JPH01249837A - 積層板 - Google Patents
積層板Info
- Publication number
- JPH01249837A JPH01249837A JP7774888A JP7774888A JPH01249837A JP H01249837 A JPH01249837 A JP H01249837A JP 7774888 A JP7774888 A JP 7774888A JP 7774888 A JP7774888 A JP 7774888A JP H01249837 A JPH01249837 A JP H01249837A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- melamine
- impregnated
- formaldehyde
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、耐衝撃性に勝れた電気用積層板（積Ｎ絶縁板
、印刷回路用銅張積層板）に関する。
、印刷回路用銅張積層板）に関する。
積層板は、樹脂を含浸した基材を積層し樹脂を硬化させ
たものである。この樹脂としては、プリプレグ化が容易
でありかつ乾式積層によって大量生産が可能なフェノー
ル樹脂又はエポキシ樹脂が用いられ、湿式積層による場
合は、不飽和ポリエステル樹脂などが用いられる。
たものである。この樹脂としては、プリプレグ化が容易
でありかつ乾式積層によって大量生産が可能なフェノー
ル樹脂又はエポキシ樹脂が用いられ、湿式積層による場
合は、不飽和ポリエステル樹脂などが用いられる。
不飽和ポリエステル樹脂を用いる場合は、不飽和ポリエ
ステル樹脂の含浸に先立ち、セルロース系基材にメラミ
ン樹脂を含浸させ、積層板の電気特性、耐湿性を向上さ
せている。
ステル樹脂の含浸に先立ち、セルロース系基材にメラミ
ン樹脂を含浸させ、積層板の電気特性、耐湿性を向上さ
せている。
従来メラミン樹脂は、貯蔵安定性を考慮して。
メラミン１モルに対して、ホルムアルデヒド３モルを反
応せさせたものを使用していた。
応せさせたものを使用していた。
ところが、このようなメラミン樹脂をセルロース系基材
に含浸させると、積層板の電気特性、耐湿性は向上する
ものの、耐衝撃性等の機械強度が低下する。
に含浸させると、積層板の電気特性、耐湿性は向上する
ものの、耐衝撃性等の機械強度が低下する。
これを解決するために種々の方法が提案されているが、
未だに耐衝撃性並びに電気特性及び耐湿性のいずれもを
満足させるに至っていない。
未だに耐衝撃性並びに電気特性及び耐湿性のいずれもを
満足させるに至っていない。
本発明は、耐衝撃性、電気特性及び耐湿性いずれも良好
な積層板を提供することを目的とするものである。
な積層板を提供することを目的とするものである。
本発明は、セルロース系基材に、メラミン１モルに対し
てホルムアルデヒド１〜２．５モル好ましくは１．２〜
２モルを加熱反応させて得られたメラミン樹脂を含浸処
理し、その後さらに不飽和結合を有する樹脂を含浸し、
該樹脂を硬化させた積層板である。
てホルムアルデヒド１〜２．５モル好ましくは１．２〜
２モルを加熱反応させて得られたメラミン樹脂を含浸処
理し、その後さらに不飽和結合を有する樹脂を含浸し、
該樹脂を硬化させた積層板である。
本発明に係るメラミン樹脂は５通常の方法により製造す
る。しかしながら、ホルムアルデヒドのモル数が少なく
なるにしたがってメラミン樹脂の保存安定性が悪くなる
から、必要に応して炭素数５以下の低級アルコールを添
加するか、あるいは低級アルコールを用いてメラミン樹
脂のメチロール基の一部または全部をエーテル化する。
る。しかしながら、ホルムアルデヒドのモル数が少なく
なるにしたがってメラミン樹脂の保存安定性が悪くなる
から、必要に応して炭素数５以下の低級アルコールを添
加するか、あるいは低級アルコールを用いてメラミン樹
脂のメチロール基の一部または全部をエーテル化する。
また、メラミン樹脂の可撓性を増すためには必要により
、可望剤としてパラトルエンスルホンアミドを添加する
。添加量はメラミン１モルに対して０．１モル以上が適
当である。
、可望剤としてパラトルエンスルホンアミドを添加する
。添加量はメラミン１モルに対して０．１モル以上が適
当である。
本発明に用いる不飽和結合を有する樹脂としては、アク
リル酸アルキルエステル、メタクリル酸アルキルエステ
ルあるいはスチレン等により重合体を得、その側鎖に不
飽和二重結合を導入したもの、ビニルエステル樹脂等の
ように分子末端に不飽和二重結合を持つもの、或いは主
鎖中に不飽和二重結合を有する不飽和ポリエステル樹脂
など及びこれらの混合物がある。
リル酸アルキルエステル、メタクリル酸アルキルエステ
ルあるいはスチレン等により重合体を得、その側鎖に不
飽和二重結合を導入したもの、ビニルエステル樹脂等の
ように分子末端に不飽和二重結合を持つもの、或いは主
鎖中に不飽和二重結合を有する不飽和ポリエステル樹脂
など及びこれらの混合物がある。
樹脂中に必要に応じてハロゲン系の添加型又は反応型の
難燃剤、りん系難燃剤、三酸化アンチモン、水酸化アル
ミニウム等の無機難燃剤を加えて使用する。
難燃剤、りん系難燃剤、三酸化アンチモン、水酸化アル
ミニウム等の無機難燃剤を加えて使用する。
セルロース系基材としては、クラフト紙、リンター祇等
のセルロース系紙基材及びガラス繊維混抄紙がある。
のセルロース系紙基材及びガラス繊維混抄紙がある。
本発明の作用は詳らかでないが、メラミンに反応させる
ホルムアルデヒドの量を少なくしたので。
ホルムアルデヒドの量を少なくしたので。
得られたメラミン樹脂が軟らかくなり、その結果耐！Ｊ
撃性が向上するものと思われる。
撃性が向上するものと思われる。
１０ メラミン樹脂の合成
１、メラミン樹脂■
３７％ホルマリン４０５重量部、メラミン４２０重量部
、水２５０重量部を８０℃で４０分間撹拌混合してメラ
ミンを溶解させ、さらにメタノール２６０重量部を添加
し冷却してメラミン樹脂Ｉを得た。
、水２５０重量部を８０℃で４０分間撹拌混合してメラ
ミンを溶解させ、さらにメタノール２６０重量部を添加
し冷却してメラミン樹脂Ｉを得た。
この樹脂はメラミン１モルに対してホルムアルデヒド１
．５モルの結合比である。
．５モルの結合比である。
ｉｉ、メラミン樹脂■
メラミン樹脂■の合成方法において、ホルマリンの量を
変えた他は同じにしてメラミン１モルに対してホルムア
ルデヒド３．０モルの結合比ヲ持つメラミン樹脂■を得
た。
変えた他は同じにしてメラミン１モルに対してホルムア
ルデヒド３．０モルの結合比ヲ持つメラミン樹脂■を得
た。
（２） 不飽和樹脂の合成
ｉ、アクリル酸エチル１０！１ｆｆｉ部、アクリル酸ブ
チル７０重量部、アクリル酸メタグリシジル２０重量部
を３０％溶液中で溶液重合を行い、溶剤を除いて共重合
体を得た。さらに、この共重合体にアクリル酸１０重量
部を添加反応させて側鎖に二重結合を付与した。次いで
スチレンを加えて不揮発分６０％の不飽和樹脂を得た。
チル７０重量部、アクリル酸メタグリシジル２０重量部
を３０％溶液中で溶液重合を行い、溶剤を除いて共重合
体を得た。さらに、この共重合体にアクリル酸１０重量
部を添加反応させて側鎖に二重結合を付与した。次いで
スチレンを加えて不揮発分６０％の不飽和樹脂を得た。
１１、スチレン３０重量部、メタクリル酸−２ヒドロキ
シ工チル４０重量部、アクリル酸にブチル４０重量部を
３０％溶液中で溶液重合を行い、さらにこれに無水マレ
イン酸を付加反応させて側鎖に二重結合を付与し、スチ
レンを加えて不揮発分６０％の不飽和樹脂を得た。
シ工チル４０重量部、アクリル酸にブチル４０重量部を
３０％溶液中で溶液重合を行い、さらにこれに無水マレ
イン酸を付加反応させて側鎖に二重結合を付与し、スチ
レンを加えて不揮発分６０％の不飽和樹脂を得た。
ｉｉｉ 、テトラブロモビスフェノールＡプリンジルエ
ーテル（エポキシ当量３９５〜４１０） １００重量部
に対し、ダイマー酸３５．７ベンジルジメチルアミン１
．３、スチレン６２．ハイドロキノン０．０５各重量部
を配合し、酸価が６以下となるまで反応を続け、さらに
メタクリル酸９重量部を配合し、酸価２．３のダイマー
酸変性エポキシメタクリレート樹脂を得た。
ーテル（エポキシ当量３９５〜４１０） １００重量部
に対し、ダイマー酸３５．７ベンジルジメチルアミン１
．３、スチレン６２．ハイドロキノン０．０５各重量部
を配合し、酸価が６以下となるまで反応を続け、さらに
メタクリル酸９重量部を配合し、酸価２．３のダイマー
酸変性エポキシメタクリレート樹脂を得た。
Ｉｖ、ジエチレングリコール８９重量部、無水マレイン
酸３７重量部、イソフタル酸６３重量部、ハイドロキノ
ン０．０２重量部を配合し、窒素ガスを吹込みながら１
９０〜２２０℃で酸価が１９となるまで加熱を続け、不
飽和ポリエステル樹脂を得た。
酸３７重量部、イソフタル酸６３重量部、ハイドロキノ
ン０．０２重量部を配合し、窒素ガスを吹込みながら１
９０〜２２０℃で酸価が１９となるまで加熱を続け、不
飽和ポリエステル樹脂を得た。
（３） 銅張積層板の製造
メラミン樹脂Ｉを１４０ｇのクラフト紙に含浸乾燥した
。クラフト紙の重量は１５．１％増加した。
。クラフト紙の重量は１５．１％増加した。
次にこの含浸紙に、ヘンシルパーオキサイド１重量部を
配合した不飽和樹脂（（ｉ）（ｉｉ） （ｉｉｉ）（ｉ
ｖ）） ４種をそれぞれ含浸させ５各６枚を重ねた後、
それぞれにエポキシ系接着剤を塗布した厚さ３５μｍの
電解銅箔をラミネートして、１３０℃。
配合した不飽和樹脂（（ｉ）（ｉｉ） （ｉｉｉ）（ｉ
ｖ）） ４種をそれぞれ含浸させ５各６枚を重ねた後、
それぞれにエポキシ系接着剤を塗布した厚さ３５μｍの
電解銅箔をラミネートして、１３０℃。
１５ｋｇ／ａｄで２０分間加圧加熱して樹脂を硬化させ
厚さ１．６■論の銅張積層板を得た。
厚さ１．６■論の銅張積層板を得た。
メラミン樹脂■を用い、実施例（３）と同様にして。
銅張積層板を得た。
実施例及び比較例によって得た銅張積層板の衝撃強さ及
び煮沸絶縁抵抗を測定した。衝撃強さは。
び煮沸絶縁抵抗を測定した。衝撃強さは。
落下衝撃試験機を用い１４０ ｇの重りを落下させ破壊
したときの高さで示す。煮沸絶縁抵抗はＪＩＳＣ６４８
１に依った。試験結果を第１表に示す。
したときの高さで示す。煮沸絶縁抵抗はＪＩＳＣ６４８
１に依った。試験結果を第１表に示す。
第１表
（以下全ｂ）
〔発明の効果〕
Claims (1)
- 【特許請求の範囲】 １、セルロース系繊維基材に、メラミン１モルにホルム
アルデヒド１〜２．５モルを反応させて得られたメラミ
ン樹脂を含浸乾燥した後、不飽和結合を有する樹脂を含
浸硬化してなる積層板。 ２、メラミン樹脂に可塑剤としてパラトルエンスルホン
アミドを加えてなる請求項１記載の積層板。 ３、不飽和結合を有する樹脂が、主鎖、側鎖又は主鎖の
末端に共重合可能な不飽和結合を有する請求項１記載の
積層板。