JPH051755B2 - - Google Patents
Info
- Publication number
- JPH051755B2 JPH051755B2 JP61128464A JP12846486A JPH051755B2 JP H051755 B2 JPH051755 B2 JP H051755B2 JP 61128464 A JP61128464 A JP 61128464A JP 12846486 A JP12846486 A JP 12846486A JP H051755 B2 JPH051755 B2 JP H051755B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording
- substrate
- selenium
- tellurium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
第１図は本発明の光記録媒体の一実施例を示す
部分断面図、第２図は従来の光記録媒体を示す部
分断面図である。 １…基板、２，６…セレン層、３，５…パラジ
ウム層、４…テルル層、２１…記録層、２２…ピ
ツト。
部分断面図、第２図は従来の光記録媒体を示す部
分断面図である。 １…基板、２，６…セレン層、３，５…パラジ
ウム層、４…テルル層、２１…記録層、２２…ピ
ツト。
Claims (1)
- 【特許請求の範囲】 １ 基板と、レーザ光によつて一部が選択的に除
去されて情報を記録する前記基板上に形成された
記録層とからなる光記録媒体において、前記記録
層がセレン層、パラジウム層、テルル層、パラジ
ウム層、セレン層を順次基板上に積層したもので
あることを特徴とする光記録媒体。 ※説［産業上の利用分野］ 本発明はレーザ光によつて情報を記録再生する
ことのできる光記録媒体に関するものである。 ［従来の技術］ レーザ光によつて情報を媒体に記録し、かつ再
生する光デイスクメモリは、記録密度が高いこと
から大容量記録装置として優れた特徴と有してい
る。この光記録媒体材料としては、テルル（Te）
等のカルコゲン元素又はこれらの化合物が使用さ
れている特公昭47−26897号公報）。とくにテルル
−セレン系合金はよく使用されている（特公昭54
−41902号公報、特公昭57−7919号公報、特公昭
57−56058号公報）。 近年、記録装置を小型化するため、レーザ光源
としては半導体レーザが使用されてきている。半
導体レーザは発振波長が8000Å前後であるが、テ
ルル−セレン系合金はこの波長帯にも比較的よく
適合し、適度な反射率と適度な吸収率が得られる
｛フイジカ・ステイタス・ソリダイ、７、189、
1964（phys.stat.sol.７、189、1964）｝。 このテルル−セレン系合金を光記録層として用
いた光記録媒体は第２図に示すような構成になつ
ている。すなわち基板１に隣接してテルル−セレ
ン系合金よりなる記録層２１が設けられている。
記録用レーザ光は基板１を通して記録層２１に集
光照射され、ピツト２２が形成される。基板１と
してはポリカーボネート、ポリオレフイン、ポリ
メチルペンテル、アクリル、エポキシ樹脂等の合
成樹脂やガラスが使用され、基板１にはピツトが
同心円状あるいはスパイラル状に一定間隔で精度
よく記録されるように通常案内溝が設けられてい
る。 ［発明が解決しようとする問題点］ しかしながら前記したような従来の光記録媒体
において、記録層として用いられているテルル−
セレン系合金はその組成を制御することが容易で
はなく、そのため量産性に問題があつた。又、ピ
ツトをトラツク１周にわたつて均一に形成するこ
とは困難であるため、充分に良好な記録再生特性
は得られなかつた。 一方、本発明者らは、基板の上にセレン層、テ
ルル層、セレン層を順次積層して記録層とするこ
とにより、量産性および耐候性に優れ、かつ、ト
ラツク１周にわたつてピツトを均一に形成でき、
良好な記録再生特性を有する光記録媒体となるこ
とを見出し、すでに提案している。 本発明はこれをさらに改善したもので、量産性
および耐候性に優れ、かつ高感度で信号品質の良
好な光記録媒体を提供することを目的とする。 ［問題点を解決するための手段］ 本発明は基板と、レーザ光によつて一部が選択
的に除去されて情報を記録する前記基板上に形成
された記録層とからなる光記録媒体において、前
記記録層がセレン層、パラジウム層、テルル層、
パラジウム層、セレン層を順次基板上に積層した
ものであることを特徴とする光記録媒体である。 本発明においては第１図に示すように基板１上
にセレン層２、パラジウム層３、テルル層４、パ
ラジウム層５、セレン層６が順次積層されて記録
層を形成する。パラジウム層３とパルジウム層５
を形成することにより、記録により形成されるピ
ツトが大きく拡がらないようになる。 上下のセレン層の膜厚はともにそれぞれ５〜
100Åの範囲、テルル層の膜厚は100〜500Åの範
囲、上下のパラジウム層の膜厚はともにそれぞれ
0.5〜50Åの範囲が記録再生特性、耐候性の観点
から望ましい。なお、ここでいう0.5〜50Åのパ
ラジウム層というのは重量平均に相当する膜厚で
あり、実際には不連続膜となつている。 基板としてはポリカーポネート、ポリオレフイ
ン、ポリメチルペンテン、アクリル、エポキシ樹
脂等の合成樹脂やガラスなど通常使用されている
ものが用いられる。 本発明の光記録媒体は、基板上にセレン、パラ
ジウム、テルル、パラジウムおよびセレンを順に
真空蒸着させることによつて製造することができ
る。 ［作 用］ テルル層とセレン層の間にパラジウム層を介在
させることによつてピツトが大きく拡がらなくな
り、優れた光記録媒体を得ることができる。これ
はピツト形成による反射率変化の主要因であるテ
ルル層４の表面張力がパラジウム層５の形成によ
り変化することによるためと、テルル層４の有無
による表面エネルギーの差がパラジウム層３の形
成により変化することによつてピツトが拡がりに
くくなるためであると思われる。 ピツトが大きく拡がらないのでピツトをつめて
記録でき、高密度記録が可能となるとともに記録
パワー変動に対する余裕度も大きくなるので実用
的な光記録媒体となる。 ［実施例］ 以下本発明の実施例について説明する。 実施例 内径15mm、外径130mm、厚さ1.2mmのポリカーボ
ネート樹脂デイスク基板を真空蒸着装置内に入
れ、６×10-6Torr以下に排気した。蒸発源とし
ては、第１の抵抗加熱用ボートにテルル（Te）
を入れ、第２の抵抗加熱用ボートにセレン（Se）
を入れ、電子ビーム加熱用るつぼにパラジウム
（Pd）を入れた。まずSeを80Å厚蒸着し、次に
Pdを水晶振動子の周波数変化からの換算で１Å
厚蒸着し、次にTeを225Å厚蒸着し、次にPdを
１Å厚蒸着し、最後にSeを80Å厚蒸着した。こ
の光デイスクを95℃で１時間アニールしたのち、
波長8300Åにおける基板入射反射率を測定したと
ころ33％であつた。波長8300Åの半導体レーザ光
を基板を通して入射して1.5μmφ程度に絞り、媒
体線速度5.6m／sec、記録周波数3.77MHz、記録
パルス幅70nsecの条件で記録し、0.7mWで再生
した。記録パワー6.0mWにおいて、バンド幅30k
Hzのキヤリアーとノイズとの比（Ｃ／Ｎ）は
49dBと良好であつた。又、Ｃ／Ｎが45dB以上得
られる記録パワー領域は5.5mWから8.0mWと広
範囲であつた。比較のための80Å厚のSe、225Å
厚のTe、80Å厚のSeの光デイスクでは、記録パ
ワー5.0mWにおいてＣ／Ｎは48dBであり、Ｃ／
Ｎが45dB以上得られる記録パワー領域は5.0mW
から6.5mWと狭い範囲であつた。 次に、本実施例のデイスクを60℃、80％の高温
高湿度の環境に60時間保存した後、上記特性を調
べたが変化はなく、耐候性に優れた光記録媒体で
あることが確認された。 ［発明の効果］ 以上説明したように本発明の光記録媒体は量産
性および耐候性に優れているばかりでなく、高感
度で信号品質の良好なものである。