JPH0423620B2 - - Google Patents

Info

Publication number
JPH0423620B2
JPH0423620B2 JP59005521A JP552184A JPH0423620B2 JP H0423620 B2 JPH0423620 B2 JP H0423620B2 JP 59005521 A JP59005521 A JP 59005521A JP 552184 A JP552184 A JP 552184A JP H0423620 B2 JPH0423620 B2 JP H0423620B2
Authority
JP
Japan
Prior art keywords
temperature
blow
mold
polypropylene resin
molded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP59005521A
Other languages
English (en)
Other versions
JPS60149427A (ja
Inventor
Tooru Ueki
Hideo Amamya
Toyoaki Hata
Takashi Myazaki
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Toatsu Chemicals Inc
Original Assignee
Mitsui Toatsu Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Toatsu Chemicals Inc filed Critical Mitsui Toatsu Chemicals Inc
Priority to JP59005521A priority Critical patent/JPS60149427A/ja
Priority to EP87110734A priority patent/EP0251340B1/en
Priority to DE3486446T priority patent/DE3486446T2/de
Priority to EP84115106A priority patent/EP0151741A3/en
Priority to CA000469959A priority patent/CA1240446A/en
Priority to AU36543/84A priority patent/AU554076B2/en
Publication of JPS60149427A publication Critical patent/JPS60149427A/ja
Publication of JPH0423620B2 publication Critical patent/JPH0423620B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】 本発明は透明性の優れたポリプロピレン樹脂製
射出延伸ブロー成形容器の製造方法に関するもの
である。 ポリプロピレン樹脂は、耐熱性、耐薬品性、安
全衛生面等に優れた樹脂であり、そのブロー成形
品は剛性、衝撃強度にも優れるため、食品容器、
洗剤容器、医療容器等に広く使用されている。し
かしながら、ポリプロピレン樹脂製のブロー成形
品は透明性が不十分であるという欠点があり、市
場からは、ポリ塩化ビニル樹脂製容器と同等の透
明性を有するものが要求されている。 従来、ポリプロピレン樹脂の透明性の改良方法
として、造核剤を添加させる方法、プロピレンに
α−オレフインを共重合させる方法、また加工法
としては２軸延伸する方法が知られているが、通
常のブロー成形法にあつては、これらの対策を行
なつても、良くても薄白く霞みがかかつたものし
か得られていない。 一方、最近射出延伸ブロー成形法において、ポ
リプロピレン樹脂にも応用できる成形機が開発さ
れ、ブロー成形品も試作されているが、透明性に
優れ、偏肉のないポリプロピレン樹脂製のブロー
成形品は得られていないのが実情である。 本発明者らは、透明性に優れ、かつ偏肉の無い
ポリプロピレン樹脂製ブロー成形容器を製造する
方法を検討した結果、射出延伸ブロー成形法によ
つても、パリソンを特定の温度範囲内の温度に調
整した予備ブロー金型兼延伸温度調整金型内で予
備ブローし、延伸温度調整してから延伸ブローす
ることによつて、透明性に優れ、偏肉のないポリ
プロピレン樹脂製延伸ブロー成形容器が得られる
ことを見出し、本発明を完成するに到つた。 即ち、本発明は、ポリプロピレン樹脂製の射出
延伸ブロー成形容器の製造において、射出成形し
た有底パリソンをポリプロピレン樹脂の結晶化温
度Tc（℃）に対して（Tc−30℃）〜（Tc＋20℃）
の温度に調整した予備ブロー金型兼延伸温度調整
金型内で予備ブローし、延伸温度調整後、延伸ブ
ロー成形することを特徴とする透明性の優れたポ
リプロピレン樹脂製射出延伸ブロー成形容器の製
造方法である。 本発明でいう射出延伸ブロー成形法とは、まず
有底パリソンを射出成形によつて成形し、次いで
これを加熱した予備ブロー金型兼延伸温度調整金
型内で予備ブローしてややふくらませ、金型内面
にパリソンを接触させ延伸温度調整したのち、延
伸ブロー金型内に移し、そこでブロー成形容器を
成形する方法である。 この成形法において、予備ブロー金型兼延伸温
度調整金型の温度を原料ポリプロピレン樹脂の結
晶化温度Tc（℃）より30℃低い温度から20℃高い
温度範囲、（Tc−30℃）〜（Tc＋20℃）の温度
範囲に調整することによつて、はじめて、透明性
が優れ、偏肉の少ないポリプロピレン樹脂製射出
延伸ブロー成形容器が得られるのである。好まし
くは、（Tc−20℃）〜（Tc＋10℃）である。 予備ブロー金型兼延伸温度調整金型の温度が
（Tc−30℃）未満では成形品の偏肉が著しく、場
合によつては延伸ブロー時にパリソンがブローエ
ア圧力により破裂し、良好な容器は得られない。
また、（Tc＋20℃）を越えると、成形品は目視で
も明らかな程に薄白く霞がかかつた状態となり、
また、破断強度も低下する。 予備ブロー金型兼延伸温度調整金型の温度調整
方法は、電気ヒーターによる方法、温度調節した
オイルを循環させる方法などいずれであつてもか
まわないが、予備ブロー終了時または終了後この
金型から予備ブローされたパリソンを取出す直前
において、この金型の温度が上記した範囲以内の
温度になつていればよい。 また、ブロー成形品の形状等によつては、ブロ
ー成形品の肉厚分布を更に改良するために、予備
ブロー金型兼延伸温度調整金型の温度調整を幾つ
かに区分して、それぞれ（Tc−30℃）から（Tc
＋20℃）以内の異なつた温度に調整しておいても
かまわない。 更に、パリソンの温度分布を均一にするため
に、予備ブローのときに、パリソンを予備ブロー
金型兼延伸温度調整金型に密着させることが望ま
しい。 延伸ブローを好適に行なうためには、下記の予
備ブロー条件が好ましい。 予備ブロー延伸倍率：縦 1.0〜1.8倍 横 1.2〜2.0倍 予備ブロー金型兼延伸温度調整金型温度：（Tc−
30℃）〜（Tc＋20℃） 予備ブローエア圧力：３〜７Kg／cm2 また、引き続き行なう延伸ブローは、以下の条
件が好ましい。 延伸ブロー延伸倍率：縦 1.2〜3.5倍 横 1.2〜6.0倍 延伸ブローエア圧力：４〜20Kg／cm2 本発明に適した成形機としては、日精ASB機
械(株)製の射出延伸ブロー成形機ASB−50、ASB
−150、ASB−250、ASB−650などがあげられ
る。 本発明に用いるポリプロピレン樹脂としては、
プロピレンとα−オレフイン、特にエチレンとの
ランダム共重合体が望ましく、少量の他の樹脂や
エラストマーをブレンドしたものであつても良
い。また、必要により造核剤を添加したものであ
つても良い。 本発明においては、通常、ポリプロピレン樹脂
に安定剤、帯電防止剤、紫外線吸収剤、着色剤、
造核剤等の添加剤を添加したのち、これをペレツ
ト化して得た樹脂を用い、上記の条件下で射出延
伸ブロー成形することにより、胴部肉厚が0.2〜
1.0mmの透明性に優れ、偏肉のないポリプロピレ
ン樹脂製射出延伸ブロー成形容器が製造される。 本発明によつて得られるポリプロピレン樹脂製
射出延伸ブロー成形容器は透明性に優れるばかり
でなく、耐熱性、耐衝撃性、表面光沢にも優れる
ので、その性質を利用して、食品容器、洗剤容
器、シヤンプー容器、トイレタリー容器、医療容
器等に好適に使用できる。 以下実施例により、本発明を詳細に説明する。 なお、本発明でいう結晶化温度Tcとは、示差
走査熱量計を用い、樹脂を一度完全に溶解したの
ち、冷却速度10℃／minで冷却固化させて得た結
晶化曲線のピーク温度である。 実施例 １ ポリプロピレン樹脂として、エチレン含有量４
重量％、メルトフローインデツクス（MFI）15
ｇ／10分であり、かつ造核剤を0.2重量％含むエ
チレン−プロピレンランダム共重合体を用いた。 この樹脂の結晶化温度Tcは118℃であつた。 この樹脂を射出延伸ブロー成形機ASB−50を
用い、予備ブロー金型兼延伸温度調整金型を110
℃にし、下記条件で成形して胴部直径70mm、内容
量500mlの丸型ボルトを得た。 射出成形温度：220℃ 射出成形金型温度：15℃ 予備ブロー延伸倍率：縦１倍、横1.4倍 予備ブローエア圧力：５Kg／cm2 延伸ブロー延伸倍率：縦1.8倍、横1.2倍 延伸ブローエア圧力：９Kg／cm2 得られたボトルは、その重量が20ｇ、胴部肉厚
が約0.53mmであり、透明性に優れ、偏肉のないボ
トルであつた。 得られたボトルの胴部より試験片を切出して測
定した霞度は3.1％、また破断強度は縦延伸方向
が740Kg／cm2、横延伸方向が710Kg／cm2であつた。 測定結果を表１にまとめて示す。 実施例２、３ 比較例１、２ ポリプロピレン樹脂として、表１に示すエチレ
ン含有量、MFI、および造核剤含有量のものを
用い、更に、予備ブロー金型兼延伸温度調整金型
の温度を表１に示す温度に変える以外は実施例１
と同様にして、丸型ボトルを成形した。 樹脂のTcおよび得られたボトルの性能の測定
結果を表１に示す。 尚、比較例１では得られたボトルは目視でも明
らかな程に薄白く霞みがかかつたボトルであつ
た。また、比較例２では、偏肉が著しく良好なボ
トルは得られなかつた。 【表】

Claims (1)

    【特許請求の範囲】
  1. １ ポリプロピレン樹脂製射出延伸ブロー成形容
    器の製造において、射出成形した有底パリソンを
    ポリプロピレン樹脂の結晶化温度Tc（℃）に対し
    て（Tc−30℃）〜（Tc＋20℃）の温度に調整し
    た予備ブロー金型兼延伸温度調整金型内で予備ブ
    ローし、延伸温度調整後延伸ブロー成形すること
    を特徴とする透明性の優れたポリプロピレン樹脂
    製射出延伸ブロー成形容器の製造方法。
JP59005521A 1983-12-13 1984-01-18 ブロ−成形容器の製造方法 Granted JPS60149427A (ja)