JPH0419925B2 - - Google Patents

Info

Publication number
JPH0419925B2
JPH0419925B2 JP23351083A JP23351083A JPH0419925B2 JP H0419925 B2 JPH0419925 B2 JP H0419925B2 JP 23351083 A JP23351083 A JP 23351083A JP 23351083 A JP23351083 A JP 23351083A JP H0419925 B2 JPH0419925 B2 JP H0419925B2
Authority
JP
Japan
Prior art keywords
propylene
transparency
random copolymer
container
blow molding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP23351083A
Other languages
English (en)
Other versions
JPS60125631A (ja
Inventor
Tooru Ueki
Hideo Amamya
Toyoaki Hata
Takashi Myazaki
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Toatsu Chemicals Inc
Original Assignee
Mitsui Toatsu Chemicals Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Toatsu Chemicals Inc filed Critical Mitsui Toatsu Chemicals Inc
Priority to JP58233510A priority Critical patent/JPS60125631A/ja
Priority to EP87110734A priority patent/EP0251340B1/en
Priority to DE3486446T priority patent/DE3486446T2/de
Priority to EP84115106A priority patent/EP0151741A3/en
Priority to CA000469959A priority patent/CA1240446A/en
Priority to AU36543/84A priority patent/AU554076B2/en
Publication of JPS60125631A publication Critical patent/JPS60125631A/ja
Publication of JPH0419925B2 publication Critical patent/JPH0419925B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】 本発明は透明性、耐熱性に優れたポリプロピレ
ン系樹脂製の医療容器に関する。更に詳しくはリ
ンゲル液、ハルトマン液等の輸液用に適した容器
に関する。
輸液用プラスチツク容器の規格については日本
薬局法に定められているが、中でも透明性につい
ては、内容液中の異物を観察するのにできるだけ
高いことが要求されている。ポリプロピレン系樹
脂は機械的性質、滅菌時の耐熱性、安全衛生性に
優れた樹脂としてこの輸液用容器として使用され
ているが、透明性の点で不十分であり、押出成形
式２軸延伸ブロー成形等により透明性の改良が行
なわれているが、未だ不十分である。
本発明者らはポリプロピレン系樹脂製の輸液容
器の透明性を改良すべく鋭意検討した結果、特定
のポリプロピレン系樹脂を使用して、射出延伸ブ
ロー成形を行なうことにより、透明性の優れた容
器が得られることを見出し、本発明に到達した。
即ち、本発明は、メルトフローインデツクスが
４〜20g／10分であるプロピレン−エチレンラン
ダム共重合体を、造核剤を添加することなく、射
出延伸ブロー成形法により成形されたことを特徴
とする医療容器である。
本発明において用いるプロピレン−エチレンラ
ンダム共重合体とは日本工業規格JISK−7210の
条件14に従つて測定したメルトフローインデツク
ス（以下、MFIと略す）が４〜20g／10分のもの
である。MFIが4g／10分以下では得られる容器
の透明性は不十分であり、20g／10分を越えると
容器の偏肉が著しくなる。
又、本発明においてはプロピレン−エチレンラ
ンダム共重合体としてはエチレンが少ないものが
望ましく、特にエチレン含量が0.5〜８重量％好
ましくは１〜６重量％であるものが透明性、耐熱
性の上から好適に用いうる。
更に造核剤を用いれば、透明性は向上するので
あるが、本用途においては使用する必要はない程
に良好な透明性が得られる。
本発明において用いる射出延伸ブロー成形法と
は、有底パリソンを射出成形によつて成形し、つ
いで予備ブロー、延伸温度調整後、延伸ブローす
ることによつて製品を得る成形法であり、延伸の
方法としてはロツドによる機械的なたて延伸と空
気吹込みによる方法の組合せが普通に行なわれ
る。
これに用いる成形機としては日精ASB機械株
式会社製射出延伸ブロー成形機ASB−50，ASB
−150，ASB−250，ASB−650等をあげることが
できる。
本発明の高透明で偏肉の少ないプロピレン−エ
チレンランダム共重合体製の医療容器を成形する
条件としては、例えば射出延伸ブロー成形機
ASB−50を用いた場合、下記条件が望ましい。
射出成形温度：200〜260℃ 予備ブロー：たて延伸倍率 1.0〜1.8倍 横延伸倍率 1.2〜2.0倍 ブロー圧力 ３〜６Kg／cm 延伸温度調整金型温度：90〜140℃ 延伸ブロー：たて延伸倍率 1.2〜3.5倍 横延伸倍率 1.2〜6.0倍 ブロー圧力 ４〜20Kg／cm2 本発明の医療容器は上記プロピレン−エチレン
ランダム共重合体に、必要に応じ、安定剤等の添
加物を極く少量、添加し、上記射出延伸ブロー成
形法により通常胴部の肉厚が0.2〜1.0mmになる様
に成形されたものである。
本発明の医療容器は透明性、耐熱性に優れてい
るので高温滅菌が可能であり、輸液用容器として
好適に用いうる。
以下、実施例により本発明を説明する。
実施例 １ MFIが15g／10分で、エチレン含有量が４重量
％であるプロピレン−エチレンランダム共重合体
を日精ASB機械(株)製、射出延伸ブロー成形機
ASB−50にて下記条件で射出延伸ブロー成形を
行ない、胴部直径70mm、容量500c.c.の丸型ボトル
を成形した。
射出延伸ブロー成形条件 射出成形温度：220℃ 射出成形金型温度：15℃ 予備ブロー：たて１倍、横1.4倍 予備ブローエアー圧力：５Kg／cm2 延伸温度調節金型温度：100℃ 延伸ブロー：たて1.8倍、横1.2倍 延伸ブロー圧力：９Kg／cm2 得られたボトルは重量24gで肉厚の均一性が良
く、透明性の優れた容器であり、特に内容液を入
れた時の透視性は良好で、輸液容器等の医療容器
として好適なものであつた。胴部の肉厚は0.50mm
で、切取つた試験片の霞度を日本電色製のヘーズ
メーターを用い、JISK−6714記載の方法によつ
て測定したところ7.8％であつた。
実施例 ２ 実施例１において、プロピレン−エチレンラン
ダム共重合体としてMFIが6g／10分でエチレン
含有量が２重量％のプロピレン−エチレンランダ
ム共重合体を用いた他は、実施例−１と同様にし
て、射出延伸ブロー成形を行ない、容量500c.c.の
丸型ボトルを成形した。得られたボトルは重量
24gで、肉厚の均一性が良く、透明性の優れた容
器であり、特に内容液を入れた時の透視性は良好
で、輸液容器等の医療容器として好適なものであ
つた。胴部の肉厚は0.50mmで、霞度は9.2％であ
つた。
比較例 １ 実施例１において、プロピレン−エチレンラン
ダム共重合体としてMFIが2g／10分で、エチレ
ン含有量が２重量％であるプロピレン−エチレン
ランダム共重合体を用いた他は、実施例１と同様
にして、射出延伸ブロー成形を行ない容量500c.c.
の丸型ボトルを得た。
得られたボトルの透明性は不十分で、胴部の肉
厚0.49mmであり、霞度は19.8％であつた。
比較例 ２ 実施例１において、プロピレン−エチレンラン
ダム共重合体としてMFIが25g／10分で、エチレ
ン含有量が2.0％であるプロピレン−エチレンラ
ンダム共重合体を用いた他は、実施例１と同様に
して、射出延伸ブロー成形を行なつたが、得られ
たボトルはたて方向、横方向いずれの方向でも偏
肉が大きく、使用できないものであつた。

Claims (1)

    【特許請求の範囲】
  1. １ メルトフローインデツクスが４〜20g／10分
    であるプロピレン−エチレンランダム共重合体
    を、造核剤を添加することなく、射出延伸ブロー
    成形法により成形されたことを特徴とする医療容
    器。
JP58233510A 1983-12-13 1983-12-13 医療容器 Granted JPS60125631A (ja)