JPH0421437A - 電気用積層板 - Google Patents
電気用積層板Info
- Publication number
- JPH0421437A JPH0421437A JP12784190A JP12784190A JPH0421437A JP H0421437 A JPH0421437 A JP H0421437A JP 12784190 A JP12784190 A JP 12784190A JP 12784190 A JP12784190 A JP 12784190A JP H0421437 A JPH0421437 A JP H0421437A
- Authority
- JP
- Japan
- Prior art keywords
- metal foil
- film
- necessary
- electrical
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は電子機器、電気機器、コンピューター、通信機
器等に用いられる電気用積層板に関するものである。
器等に用いられる電気用積層板に関するものである。
従来の弗素樹脂からなる電気用積層板は、弗素樹脂エマ
ルジョンを基材に含浸、乾燥することを反復して所要樹
脂量を基材に付着させて得られるものであるが、基材へ
の樹脂含浸性が悪く電気性能のバラツキ、反りが大きく
なる問題があった。
ルジョンを基材に含浸、乾燥することを反復して所要樹
脂量を基材に付着させて得られるものであるが、基材へ
の樹脂含浸性が悪く電気性能のバラツキ、反りが大きく
なる問題があった。
〔発明が解決しようとする問題点］
従来の技術で述べたように弗素樹脂エマルジョンを基材
に含浸、乾燥してなるプリプレグを用いた電気用積層板
は電気性能のバラツキ、反りが太き（なる問題点がある
。本発明は実施例の技術における上述の問題点に鑑みて
なされたもので、その目的とするところは電気性能のバ
ラツキ及び反りの少ない電気用積層板を提供することに
ある。
に含浸、乾燥してなるプリプレグを用いた電気用積層板
は電気性能のバラツキ、反りが太き（なる問題点がある
。本発明は実施例の技術における上述の問題点に鑑みて
なされたもので、その目的とするところは電気性能のバ
ラツキ及び反りの少ない電気用積層板を提供することに
ある。
本発明は所要枚数の基材の各上面及び又は下面に弗素樹
脂フィルムを配し、更に必要に応じて最外層に金属箔を
配設した積層体を一体化してなることを特徴とする電気
用積層板のため、基材に溶融樹脂が圧入されるので基材
への樹脂の含浸が均一となり電気性能のバラツキ、反り
を少なくすることができたもので、以下本発明の詳細な
説明する。
脂フィルムを配し、更に必要に応じて最外層に金属箔を
配設した積層体を一体化してなることを特徴とする電気
用積層板のため、基材に溶融樹脂が圧入されるので基材
への樹脂の含浸が均一となり電気性能のバラツキ、反り
を少なくすることができたもので、以下本発明の詳細な
説明する。
本発明に用いる基材としてはガラス、アスベスト等の無
機繊維やポリエステル、ポリアクリル、ポリビニルアル
コール、ポリアミド、ポリイミド、ポリフェニレンサル
ファイド、ポリウレタン等の有機合成繊維や木綿等の天
然繊維からなる織布、不織布、７７）或いは祇又はこれ
等の組合せ基材で基材は予じめカンプリング剤等で処理
しておくこともできる。弗素樹脂フィルムとしては、四
弗化エチレン樹脂、四弗化エチレンパーフルオロビニル
エーテル共重合体、四弗化エチレン六弗化プロピレン共
重合体、四弗化エチレンエチレン共重合体、三弗化塩化
エチレン樹脂等のように弗素樹脂全般のフィルムを用い
ることができる。フィルムの厚みはＯ，ＯＯ５〜０．５
ｍｍが好ましく、必要に応じて弗素樹脂には水酸化ア
ルミニウム、タルク、シリカ、アルミナ、炭酸カルシウ
ム、炭酸マグネシウム等の無機充填剤やガラス繊維チッ
プ、アスベスト、木粉、パルプ、綿粉等の繊維質充填剤
を添加することもできる。金属箔としては銅、アルミニ
ウム、鉄、ニンケル、亜鉛等の単独、合金、複合箔が用
いられ、必要に応じて金属箔の片面に接着剤層を設けて
おき、より接着性を向上させることもできる。一体止手
段としてはプレス、多段プレス、マルチロール等が用い
られる。
機繊維やポリエステル、ポリアクリル、ポリビニルアル
コール、ポリアミド、ポリイミド、ポリフェニレンサル
ファイド、ポリウレタン等の有機合成繊維や木綿等の天
然繊維からなる織布、不織布、７７）或いは祇又はこれ
等の組合せ基材で基材は予じめカンプリング剤等で処理
しておくこともできる。弗素樹脂フィルムとしては、四
弗化エチレン樹脂、四弗化エチレンパーフルオロビニル
エーテル共重合体、四弗化エチレン六弗化プロピレン共
重合体、四弗化エチレンエチレン共重合体、三弗化塩化
エチレン樹脂等のように弗素樹脂全般のフィルムを用い
ることができる。フィルムの厚みはＯ，ＯＯ５〜０．５
ｍｍが好ましく、必要に応じて弗素樹脂には水酸化ア
ルミニウム、タルク、シリカ、アルミナ、炭酸カルシウ
ム、炭酸マグネシウム等の無機充填剤やガラス繊維チッ
プ、アスベスト、木粉、パルプ、綿粉等の繊維質充填剤
を添加することもできる。金属箔としては銅、アルミニ
ウム、鉄、ニンケル、亜鉛等の単独、合金、複合箔が用
いられ、必要に応じて金属箔の片面に接着剤層を設けて
おき、より接着性を向上させることもできる。一体止手
段としてはプレス、多段プレス、マルチロール等が用い
られる。
以下本発明を実施例にもとづいて説明する。
〔実施例１〕
厚さ０．１５ｍｍのガラス布７枚の各層間及び最外層に
厚さ０．１ｍｍの四弗化エチレン六弗化プロピレン共重
合体フィルム（ダイキン工業株式会社製、ネオフロンフ
ィルム）を配し、更に最外層に厚さ０．０３５ｍｍの接
着剤付銅箔の接着剤側をフィルムと対向させて夫々配設
した積層体を成形圧力２゜ｋｇ／ｃｄ、２８０℃で６０
分間プレスで積層成形して厚さ１．２閣の電気用積層板
を得た。
厚さ０．１ｍｍの四弗化エチレン六弗化プロピレン共重
合体フィルム（ダイキン工業株式会社製、ネオフロンフ
ィルム）を配し、更に最外層に厚さ０．０３５ｍｍの接
着剤付銅箔の接着剤側をフィルムと対向させて夫々配設
した積層体を成形圧力２゜ｋｇ／ｃｄ、２８０℃で６０
分間プレスで積層成形して厚さ１．２閣の電気用積層板
を得た。
実施例と同じ四弗化エチレン六弗化プロピレン共重合体
エマルジョンを樹脂量が３０重量％になるように厚さ０
．１５ｍのガラス布に含浸、乾燥したプリプレグ７枚を
重ね、更にその最外層に実施例と同じＦ４箔を夫々配設
した積層体を実施例と同様に処理して厚さ１．２ｍｍの
電気用積層板を得た。
エマルジョンを樹脂量が３０重量％になるように厚さ０
．１５ｍのガラス布に含浸、乾燥したプリプレグ７枚を
重ね、更にその最外層に実施例と同じＦ４箔を夫々配設
した積層体を実施例と同様に処理して厚さ１．２ｍｍの
電気用積層板を得た。
実施例及び比較例の電気用積層板の性能は第１表のよう
である。
である。
第
表
〔発明の効果〕
本発明は上述した如く構成されている。特許請求の範囲
に記載した構成を有する電気用積層板においては電気性
能のバラツキ、反りが少なくなる効果がある。
に記載した構成を有する電気用積層板においては電気性
能のバラツキ、反りが少なくなる効果がある。
Claims (1)
- （１）所要枚数の基材の各上面及び又は下面に、弗素樹
脂フイルムを配し、更に必要に応じて最外層に金属箔を
配設した積層体を一体化してなることを特徴とする電気
用積層板。