JPH0125134B2 - - Google Patents

Info

Publication number
JPH0125134B2
JPH0125134B2 JP53144285A JP14428578A JPH0125134B2 JP H0125134 B2 JPH0125134 B2 JP H0125134B2 JP 53144285 A JP53144285 A JP 53144285A JP 14428578 A JP14428578 A JP 14428578A JP H0125134 B2 JPH0125134 B2 JP H0125134B2
Authority
JP
Japan
Prior art keywords
vinyl
manufactured
acetate copolymer
vinyl acetate
vinyl chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP53144285A
Other languages
English (en)
Other versions
JPS5570936A (en
Inventor
Hiroshi Oota
Eiji Horigome
Hitoshi Azegami
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TDK Corp
Original Assignee
TDK Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TDK Corp filed Critical TDK Corp
Priority to JP14428578A priority Critical patent/JPS5570936A/ja
Priority to US06/095,647 priority patent/US4340644A/en
Priority to GB7940445A priority patent/GB2037782B/en
Priority to DE2947159A priority patent/DE2947159C2/de
Priority to NL7908554A priority patent/NL7908554A/nl
Publication of JPS5570936A publication Critical patent/JPS5570936A/ja
Publication of JPH0125134B2 publication Critical patent/JPH0125134B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
本発明は磁気記録媒体に関し、特に走行性及び
周波数特性の良好な磁気記録媒体に関する。 一般に、磁気記録媒体はγFe2O3等の磁性粉末
を高分子樹脂バインダー中に分散した磁性塗料を
ポリエステルフイルム等の基体に塗布して成るも
のである。磁性塗膜の性質は走行性等の物理的性
質のみならず、磁性粉末の分散性等から磁気特性
にも大いに関係しており、これは主としてバイン
ダー及び添加剤によつて大きく支配される。また
物理的特性と電磁特性とは密接に関連するもので
ある。従つて、従来磁性塗料のバインダーとして
種々提案されているが未だ充分に満足なものは得
られていない。 また、これまで用いられて来たバインダーとし
ては従来ウレタン系、塩化ビニル―酢酸ビニル
系、セルロース系、エポキシ系、ポリエステル系
の樹脂の２種を組合わせるものが多かつた。本発
明はそのうち、塩化ビニル―酢酸ビニル共重合体
とポリエステル樹脂とを使用する磁気記録媒体の
改良に関する。 塩化ビニル―酢酸ビニル共重合体とポリエステ
ル樹脂をバインダーとして用いた磁気記録媒体
は、高温多湿下（60℃、75％RH）でのカセツト
デツキ走行性において特にすぐれた結果を与える
が周波数特性はあまり好ましくなく、改善が望ま
れていた。 本発明は種々研究の結果、ビニルアルコールを
含有する塩化ビニル―酢酸ビニル共重合を上記の
２成分系のバインダーと共に用いることにより周
波数特性を大幅に改善し得た。ビニルアルコール
【式】はそれを含有する塩化ビニル― 酢酸ビニル共重合体を基にして重量比で少くとも
10％含有されなければ効果が低い。一方この共重
合体はバインダー全量に対して40％以上になると
磁性塗料のゲル化を促進する効果が生じ、50％を
超えるとゲル化が促進されるので好ましくない。
しかし、これ以下の範囲では磁性塗料のゲル化は
ほとんど進まず、磁性塗料の調製において上記共
重合体の含有率の厳密な規制はあまり気にしなく
てよいことが分つた。 本発明によると、高温多湿下における走行性が
良好であると共に、電磁性が良好であるという作
用効果が達成される。 次に本発明の実施例について説明し、これを比
較例と共に検討する。各実施例はバインダーとな
る樹脂組成のみについて示した。これらの組成は
組成Ａと合体して使用された。 なお、以下でVAGHとは米国ユニオン・カー
バイド・コーポレーシヨン（UCC）製のビニル
アルコールが６％の塩化ビニル―酢酸ビニル共重
合体である。 実施例 １ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） 17重量部 ポリエステル樹脂（デスモフエン 2200日本ポ
リウレタン工業社製） 13 〃 塩化ビニル―酢酸ビニル共重合体（OH―DEX
電気化学工業社製）（ビニル―アルコールを12
％含有） ３ 〃 実施例 ２ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） 13重量部 ポリエステル樹脂（ニツポラン 143日本ポリ
ウレタン工業社製） 13 〃 塩化ビニル―酢酸ビニル共重合体（OH―DEX
電気化学工業社製）（ビニル―アルコールを12
％含有） ７ 〃 実施例 ３ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） 10重量部 ポリエステル樹脂（デスモフエン 1800住友バ
イエルウレタン社製） 13 〃 塩化ビニル―酢酸ビニル共重合体（OH―DEX
電気化学工業社製）（ビニル―アルコールを12
％含有） 10 〃 実施例 ４ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） ７重量部 ポリエステル樹脂（デスモフエン 1100住友バ
イエルウレタン社製） 13 〃 塩化ビニル―酢酸ビニル共重合体（OH―DEX
電気化学工業社製）（ビニル―アルコールを12
％含有） 17 〃 比較例 １ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） 20重量部 ポリエステル樹脂（ニツポラン 4032日本ポリ
ウレタン工業社製） 13 〃 比較例 ２ 塩化ビニル―酢酸ビニル共重合体（VAGH
UCC製） 20重量部 ポリエステル樹脂（デスモフエン 1800住友バ
イエルウレタン社製） 13 〃 Ａ組成分 γ―Fe2O3粉末（コバルト・ドープ）
100重量部 潤滑剤 ５ 〃 メチル・エチル・ケトン 100 〃 メチル・イソブチル・ケトン 100 〃 トルエン 100 〃 比較例１、２及び実施例１、２、３、４の各成
分とＡ組成分をボールミル中にて充分混合分散さ
せた後、多官能芳香剤イソシアネート（デスモジ
ユールＬ 住友バイエルウレタン社製）を５重量
部添加後、均一に分散するよう混合撹拌後12μの
ポリエステルベースの支持体に乾燥厚が6μにな
るように塗布し、表面加工後、60℃で48時間熱処
理硬化後切断し、磁気テープ化した。このように
して周波数特性を測定したものが第１図である。
尚、比較例１をテープ化したものが比較例1′のよ
うに各々対応する。なお第１図において「レスポ
ンス」とはIECで測定したIEC―タイプの標準
テープにIECで制定した標準条件で記録再生した
ときの出力を0dBとし、それに対する相対出力
（dB）であらわす。 第２図には、塩化ビニル―酢酸ビニル共重合体
とポリエステル樹脂と塩化ビニル―酢酸ビニル共
重合体（ビニルアルコールを10％以上含有）の組
成比を変えたものとＡ組成分からγ―Fe2O3粉末
を抜いたものを混合後サンプル管にとり、多官能
芳香族イソシアネート（デスモジユールＬ 住友
バイエルウレタン社製）を添加混合後、密栓して
20℃で保存後ゲル化する迄の日数を表わしたもの
である。 第１図から分るように、比較例１、２の組成即
ちビニルアルコールを含有する塩化ビニル―酢酸
ビニルを使用しない従来の塩化ビニル―酢酸ビニ
ル及びポリエステル樹脂より成る２元系のバイン
ダーから製造された磁気記録媒体（比較例1′、
2′）は周波数特性が良好でない。これに対して、
本発明の実施例１〜４の組成即ちビニルアルコー
ルを含有する塩化ビニル―酢酸ビニル共重合体を
使用した３元系のバインダーから製造された磁気
記録媒体（実施例1′〜4′）は0.5〜2dB程度の周波
数特性の改善を示し、しかも周波数の全域に対し
て良好である。実施例１はビニルアルコールの含
有量（バインダー全量に対して）が比較的少な
く、実施例４は比較的多い例であり、これに対応
して周波数特性が改善されている。 第２図のゲル化時間のデータからは、10％以上
のビニルアルコールを含有する塩化ビニル―酢酸
ビニル共重合体の量が40重量％程度までの場合は
ゲル化時間がほとんど低下せず、50重量％から目
立つて低下して来る。従つて上記共重合体の量は
50重量％の含有率がほぼ限界と考えられる。 なお実施例１〜４、比較例１〜２はすべて高温
多湿（60℃、75％RH）条件下にすぐれた走行性
を示した。 以上により、本発明の磁気記録媒体はすぐれた
走行性のほかに、良好な電磁特性を有することが
明らかになつた。
【図面の簡単な説明】
第１図は本発明の実施例及び比較例により製造
された磁気記録媒体の周波数特性を示すグラフ、
及び第２図は本発明で用いるビニルアルコール含
有塩化ビニル―酢酸ビニル共重合体の含有率とゲ
ル化時間の関係を示すグラフである。

Claims (1)

    【特許請求の範囲】
  1. １ 塩化ビニル―酢酸ビニル共重合体とポリエス
    テル樹脂とをバインダーとして磁性粉末を分散し
    て成る磁性塗料を基体に塗布して成る磁気記録媒
    体において、少くとも10％以上のビニルアルコー
    ルを含有する塩化ビニル―酢酸ビニル共重合体を
    バインダー全量に対して10〜50重量％添加したこ
    とを特徴とする磁気記録媒体。
JP14428578A 1978-11-24 1978-11-24 Magnetic recording media Granted JPS5570936A (en)