JPS614113A - 含ふつ素エラストマ被覆電線・ケ−ブル - Google Patents
含ふつ素エラストマ被覆電線・ケ−ブルInfo
- Publication number
- JPS614113A JPS614113A JP59124760A JP12476084A JPS614113A JP S614113 A JPS614113 A JP S614113A JP 59124760 A JP59124760 A JP 59124760A JP 12476084 A JP12476084 A JP 12476084A JP S614113 A JPS614113 A JP S614113A
- Authority
- JP
- Japan
- Prior art keywords
- fluorine
- cable
- containing elastomer
- tetrafluoroethylene
- coated wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は、含ふっ素エラストマ被覆電線・ケーブル、特
に耐熱変形性に優れた電線・ケーブルに関するものであ
る。
に耐熱変形性に優れた電線・ケーブルに関するものであ
る。
［従来の技術］
テトラフルオ［１エチレン−プロピレン系共重合体は、
高度の熱安定性、絶縁性、耐薬品性、難燃性を有する架
橋可能な含ふっ素エラストマ共重合体として知られてお
り、かかる共重合体を導体又は電線コア外周に被覆する
ことにより、上記の特長を有する電線・ケーブルを得る
ことが可能である。
高度の熱安定性、絶縁性、耐薬品性、難燃性を有する架
橋可能な含ふっ素エラストマ共重合体として知られてお
り、かかる共重合体を導体又は電線コア外周に被覆する
ことにより、上記の特長を有する電線・ケーブルを得る
ことが可能である。
［発明が解決しようとする問題点］
しかしながら、テトラフルオロエチレン−プロピレン系
共重合体は耐熱変形性に劣るという問題があり、これを
電線・ケーブルに適用する場合、従来はＭＴやＦＴなど
のカーボンブラック、タルク、クレー、けい酸等の白色
系フィラーを混和しているが、カーボンブラックを混和
した場合には電気絶縁性が、白色系フィラーを混和した
場合には熱安定性が損なわれるという問題が新たに認識
されるに到った。
共重合体は耐熱変形性に劣るという問題があり、これを
電線・ケーブルに適用する場合、従来はＭＴやＦＴなど
のカーボンブラック、タルク、クレー、けい酸等の白色
系フィラーを混和しているが、カーボンブラックを混和
した場合には電気絶縁性が、白色系フィラーを混和した
場合には熱安定性が損なわれるという問題が新たに認識
されるに到った。
本発明は上記に基づいてなされたものであり、テトラフ
ルオロエチレン−プロピレン系共重合体の本来の特長で
ある耐熱性を損なうことなく耐熱変形性を向上した被覆
を有する電線・ケーブルの提供を目的とするものである
。
ルオロエチレン−プロピレン系共重合体の本来の特長で
ある耐熱性を損なうことなく耐熱変形性を向上した被覆
を有する電線・ケーブルの提供を目的とするものである
。
［問題点を解決するための手段］
本発明の電線・ケーブルは、テトラフルオロ］。
チレンープロピレン系共重合体１００Ｅｉ１部に対し、
けい酸カルシウムを１０〜１００重り部含有する組成物
の被覆層を設け、該被覆層を架橋して構成したものであ
る。
けい酸カルシウムを１０〜１００重り部含有する組成物
の被覆層を設け、該被覆層を架橋して構成したものであ
る。
本発明において、テトラフルオロＪヂレンープロピレン
系共重合体としては、主成分の°ア１〜ラフルオロエチ
レンとプロピレンに加えて、これらと共重合可能な成分
、例えばエチレン、ブテン−１、イソブチン、フクリル
酸およびそのアルキルエステル、メタクリル酸およびそ
のアルキルニスデル、ふり化ビニル、ぶつ化ビニリデン
、ヘキザフルオロプロペン、クロロエチルビニルエーテ
ル、グリシジルビニルエーテル、クロロトリフルオロエ
チレン、パーフルオロアルキルビニルエーテル等を適当
に含有せしめたものであってもよい。
系共重合体としては、主成分の°ア１〜ラフルオロエチ
レンとプロピレンに加えて、これらと共重合可能な成分
、例えばエチレン、ブテン−１、イソブチン、フクリル
酸およびそのアルキルエステル、メタクリル酸およびそ
のアルキルニスデル、ふり化ビニル、ぶつ化ビニリデン
、ヘキザフルオロプロペン、クロロエチルビニルエーテ
ル、グリシジルビニルエーテル、クロロトリフルオロエ
チレン、パーフルオロアルキルビニルエーテル等を適当
に含有せしめたものであってもよい。
かかる共重合体において、テトラフルオロエチレン／プ
ロピレンの含有モル比としては９５１５〜３０／７０、
特に９０／１０〜４５１５５の範囲から選定することが
耐熱性、成形性等の面から好ましく、また、適宜加えら
れる主成分以外の成°分の含有量としては通常５０モル
％以下、特に３０モル％以下の範囲から選定することが
好ましい。
ロピレンの含有モル比としては９５１５〜３０／７０、
特に９０／１０〜４５１５５の範囲から選定することが
耐熱性、成形性等の面から好ましく、また、適宜加えら
れる主成分以外の成°分の含有量としては通常５０モル
％以下、特に３０モル％以下の範囲から選定することが
好ましい。
本発明において使用されるケイ酸カルシウム番よ、通常
ワラストナイトと呼ばれ、粒径は１μ前後の′ ものが
多い、また、けい酸カルシウムは、分散性や補強性を上
げるため表面を脂肪酸、シランカップリング剤、チタネ
ートカップリング剤等で処理したものでもよい。
ワラストナイトと呼ばれ、粒径は１μ前後の′ ものが
多い、また、けい酸カルシウムは、分散性や補強性を上
げるため表面を脂肪酸、シランカップリング剤、チタネ
ートカップリング剤等で処理したものでもよい。
けい酸カルシウムの含有量は、テトラフルオロエチレン
−プロピレン系共重合体１００重量部に対して１０〜１
００重量部とする必要があり、１０重量部未満では耐熱
変形性を改善する効果が少なく、１００重量部を越える
と組成物の熱安定性が損なわれると共に粘度が高くなっ
て押出が困難になる。
−プロピレン系共重合体１００重量部に対して１０〜１
００重量部とする必要があり、１０重量部未満では耐熱
変形性を改善する効果が少なく、１００重量部を越える
と組成物の熱安定性が損なわれると共に粘度が高くなっ
て押出が困難になる。
上記したテトラフルオロエチレンープ［１ピレン系共重
合体及びけ゛い酸カルシウムを必須成分ど゛リ−る組成
物は導体又は電線コア外周に押出被覆された後に架橋さ
れる。
合体及びけ゛い酸カルシウムを必須成分ど゛リ−る組成
物は導体又は電線コア外周に押出被覆された後に架橋さ
れる。
架橋方法としては、有機過酸化物やアミン類等の添加に
よる化学架橋、あるいはγ線や電子線等の電離性放射線
の照射による照射架橋等が採用され、特に限定されない
。
よる化学架橋、あるいはγ線や電子線等の電離性放射線
の照射による照射架橋等が採用され、特に限定されない
。
有機過酸化物の具体例としては、ジ−ｔ−ブチルバーオ
キサイド、ｔ−ブチルクミルパーＡキサイド、ジクミル
パーオキサイド、２，５−ジメチル−２，５−ジ（ｔ−
ブチルパーオキシ）−へ４−シン−３，１，３−ビス−
（ｔ−ブチルパーオキシ−イソプロビル）ベンゼン等が
あげられる。
キサイド、ｔ−ブチルクミルパーＡキサイド、ジクミル
パーオキサイド、２，５−ジメチル−２，５−ジ（ｔ−
ブチルパーオキシ）−へ４−シン−３，１，３−ビス−
（ｔ−ブチルパーオキシ−イソプロビル）ベンゼン等が
あげられる。
アミン類の具体例としては、ヘキサメヂレンジアミン、
テトラエチレンペンタミン、トリエチレンテトラミン等
のいわゆるアルキルポリアミンあるいはそのカルバミン
酸、シンナミリデン酸等の塩、またはピペラジン、ピペ
リジン、トリジン、アニリン、フェナンスロリン等のア
ロマティックポリアミンおよびその塩等があげられる。
テトラエチレンペンタミン、トリエチレンテトラミン等
のいわゆるアルキルポリアミンあるいはそのカルバミン
酸、シンナミリデン酸等の塩、またはピペラジン、ピペ
リジン、トリジン、アニリン、フェナンスロリン等のア
ロマティックポリアミンおよびその塩等があげられる。
また、アリル化合物、硫黄、有機アミン類、マレイミド
、メタクリレート類、ジビニル化合物等の架橋助剤の採
用も可能であり、好ましくは、フタル酸ジアリル、トリ
アリル燐酸、トリアリルイソシアヌレート、トリアリル
シアヌレート等のアリル化合物が採用可能である。
、メタクリレート類、ジビニル化合物等の架橋助剤の採
用も可能であり、好ましくは、フタル酸ジアリル、トリ
アリル燐酸、トリアリルイソシアヌレート、トリアリル
シアヌレート等のアリル化合物が採用可能である。
本発明においては、上記成分以外にポリぶつ化ビニリデ
ン、■ヂレンテトラフルオロエチレン、ポリテトラフル
オロエチレン等のふっ素樹脂、ぶつ化ビニリデン−へキ
サフルオロプロピレン共重合体に代表されるふっ素ゴム
を適宜混合してもよい。また、その他補強剤、顔料、滑
剤、押出助剤、酸化防止剤、安定剤等の各種添加剤を配
合してもよい。
ン、■ヂレンテトラフルオロエチレン、ポリテトラフル
オロエチレン等のふっ素樹脂、ぶつ化ビニリデン−へキ
サフルオロプロピレン共重合体に代表されるふっ素ゴム
を適宜混合してもよい。また、その他補強剤、顔料、滑
剤、押出助剤、酸化防止剤、安定剤等の各種添加剤を配
合してもよい。
［実施例］
第１表に示すＪ：うに各種成分を所定量配合し、６０℃
に加熱した８インチロールで混練した。次に、これをヘ
ッド：１００℃、シリンダ１：１００℃、シリンダー２
二８０℃に設定した４０ＴｒＬ／′ｒｒＬ押出１１１（
Ｌ／Ｄ＝２２）により、外径１゜６Ｍφのスズメッキ銅
撚線外周に０．５姻の厚さに押出被覆し１３気圧のスチ
ーム（温度：１９５℃）中に３分間保持することにより
電線を作成した。 このようにして作成した電線につい
て、ＪＩＳ規格に基づいて加熱変形率と絶縁抵抗を評価
すると共に、ふっ素樹脂に関する電気用品の熱安定性試
験条件である２５０’ＣＸｄ日で熱劣化後の引張強さと
伸びの変化を測定した。なお、熱劣化は心線を抜いて測
定した。これらの結果を第１表の下欄に示す。
に加熱した８インチロールで混練した。次に、これをヘ
ッド：１００℃、シリンダ１：１００℃、シリンダー２
二８０℃に設定した４０ＴｒＬ／′ｒｒＬ押出１１１（
Ｌ／Ｄ＝２２）により、外径１゜６Ｍφのスズメッキ銅
撚線外周に０．５姻の厚さに押出被覆し１３気圧のスチ
ーム（温度：１９５℃）中に３分間保持することにより
電線を作成した。 このようにして作成した電線につい
て、ＪＩＳ規格に基づいて加熱変形率と絶縁抵抗を評価
すると共に、ふっ素樹脂に関する電気用品の熱安定性試
験条件である２５０’ＣＸｄ日で熱劣化後の引張強さと
伸びの変化を測定した。なお、熱劣化は心線を抜いて測
定した。これらの結果を第１表の下欄に示す。
第１表からも明らかな通り、本発明の範囲にある実施例
１〜５ではいずれも加熱変形も小ざく、熱安定性、絶縁
抵抗も良好であった。
１〜５ではいずれも加熱変形も小ざく、熱安定性、絶縁
抵抗も良好であった。
これに対し、けい酸カルシウムの含有量が少ない比較例
１では加熱変形率が大きく、多すぎる比較例２では熱安
定性に劣る。また、従来使用されているフィラー（比較
例３〜７）では、熱安定性又は絶縁性のいずれか一方が
大きく劣っている。
１では加熱変形率が大きく、多すぎる比較例２では熱安
定性に劣る。また、従来使用されているフィラー（比較
例３〜７）では、熱安定性又は絶縁性のいずれか一方が
大きく劣っている。
［発明の効果］
以上説明してきた通り、本発明はテトラフルオロエチレ
ン−プロピレン系共重合体及びけい酸カルシウムを所定
量含有する組成物の架橋体を被覆層とするものであり、
耐熱性及び耐熱変形性に優れた含ふっ素エラストマ被覆
電線・ケーブルが得られる。
ン−プロピレン系共重合体及びけい酸カルシウムを所定
量含有する組成物の架橋体を被覆層とするものであり、
耐熱性及び耐熱変形性に優れた含ふっ素エラストマ被覆
電線・ケーブルが得られる。
Claims (2)
- （１）テトラフルオロエチレン−プロピレン系共重合体
１００重量部に対し、けい酸カルシウムを１０〜１００
重量部含有する組成物の被覆層を有し、該被覆層は架橋
されていることを特徴とする含フッ素エラストマ被覆電
線・ケーブル。 - （２）テトラフルオロエチレン−プロピレン系共重合体
のテトラフルオロエチレン／プロピレンの含有モル比が
９５／５〜３０／７０である特許請求の範囲第１項記載
の含ふっ素エラストマ被覆電線・ケーブル。