WO2017040109A1 - Solution de polyuréthane et utilisation de celle-ci - Google Patents

Solution de polyuréthane et utilisation de celle-ci Download PDF

Info

Publication number
WO2017040109A1
WO2017040109A1 PCT/US2016/048161 US2016048161W WO2017040109A1 WO 2017040109 A1 WO2017040109 A1 WO 2017040109A1 US 2016048161 W US2016048161 W US 2016048161W WO 2017040109 A1 WO2017040109 A1 WO 2017040109A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyurethane
solution
substrate
solvent
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2016/048161
Other languages
English (en)
Inventor
Sergei V. Levchik
Robert STENEKES
Jens LEOPOLD
Jeffrey Stowell
Kali SURYADEVARA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ICL IP America Inc
Original Assignee
ICL IP America Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ICL IP America Inc filed Critical ICL IP America Inc
Publication of WO2017040109A1 publication Critical patent/WO2017040109A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une solution de polyuréthane comportant un soluté de polyuréthane dissous dans un solvant de trialkylephosphate. La solution de polyuréthane, selon certains aspects de l'invention, est utilisée pour enduire un substrat, par exemple, un substrat textile, de façon à former un substrat enduit de polyuréthane. L'invention concerne aussi un procédé de préparation de la solution de polyuréthane. Enfin, l'invention concerne également dans les présentes un procédé de préparation d'un substrat enduit de polyuréthane thermoplastique.
PCT/US2016/048161 2015-09-02 2016-08-23 Solution de polyuréthane et utilisation de celle-ci Ceased WO2017040109A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201562213336P 2015-09-02 2015-09-02
US62/213,336 2015-09-02

Publications (1)

Publication Number Publication Date
WO2017040109A1 true WO2017040109A1 (fr) 2017-03-09

Family

ID=56943910

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/048161 Ceased WO2017040109A1 (fr) 2015-09-02 2016-08-23 Solution de polyuréthane et utilisation de celle-ci

Country Status (1)

Country Link
WO (1) WO2017040109A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020180946A1 (fr) * 2019-03-05 2020-09-10 Engineered Floors LLC Stabilisation de surfaces de tissu
CN117005213A (zh) * 2023-08-09 2023-11-07 江苏华峰超纤材料有限公司 一种具有高延展性的水性聚氨酯复合涂层的制备和应用
CN117580982A (zh) * 2021-07-13 2024-02-20 旭化成株式会社 热塑性聚氨酯弹性纤维及其卷装体、包含该热塑性聚氨酯弹性纤维的褶裥和卫生材料、以及该聚氨酯弹性纤维的制造方法
WO2024120897A1 (fr) 2022-12-07 2024-06-13 Basf Se Couches minces de polyuréthane et leur procédé de production

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2636648A (en) 1948-06-19 1953-04-28 Modern Equipment Co Weigh hopper
US3342909A (en) 1964-10-26 1967-09-19 Union Oil Co Preparation of trialkyl phosphates from dialkyl phosponates
US3575894A (en) * 1967-07-22 1971-04-20 Bayer Ag Process for making water vapor permeable microporous sheeting
WO2012061373A1 (fr) 2010-11-04 2012-05-10 Icl-Ip America Inc. Textile ignifugé et procédé de revêtement de textile
CN104774552A (zh) * 2015-03-30 2015-07-15 广西吉宽太阳能设备有限公司 一种水溶性聚氨酯隔热反光涂料及其制备方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2636648A (en) 1948-06-19 1953-04-28 Modern Equipment Co Weigh hopper
US3342909A (en) 1964-10-26 1967-09-19 Union Oil Co Preparation of trialkyl phosphates from dialkyl phosponates
US3575894A (en) * 1967-07-22 1971-04-20 Bayer Ag Process for making water vapor permeable microporous sheeting
WO2012061373A1 (fr) 2010-11-04 2012-05-10 Icl-Ip America Inc. Textile ignifugé et procédé de revêtement de textile
CN104774552A (zh) * 2015-03-30 2015-07-15 广西吉宽太阳能设备有限公司 一种水溶性聚氨酯隔热反光涂料及其制备方法

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020180946A1 (fr) * 2019-03-05 2020-09-10 Engineered Floors LLC Stabilisation de surfaces de tissu
CN117580982A (zh) * 2021-07-13 2024-02-20 旭化成株式会社 热塑性聚氨酯弹性纤维及其卷装体、包含该热塑性聚氨酯弹性纤维的褶裥和卫生材料、以及该聚氨酯弹性纤维的制造方法
WO2024120897A1 (fr) 2022-12-07 2024-06-13 Basf Se Couches minces de polyuréthane et leur procédé de production
CN117005213A (zh) * 2023-08-09 2023-11-07 江苏华峰超纤材料有限公司 一种具有高延展性的水性聚氨酯复合涂层的制备和应用

Similar Documents

Publication Publication Date Title
RU2496799C2 (ru) Способ получения реакционно-способной полиуретановой эмульсии
DE2931125C2 (de) Verfahren zur Herstellung eines mit Polyurethan imprägnierten faserigen porösen Bahnmaterials
WO2017040109A1 (fr) Solution de polyuréthane et utilisation de celle-ci
JP5090319B2 (ja) 植物由来成分からなる合成皮革
KR20180072664A (ko) 실크 성능 의류와 제품들 및 이의 제조 방법
EP3044362B1 (fr) Polymères époxydes bromés utilisés comme formulations ignifuges de finition textile
BE897013A (fr) Compositions de revetement a base de polyurethanne coagule et leurs applications
TW201026763A (en) Phosphorus flame retardants and applications therefor
DE3234590A1 (de) Thermisch reaktives, wasserloesliches urethanprepolymerisat
EP3697958B1 (fr) Procédé de fabrication d'un article textile ayant une surface textile hydrophobisée par traitement plasma et un traitement chimique au mouillé
EP2780501B1 (fr) Procédé pour la préparation d'un tissu synthétique de type velours microfibreux non tissé
EP0323481B1 (fr) Revetements microporeux
CN109338738B (zh) 一种多功能复合装饰材料的制备方法
EP0697029B1 (fr) Dispersions polymeres aqueuses et leur utilisation pour realiser des revetements permeables a la vapeur d'eau
CN102337677B (zh) 表面涂覆过的聚酯纤维基质及其制备方法
EP3049488B1 (fr) Polysiloxanes comprenant des groupes hétérocycliques quaternisés
CN109367159B (zh) 一种多功能复合装饰材料
EP2283182B1 (fr) Composition pour le traitement de matériaux fibreux en particulier par un procédé par épuisement
EP4392602A1 (fr) Fibre
CN110042674A (zh) 添加型三防海岛超细纤维革制备方法
CN102330346A (zh) 一种粘棉织物用防霉剂
WO2024120897A1 (fr) Couches minces de polyuréthane et leur procédé de production
RU2523330C2 (ru) Огнестойкий декоративно-отделочный материал и способ его получения
JP2025062719A (ja) 繊維処理剤組成物、繊維加工品、及び繊維加工品の製造方法
CN107001792A (zh) 具有改性表面特性的聚合物和其制造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16767054

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16767054

Country of ref document: EP

Kind code of ref document: A1