり、特に内容液を入れた時の透視
性は良好で、輸液容器等の医療容器として好適なもので
あった。胴部の肉厚は０．５０　ｍｍで、霞度は９２ヂ
であった。
比較例１ 実施例１において、プロピレン−エチレンランダム共重
合体としてＭＦＩが２ｉｉ’７１０分で、エチレン含有
量が２重置部であるプロピレン−エチレンランダム共重
合体を用いた他は、実施例１と同様にして、射出延伸ブ
ロー成形を行ない容量５００ｃｃの丸型ボトルを得た。
得られたボトルの透明性は不十分で、胴部の肉厚０．４
９　ｍｍであり、霞度は１９８チであった。
比較例２ １１Ｔｉ例１において、プロピレン−エチレンランダム
共重合体としてＭＦＩが２５１７１０分で、エチレン含
有量が２０％であるプロピレン−エチレンランダム共重
合体を用いた他は、実施例１と同様にして、射出延伸ブ
ロー成形を行彦っだが、得られたボトルはたて方向、横
方向いずれの方向でも偏肉が大きく、使用できないもの
であった。
特許出願人 三井東圧化学株式会社

Claims (1)

    【特許請求の範囲】
  1. メルトフローインデックスが４〜２ｏｆ／１゜分である
    プロピレン−エチレンランダム共重合体を、造核剤を添
    加することなく、射出延伸ブロー成形法により成形され
    たことを特徴とする医療容器
JP58233510A 1983-12-13 1983-12-13 医療容器 Granted JPS60125631A (ja)