JPS645557B2 - - Google Patents
Info
- Publication number
- JPS645557B2 JPS645557B2 JP55080948A JP8094880A JPS645557B2 JP S645557 B2 JPS645557 B2 JP S645557B2 JP 55080948 A JP55080948 A JP 55080948A JP 8094880 A JP8094880 A JP 8094880A JP S645557 B2 JPS645557 B2 JP S645557B2
- Authority
- JP
- Japan
- Prior art keywords
- color
- heat
- zinc
- sensitive recording
- recording material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は加熱により発色剤と顕色剤が反応し
て、画像が記録される感熱記録体に関し特に顕色
剤として、特定の亜鉛化合物の１種または２種以
上を使用することにより、記録画像の保存安定性
を改良した感熱記録体を得ることを目的とする。 従来感熱記録体としては例えば米国特許第
2712507号、あるいは同第2730457号明細書に記載
されているクリスタルバイオレツトラクトン
（Ｃ・Ｖ・Ｌ・）などのロイコ染料とフエノール
性化合物の如き有機酸との組み合せよりなるもの
が公知である。 しかし、従来のこの種の感熱記録体は感熱発色
部がポリ塩化ビニルなどのプラスチツクと接触す
ると、プラスチツク中に含まれている可塑剤や安
定剤などにより、発色画像が退色し、消えてしま
つたり、また未発色部が接触した場合には発色し
なくなる欠点があつた。例えば感熱記録体の発色
部の上にプラスチツク消しゴムを置いておくと数
時間程度で発色画像が消えてしまつたり、発色記
録した感熱記録体をポリ塩化ビニル製のカードケ
ース中で長期間保存した場合には記録画像が消え
てしまうなどの不都合が生じた。 そこで、本発明者らは従来の感熱記録体に用い
られている感熱記録材料がプラスチツクに用いら
れる可塑剤などに対して不安定である原因を究明
するために種々検討した結果、従来顕色剤として
使用されているフエノール性化合物のごとき有機
酸はプラスチツクの可塑剤との相溶性が良いため
に、ロイコ染料との発色が起りにくくなり、また
発色している部分をも消してしまうことをつきと
め、ロイコ染料の顕色剤について検討した結果、
特定の亜鉛化合物を顕色剤として使用したときに
保存安定性の良い感熱記録体が得られることを見
出して、本発明に到達したものである。 すなわち本発明は、支持体上に通常無色または
淡色の発色性染料と該発色性染料を熱時発色させ
る顕色剤及び結着剤とを含有する記録層を設けた
感熱記録体において顕色剤として水酸化亜鉛、炭
酸亜鉛、しゆう酸亜鉛、酢酸亜鉛、或はこれらの
アンモニア錯体若しくは塩化亜鉛及び過酸化亜鉛
のアンモニア錯体の１種または２種以上を使用す
ることを特徴とする感熱記録体である。 本発明に用いられる無色または淡色の発色性染
料としては各種のものが公知であり、例えば次の
ようなものである。 ３・３−ビス（Ｐ−ジメチルアミノフエニル）
フタリド、３・３−ビス（ジメチルアミノフエニ
ル）−６−ジメチルアミノフタリド、３−（Ｐ−ジ
メチルアミノフエニル）−３−（１，２−ジメチル
インドール−３イル）フタリド、４・4′−ビス−
ジメチルアミノベンゾヒドリルベンジルエーテ
ル、Ｎ−ハロフエニルロイコオーラミン、Ｎ−
２・４・５−トリクロロフエニルロイコオーラミ
ン、７−ジエチルアミノ−３−クロロフルオラ
ン、７−ジエチルアミノ−３−クロロ−２−メチ
ルフルオラン、２−フエニルアミノ−３−メチル
−６−（Ｎ−エチル−Ｎ−Ｐ−トリル）アミノフ
ルオラン、３−ジエチルアミノ−６−メチル−７
−アニリノフルオラン、ベンゾイルロイコメチレ
ンブルー、Ｐ−ニトロベンジルロイコメチレンブ
ルー、３−メチル−スピロ−ジナフトピラン、な
ど。 結着剤としては、水溶性の高分子が用いられ例
えばポリビニルアルコール、ヒドロキシエチルセ
ルロース、デンプン、カゼイン、スチレン−無水
マレイン酸共重合体の塩、スチレン−ブタジエン
ラテツクスなどである。 その他必要により、白色顔料、ワツクス類、分
散剤、消泡剤、などを用いてもよい。 上記の発色性物質、および顕色剤は各々別々に
ボールミルなどにより結着剤と共に分散せしめた
後、混合し、さらに必要に応じて顔料、ワツクス
などを加えた感熱塗料を紙もしくはプラスチツク
フイルムなどの支持体上に塗布して感熱記録体が
得られる。 本発明で得られた感熱記録体は、従来技術では
克服できなかつたプラスチツクの可塑剤などによ
る発色画像の消失を防止することができ、長期間
の保存安定性が顕著に改良され、また従来品では
発色しなかつた可塑剤が付着した部分の発色も可
能となつたものである。 以下、本発明を実施例にて具体的に説明する。 実施例 １ ＜Ａ液＞ ３−ジエチルアミノ−６−メチル−７−アニリノ
フルオラン ５重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 ＜Ｂ液＞ 水酸化亜鉛 10重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 Ａ液とＢ液を別々のボールミルで24時間粉砕、
分散した後、混合して調製した塗料を原紙上に乾
燥後の塗布量が７ｇ／m2となるよう塗布して感熱
記録体を得た。 実施例 ２ ＜Ａ液＞ ３−ジエチルアミノ−６−メチル−７−アニリノ
フルオラン ５重量部 10％ポリビニルアルコール水溶液 20 〃 水 20 〃 ＜Ｂ液＞ 水酸化亜鉛アンモニア錯体 10重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 ＜Ｃ液＞ ステアリン酸アミド 10重量部 ドデシルベンゼンスルホン酸ソーダー 10 〃 水 20 〃 Ａ液、Ｂ液、Ｃ液を別々のボールミルで24時間
粉砕、分散した後混合して調製した塗料を原紙上
に乾燥後の塗布量が７ｇ／m2となるよう塗布して
感熱記録体を得た。 比較例 一般用のビスフエノールＡを顕色剤とした感熱
記録体。 上記の実施例ならびに比較例の感熱記録体を加
熱発色させ、発色部にプラスチツク消しゴムをの
せ、500ｇの圧力を加えて２時間放置して消色テ
ストを行なつた。この時の発色濃度と消色テスト
後の濃度を下表に示す。 発色濃度の測定はマクベス反射濃度計で測定し
た。
て、画像が記録される感熱記録体に関し特に顕色
剤として、特定の亜鉛化合物の１種または２種以
上を使用することにより、記録画像の保存安定性
を改良した感熱記録体を得ることを目的とする。 従来感熱記録体としては例えば米国特許第
2712507号、あるいは同第2730457号明細書に記載
されているクリスタルバイオレツトラクトン
（Ｃ・Ｖ・Ｌ・）などのロイコ染料とフエノール
性化合物の如き有機酸との組み合せよりなるもの
が公知である。 しかし、従来のこの種の感熱記録体は感熱発色
部がポリ塩化ビニルなどのプラスチツクと接触す
ると、プラスチツク中に含まれている可塑剤や安
定剤などにより、発色画像が退色し、消えてしま
つたり、また未発色部が接触した場合には発色し
なくなる欠点があつた。例えば感熱記録体の発色
部の上にプラスチツク消しゴムを置いておくと数
時間程度で発色画像が消えてしまつたり、発色記
録した感熱記録体をポリ塩化ビニル製のカードケ
ース中で長期間保存した場合には記録画像が消え
てしまうなどの不都合が生じた。 そこで、本発明者らは従来の感熱記録体に用い
られている感熱記録材料がプラスチツクに用いら
れる可塑剤などに対して不安定である原因を究明
するために種々検討した結果、従来顕色剤として
使用されているフエノール性化合物のごとき有機
酸はプラスチツクの可塑剤との相溶性が良いため
に、ロイコ染料との発色が起りにくくなり、また
発色している部分をも消してしまうことをつきと
め、ロイコ染料の顕色剤について検討した結果、
特定の亜鉛化合物を顕色剤として使用したときに
保存安定性の良い感熱記録体が得られることを見
出して、本発明に到達したものである。 すなわち本発明は、支持体上に通常無色または
淡色の発色性染料と該発色性染料を熱時発色させ
る顕色剤及び結着剤とを含有する記録層を設けた
感熱記録体において顕色剤として水酸化亜鉛、炭
酸亜鉛、しゆう酸亜鉛、酢酸亜鉛、或はこれらの
アンモニア錯体若しくは塩化亜鉛及び過酸化亜鉛
のアンモニア錯体の１種または２種以上を使用す
ることを特徴とする感熱記録体である。 本発明に用いられる無色または淡色の発色性染
料としては各種のものが公知であり、例えば次の
ようなものである。 ３・３−ビス（Ｐ−ジメチルアミノフエニル）
フタリド、３・３−ビス（ジメチルアミノフエニ
ル）−６−ジメチルアミノフタリド、３−（Ｐ−ジ
メチルアミノフエニル）−３−（１，２−ジメチル
インドール−３イル）フタリド、４・4′−ビス−
ジメチルアミノベンゾヒドリルベンジルエーテ
ル、Ｎ−ハロフエニルロイコオーラミン、Ｎ−
２・４・５−トリクロロフエニルロイコオーラミ
ン、７−ジエチルアミノ−３−クロロフルオラ
ン、７−ジエチルアミノ−３−クロロ−２−メチ
ルフルオラン、２−フエニルアミノ−３−メチル
−６−（Ｎ−エチル−Ｎ−Ｐ−トリル）アミノフ
ルオラン、３−ジエチルアミノ−６−メチル−７
−アニリノフルオラン、ベンゾイルロイコメチレ
ンブルー、Ｐ−ニトロベンジルロイコメチレンブ
ルー、３−メチル−スピロ−ジナフトピラン、な
ど。 結着剤としては、水溶性の高分子が用いられ例
えばポリビニルアルコール、ヒドロキシエチルセ
ルロース、デンプン、カゼイン、スチレン−無水
マレイン酸共重合体の塩、スチレン−ブタジエン
ラテツクスなどである。 その他必要により、白色顔料、ワツクス類、分
散剤、消泡剤、などを用いてもよい。 上記の発色性物質、および顕色剤は各々別々に
ボールミルなどにより結着剤と共に分散せしめた
後、混合し、さらに必要に応じて顔料、ワツクス
などを加えた感熱塗料を紙もしくはプラスチツク
フイルムなどの支持体上に塗布して感熱記録体が
得られる。 本発明で得られた感熱記録体は、従来技術では
克服できなかつたプラスチツクの可塑剤などによ
る発色画像の消失を防止することができ、長期間
の保存安定性が顕著に改良され、また従来品では
発色しなかつた可塑剤が付着した部分の発色も可
能となつたものである。 以下、本発明を実施例にて具体的に説明する。 実施例 １ ＜Ａ液＞ ３−ジエチルアミノ−６−メチル−７−アニリノ
フルオラン ５重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 ＜Ｂ液＞ 水酸化亜鉛 10重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 Ａ液とＢ液を別々のボールミルで24時間粉砕、
分散した後、混合して調製した塗料を原紙上に乾
燥後の塗布量が７ｇ／m2となるよう塗布して感熱
記録体を得た。 実施例 ２ ＜Ａ液＞ ３−ジエチルアミノ−６−メチル−７−アニリノ
フルオラン ５重量部 10％ポリビニルアルコール水溶液 20 〃 水 20 〃 ＜Ｂ液＞ 水酸化亜鉛アンモニア錯体 10重量部 10％ポリビニルアルコール水溶液 10 〃 水 20 〃 ＜Ｃ液＞ ステアリン酸アミド 10重量部 ドデシルベンゼンスルホン酸ソーダー 10 〃 水 20 〃 Ａ液、Ｂ液、Ｃ液を別々のボールミルで24時間
粉砕、分散した後混合して調製した塗料を原紙上
に乾燥後の塗布量が７ｇ／m2となるよう塗布して
感熱記録体を得た。 比較例 一般用のビスフエノールＡを顕色剤とした感熱
記録体。 上記の実施例ならびに比較例の感熱記録体を加
熱発色させ、発色部にプラスチツク消しゴムをの
せ、500ｇの圧力を加えて２時間放置して消色テ
ストを行なつた。この時の発色濃度と消色テスト
後の濃度を下表に示す。 発色濃度の測定はマクベス反射濃度計で測定し
た。
【表】
表からも解るように、本願の感熱記録体の発色
画像はプラスチツクの可塑剤に対して極めて安定
なものである。
画像はプラスチツクの可塑剤に対して極めて安定
なものである。
Claims (1)
- １ 支持体上に通常無色または淡色の発色性染料
と該発色性染料を熱時発色させる顕色剤及び結着
剤とを含有する記録層を設けた感熱記録体におい
て、顕色剤として水酸化亜鉛、炭酸亜鉛、しゆう
酸亜鉛、酢酸亜鉛、或はこれらのアンモニア錯体
若しくは塩化亜鉛及び過酸化亜鉛のアンモニア錯
体のうちから選ばれる１種または２種以上を使用
することを特徴とする感熱記録体。