JPH04292676A - 塗料組成物 - Google Patents
塗料組成物Info
- Publication number
- JPH04292676A JPH04292676A JP8167391A JP8167391A JPH04292676A JP H04292676 A JPH04292676 A JP H04292676A JP 8167391 A JP8167391 A JP 8167391A JP 8167391 A JP8167391 A JP 8167391A JP H04292676 A JPH04292676 A JP H04292676A
- Authority
- JP
- Japan
- Prior art keywords
- coating composition
- abrasion resistance
- substrate
- diol
- urethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【０００１】
【産業上の利用分野】本発明はゴム、樹脂製品等の塗装
に適した塗料組成物に関するものである。
に適した塗料組成物に関するものである。
【０００２】
【従来の技術】一般に、ＮＲ、ＳＢＲ、ＢＲ、ＩＩＲ、
ＣＲ、ＮＢＲ、ＩＲ、ＥＰＤＭ、ＥＰＴ等のゴムや、木
綿、レーヨン、ＡＢＳ、ＰＳ等の樹脂、繊維は耐摩耗性
が非常に悪い。これらにナイロン、エポキシ樹脂、アク
リル樹脂、アクリル−エチレン系樹脂等の樹脂系塗料お
よびＢＲ、ＣＲ、ＳＢＲ等のゴム系塗料を塗布し摩耗を
行なった場合 （Ａ）ゴム、合成樹脂製品、繊維との密着性がないため
摩耗中基材と塗料がはがれる不具合が発生する（Ｂ）塗
料自体に耐摩耗性がないため耐摩耗性にとぼしい という問題がある。
ＣＲ、ＮＢＲ、ＩＲ、ＥＰＤＭ、ＥＰＴ等のゴムや、木
綿、レーヨン、ＡＢＳ、ＰＳ等の樹脂、繊維は耐摩耗性
が非常に悪い。これらにナイロン、エポキシ樹脂、アク
リル樹脂、アクリル−エチレン系樹脂等の樹脂系塗料お
よびＢＲ、ＣＲ、ＳＢＲ等のゴム系塗料を塗布し摩耗を
行なった場合 （Ａ）ゴム、合成樹脂製品、繊維との密着性がないため
摩耗中基材と塗料がはがれる不具合が発生する（Ｂ）塗
料自体に耐摩耗性がないため耐摩耗性にとぼしい という問題がある。
【０００３】
【発明が解決しようとする課題】本発明の目的は上記問
題点を解消し、被塗布物表面との密着性がよく、耐摩耗
性の優れた塗料組成物を提供するものである。
題点を解消し、被塗布物表面との密着性がよく、耐摩耗
性の優れた塗料組成物を提供するものである。
【０００４】
【課題を解決するための手段】本発明者は、これらの欠
点を改良するための研究をつづけ、その結果、上記欠点
を改良する塗料組成物をみいだした。
点を改良するための研究をつづけ、その結果、上記欠点
を改良する塗料組成物をみいだした。
【０００５】本発明の塗料組成物とはシリコーンジオー
ルとジイソシアナートよりなり、末端にＮＣＯ基を有す
るウレタンプレポリマーにさらに低分子ジオールを反応
させ得られるウレタン組成物よりなる塗料組成物である
。
ルとジイソシアナートよりなり、末端にＮＣＯ基を有す
るウレタンプレポリマーにさらに低分子ジオールを反応
させ得られるウレタン組成物よりなる塗料組成物である
。
【０００６】
【実施例】以下に本発明を具体化した実施例について説
明する。本発明で用いるシリコーンジオールとは、化−
１、及び表−１に示すシリコーンジオール等を用いる。 ジイソシアネートには、ＭＤＩ、ＴＤＩ、ＩＰＤＩ、Ｘ
ＤＩ、ＮＤＩ等のジイソシアネート及び前記ジイソシア
ネートの水添化合物が例示できる。低分子ジオールとは
、エチレングリコール、プロピレングリコール、ブチレ
ングリコール、ペンタンジオール、１，６−ヘキサンジ
オール、デカンジオール、ジエチレングリコール、トリ
エチレングリコール、ペンタエリストリー、水添ビスフ
ェノールＡ、ジプロピレングリコール等２官能のもので
あればよい。
明する。本発明で用いるシリコーンジオールとは、化−
１、及び表−１に示すシリコーンジオール等を用いる。 ジイソシアネートには、ＭＤＩ、ＴＤＩ、ＩＰＤＩ、Ｘ
ＤＩ、ＮＤＩ等のジイソシアネート及び前記ジイソシア
ネートの水添化合物が例示できる。低分子ジオールとは
、エチレングリコール、プロピレングリコール、ブチレ
ングリコール、ペンタンジオール、１，６−ヘキサンジ
オール、デカンジオール、ジエチレングリコール、トリ
エチレングリコール、ペンタエリストリー、水添ビスフ
ェノールＡ、ジプロピレングリコール等２官能のもので
あればよい。
【０００７】溶剤としてはベンゼン、キシレン、エチル
ベンゼン、トリクロロエチレン、塩化エチレン、ジメチ
ルホルムアミド、ジメチルスルフォキサイド、メチルエ
チルケトン、アセトン、メチルイソプロピルケトン、酢
酸メチル、酢酸エチル、酢酸イソプロピル、酢酸ｎ−ブ
チル、アニソール、テトラヒドロフラン等を用いる。
ベンゼン、トリクロロエチレン、塩化エチレン、ジメチ
ルホルムアミド、ジメチルスルフォキサイド、メチルエ
チルケトン、アセトン、メチルイソプロピルケトン、酢
酸メチル、酢酸エチル、酢酸イソプロピル、酢酸ｎ−ブ
チル、アニソール、テトラヒドロフラン等を用いる。
【０００８】ａ）塗料組成物の調製
上記シリコーンジオールとジイソシアネートと溶剤を適
宜選択して使用し（選択例を表−１に示す）、乾燥窒素
ガス中、８０℃、３時間反応させ、末端にＮＣＯ基を有
するウレタンプレポリマーを合成し、さらに低分子ジオ
ールと溶剤を加え乾燥窒素ガス中３０分間反応を行ない
得られる末端にＯＨ基又はＮＣＯ基を有するウレタン組
成物を合成した。
宜選択して使用し（選択例を表−１に示す）、乾燥窒素
ガス中、８０℃、３時間反応させ、末端にＮＣＯ基を有
するウレタンプレポリマーを合成し、さらに低分子ジオ
ールと溶剤を加え乾燥窒素ガス中３０分間反応を行ない
得られる末端にＯＨ基又はＮＣＯ基を有するウレタン組
成物を合成した。
【０００９】ｂ）基材の調製
ＥＰＤＭ１００重量部に対して、カーボンブラック７０
重量部、鉱物油３５重量部、亜鉛華７重量部、ステアリ
ン酸２重量部、加硫促進剤２重量部、イオウ１．５重量
部のゴム配合物を１６０℃で３０分間加硫した。
重量部、鉱物油３５重量部、亜鉛華７重量部、ステアリ
ン酸２重量部、加硫促進剤２重量部、イオウ１．５重量
部のゴム配合物を１６０℃で３０分間加硫した。
【００１０】また、耐摩耗試験方法は、下記条件で行い
摩耗減量で耐摩耗性を評価した。 試験機：テイパー式ロータリアブレッサー（株式会社東
洋精機製作所製） 試験条件：摩耗輪…Ｈ−２２、荷重…１ｋｇ摩耗回転速
度…６０ｒｐｍ 試料寸法…１００ｍｍ×１００ｍｍ 摩耗回転…１０００回
摩耗減量で耐摩耗性を評価した。 試験機：テイパー式ロータリアブレッサー（株式会社東
洋精機製作所製） 試験条件：摩耗輪…Ｈ−２２、荷重…１ｋｇ摩耗回転速
度…６０ｒｐｍ 試料寸法…１００ｍｍ×１００ｍｍ 摩耗回転…１０００回
【００１１】このようにして得られた本発明の塗料組成
物を用いた耐摩耗性の試験結果を表−２に示す。
物を用いた耐摩耗性の試験結果を表−２に示す。
【００１２】
【発明の効果】これらの塗料組成物は被塗布物に塗布し
た場合、被塗布物の材料特性を損なうことなく、塗膜が
被塗布物表面との優れた密着性を有し、優れた耐摩耗性
を示す。
た場合、被塗布物の材料特性を損なうことなく、塗膜が
被塗布物表面との優れた密着性を有し、優れた耐摩耗性
を示す。
【００１３】
【００１４】
【００１５】
【００１６】
Claims (1)
- 【請求項１】シリコーンジオールとジイソシアナートよ
りなり末端にＮＣＯ基を有するウレタンプレポリマーに
さらに低分子ジオールを反応させて得られる末端にＮＣ
Ｏ基又はＯＨ基を有するウレタン組成物よりなる塗料組
成物。