JPH04285679A - 塗料組成物 - Google Patents
塗料組成物Info
- Publication number
- JPH04285679A JPH04285679A JP7401691A JP7401691A JPH04285679A JP H04285679 A JPH04285679 A JP H04285679A JP 7401691 A JP7401691 A JP 7401691A JP 7401691 A JP7401691 A JP 7401691A JP H04285679 A JPH04285679 A JP H04285679A
- Authority
- JP
- Japan
- Prior art keywords
- diol
- compound composition
- urethane prepolymer
- coating compound
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【０００１】
【産業上の利用分野】本発明はゴム、樹脂製品等の塗装
に適した塗料組成物に関するものである。
に適した塗料組成物に関するものである。
【０００２】
【従来の技術】一般に、ＮＲ、ＳＢＲ、ＢＲ、ＩＩＲ、
ＣＲ、ＮＢＲ、ＩＲ、ＥＰＤＭ、ＥＰＴ等のゴムや、木
綿、レーヨン、ＡＢＳ、ＰＳ等の樹脂、繊維は耐摩耗性
が非常に悪い。これらにナイロン、エポキシ樹脂、アク
リル樹脂、アクリル−エチレン系樹脂等の樹脂系塗料お
よびＢＲ、ＣＲ、ＳＢＲ等のゴム系塗料を塗布し摩耗を
行なった場合 （Ａ）ゴム、合成樹脂製品、繊維との密着性がないため
摩耗中基材と塗料がはがれる不具合が発生する（Ｂ）塗
料自体に耐摩耗性がないため耐摩耗性にとぼしいという
問題がある。
ＣＲ、ＮＢＲ、ＩＲ、ＥＰＤＭ、ＥＰＴ等のゴムや、木
綿、レーヨン、ＡＢＳ、ＰＳ等の樹脂、繊維は耐摩耗性
が非常に悪い。これらにナイロン、エポキシ樹脂、アク
リル樹脂、アクリル−エチレン系樹脂等の樹脂系塗料お
よびＢＲ、ＣＲ、ＳＢＲ等のゴム系塗料を塗布し摩耗を
行なった場合 （Ａ）ゴム、合成樹脂製品、繊維との密着性がないため
摩耗中基材と塗料がはがれる不具合が発生する（Ｂ）塗
料自体に耐摩耗性がないため耐摩耗性にとぼしいという
問題がある。
【０００３】
【発明が解決しようとする課題】本発明の目的は上記問
題点を解消し、被塗布物表面との密着性がよく、耐摩耗
性の優れた塗料組成物を提供するものである。
題点を解消し、被塗布物表面との密着性がよく、耐摩耗
性の優れた塗料組成物を提供するものである。
【０００４】
【課題を解決するための手段】本発明者は、これらの欠
点を改良するための研究をつづけ、その結果、上記欠点
を改良する塗料組成物をみいだした。
点を改良するための研究をつづけ、その結果、上記欠点
を改良する塗料組成物をみいだした。
【０００５】本発明の塗料組成物とはポリエーテルジオ
ール、ポリエステルジオール、ジイソシアナートと低
分子ジオールよりなるウレタンプレポリマー１００重
量部、フッ素樹脂２〜１００重量部、ひまし油ポリオー
ルよりなる塗料組成物である。
ール、ポリエステルジオール、ジイソシアナートと低
分子ジオールよりなるウレタンプレポリマー１００重
量部、フッ素樹脂２〜１００重量部、ひまし油ポリオー
ルよりなる塗料組成物である。
【０００６】
【実施例】以下に本発明を具体化した実施例について説
明する。本発明で用いるポリエーテルジオールとはポリ
エチレンオキシドグリコール、ポリプロピレンオキシド
グリコール、ポリテトラメチレンオキシドグリコール等
である。ポリエステルジオールとはエチレングリコール
、プロピレングリコール、ブチレングリコール、ペンタ
ンジオール、ヘキサンジオール、ヘキシレンジオール、
オクタンジオール、デカンジオール、ネオペンチルグリ
コール等（ジオール類に二重結合、三重結合を含有する
ものも含まれる）の一種又は二種以上の混合物と、アジ
ピン酸、マロン酸、コハク酸、マレイン酸、無水マレイ
ン酸、フマル酸、テレフタル酸、無水フタル酸等の有機
酸の一種又は二種以上の混合物を反応させて得られる末
端にＯＨ基を有するポリエステルジオールである。
明する。本発明で用いるポリエーテルジオールとはポリ
エチレンオキシドグリコール、ポリプロピレンオキシド
グリコール、ポリテトラメチレンオキシドグリコール等
である。ポリエステルジオールとはエチレングリコール
、プロピレングリコール、ブチレングリコール、ペンタ
ンジオール、ヘキサンジオール、ヘキシレンジオール、
オクタンジオール、デカンジオール、ネオペンチルグリ
コール等（ジオール類に二重結合、三重結合を含有する
ものも含まれる）の一種又は二種以上の混合物と、アジ
ピン酸、マロン酸、コハク酸、マレイン酸、無水マレイ
ン酸、フマル酸、テレフタル酸、無水フタル酸等の有機
酸の一種又は二種以上の混合物を反応させて得られる末
端にＯＨ基を有するポリエステルジオールである。
【０００７】ジイソシアネートには、ＭＤＩ、ＴＤＩ、
ＩＰＤＩ、ＸＤＩ、ＮＤＩ等のジイソシアネートが例示
できる。溶剤にはベンゼン、トルエン、キシレン、エチ
ルベンゼン、トリクロルエチレン、塩化エチレン、ジメ
チルホルムアミド、ジメチルスルホキサイド、メチルエ
チルケトン、アセトン、メチルイソプロピルケトン、酢
酸メチル、酢酸エチル、酢酸イソプロピル、酢酸ｎ−ブ
チル、酢酸イソプロピル、アニソール、テトラヒドロフ
ラン等を用いる。
ＩＰＤＩ、ＸＤＩ、ＮＤＩ等のジイソシアネートが例示
できる。溶剤にはベンゼン、トルエン、キシレン、エチ
ルベンゼン、トリクロルエチレン、塩化エチレン、ジメ
チルホルムアミド、ジメチルスルホキサイド、メチルエ
チルケトン、アセトン、メチルイソプロピルケトン、酢
酸メチル、酢酸エチル、酢酸イソプロピル、酢酸ｎ−ブ
チル、酢酸イソプロピル、アニソール、テトラヒドロフ
ラン等を用いる。
【０００８】ａ）塗料組成物の調製
上記ポリエステルジオール、ポリエーテルジオール、ジ
イソシアナートと溶剤を適宜選択して使用し（選択例を
表−１に示す）、乾燥窒素ガス中、８０℃、３時間反応
させ、末端にＮＣＯ基を有するウレタンプレポリマーを
合成し、さらに低分子ジオールと溶剤を加え乾燥窒素ガ
ス中３０分間反応を行ない得られる末端にＯＨ基又はＮ
ＣＯ基を有するウレタンポリマー（固形分）１００重量
部に対して、フッ素樹脂２〜１００重量部、ひまし油ポ
リオール（ひまし油ポリオールの末端ＯＨ基とウレタン
プレポリマーの末端ＮＣＯ基のモル当量比が０．７〜１
．３）、さらに溶剤を加えて塗布に適した、粘度に調整
する。この場合、フッ素樹脂のかわりに二硫化モリブデ
ン、ガラス繊維、カーボン繊維、ポリエチレン、酸化ケ
イ素、炭酸カルシウム、炭酸マグネシウム、クレー、ナ
イロン等を使用してもよい。
イソシアナートと溶剤を適宜選択して使用し（選択例を
表−１に示す）、乾燥窒素ガス中、８０℃、３時間反応
させ、末端にＮＣＯ基を有するウレタンプレポリマーを
合成し、さらに低分子ジオールと溶剤を加え乾燥窒素ガ
ス中３０分間反応を行ない得られる末端にＯＨ基又はＮ
ＣＯ基を有するウレタンポリマー（固形分）１００重量
部に対して、フッ素樹脂２〜１００重量部、ひまし油ポ
リオール（ひまし油ポリオールの末端ＯＨ基とウレタン
プレポリマーの末端ＮＣＯ基のモル当量比が０．７〜１
．３）、さらに溶剤を加えて塗布に適した、粘度に調整
する。この場合、フッ素樹脂のかわりに二硫化モリブデ
ン、ガラス繊維、カーボン繊維、ポリエチレン、酸化ケ
イ素、炭酸カルシウム、炭酸マグネシウム、クレー、ナ
イロン等を使用してもよい。
【０００９】ｂ）基材の調製
ＥＰＤＭ１００重量部に対して、カーボンブラック７０
重量部、鉱物油３５重量部、亜鉛華７重量部、ステアリ
ン酸２重量部、加硫促進剤２重量部、イオウ１．５重量
部のゴム配合物を１６０℃で３０分間加硫した。また、
耐摩耗試験方法は、下記条件で行い摩耗減量で耐摩耗性
を評価した。 試験機：テイパー式ロータリアブレッサー（株式会社東
洋精機製作所製） 試験条件：摩耗輪…Ｈ−２２、荷重…１ｋｇ摩耗回転速
度…６０ｒｐｍ 試料寸法…１００ｍｍ×１００ｍｍ 摩耗回転…１０００回
重量部、鉱物油３５重量部、亜鉛華７重量部、ステアリ
ン酸２重量部、加硫促進剤２重量部、イオウ１．５重量
部のゴム配合物を１６０℃で３０分間加硫した。また、
耐摩耗試験方法は、下記条件で行い摩耗減量で耐摩耗性
を評価した。 試験機：テイパー式ロータリアブレッサー（株式会社東
洋精機製作所製） 試験条件：摩耗輪…Ｈ−２２、荷重…１ｋｇ摩耗回転速
度…６０ｒｐｍ 試料寸法…１００ｍｍ×１００ｍｍ 摩耗回転…１０００回
【００１０】このようにして得られた本発明の塗料組成
物を用いた耐摩耗性の試験結果を表−２に示す。
物を用いた耐摩耗性の試験結果を表−２に示す。
【００１１】
【発明の効果】これらの塗料組成物は被塗布物に塗布し
た場合、被塗布物の材料特性を損なうことなく、塗膜が
被塗布物表面との優れた密着性を有し、優れた耐摩耗性
を示す。
た場合、被塗布物の材料特性を損なうことなく、塗膜が
被塗布物表面との優れた密着性を有し、優れた耐摩耗性
を示す。
【００１２】
【００１３】
【００１３】
【００１４】
【００１５】
出光シールＡＢ−７００Ｗ：商品名、液状ポリブタジエ
ン出光石油株式会社製 出光シールＡＢ−１００：商品名、液状ポリブタジエン
出光石油株式会社製 ボンド Ｇ２ ：商品名、クロロプレン系ゴム ト
ルエン７４％溶液 コニシ株式会社製
ン出光石油株式会社製 出光シールＡＢ−１００：商品名、液状ポリブタジエン
出光石油株式会社製 ボンド Ｇ２ ：商品名、クロロプレン系ゴム ト
ルエン７４％溶液 コニシ株式会社製
Claims (1)
- 【請求項１】ポリエーテルジオール、ポリエステルジオ
ールとジイソシアナートよりなり末端にＮＣＯ基を有す
るウレタンプレポリマーにさらに低分子ジオールを反応
させて得られる末端にＮＣＯ基又はＯＨ基を有するウレ
タンプレポリマー１００重量部、フッ樹脂２〜１００重
量部、ひまし油ポリオールよりなり、前記ひまし油ポリ
オールの末端ＯＨ基と前記ウレタンプレポリマーの末端
ＮＣＯ基のモル当量比が０．７〜１．３であることを特
徴とする塗料組成物。